BCN nanotube

(a,d,e) Electron micrographs of BC2N nanotubes, (b) Electron diffraction pattern, (c) fragment of the nanotube wall.[1]

BCN nanotubes are tubular structures with a sub-micrometer diameter and a length much longer than diameter. They are composed of comparable amounts of boron, carbon and nitrogen atoms.

First made in 1994, synthesis methods have included: arc-discharge, laser ablation, chemical vapor deposition (CVD), template route, and pyrolysis techniques. Single-walled B–C–N nanotubes have been made with a hot-filament method.[2]

Solvothermal synthesis

Vertically aligned arrays of ~BC2N nanotubes can be produced by solvothermal synthesis in a stainless steel autoclave from a mixture of sodium azide (NaN3), ammonium fluoroborate (NH4BF4) and methyl cyanide (CH3CN). The mixture, together with the solvent and other additives is heated to 400 °C for ~14 h.[1] The final composition was approx B19C55N26.[1]

Potential applications

The vertically-aligned BCN nanotubes (made as above) exhibit a high and stable specific capacitance (>500 F/g), which exceeds that of alternative carbon nanomaterials, and therefore have potential applications in supercapacitors.[1][3]

Facile synthesis

Another method produced nanotubes of composition : B45%,C31%,N24% [2] The method was grow them on stainless steel by reacting boron, zinc oxide (ZnO), and ethanol in nitrogen and hydrogen at 1150°C. The resulting nanotubes had an average diameter of about 90 nm.

References

  1. 1 2 3 4 Zhou, Junshuang; Li, Na; Gao, Faming; Zhao, Yufeng; Hou, Li; Xu, Ziming (2014). "Vertically-aligned BCN Nanotube Arrays with Superior Performance in Electrochemical capacitors". Scientific Reports 4. doi:10.1038/srep06083.
  2. 1 2 Facile Synthesis of Ternary Boron Carbonitride Nanotubes. Nanoscale Res Lett. 2009; 4(8): 834–838.
  3. Zhi, C. Y.; Bai, X. D.; Wang, E. G. (2004). "Boron carbonitride nanotubes". Journal of nanoscience and nanotechnology 4 (1–2): 35–51. doi:10.1166/jnn.2004.018. PMID 15112540.


This article is issued from Wikipedia - version of the Saturday, January 02, 2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.