Coring

For geological coring, see core sample.

Coring happens when a heated alloy, such as a Cu-Ni system, cools in non-equilibrium conditions. This causes the exterior of the material to solidify before the interior. Coring causes the centers of the grains to retain more of the higher melting temperature element. In this case, the dendrite arms formed from the exterior have a different composition than the alloy in the inner regions, resulting in a local compositional difference. It does not have good performance.

Coring is predominantly observed in alloys having a marked difference between liquidus and solidus temperatures. It is often being removed by subsequent annealing and/or hot-working. It is exploited in zone-refining techniques to produce high purity metals.

References

Beddoes, J. and Bibby, M.J. Principles of Metal Manufacturing Processes. Elsevier Butterworth-Heinemann, 1999. ISBN 0-340-73162-1

This article is issued from Wikipedia - version of the Tuesday, November 10, 2015. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.