Nickel–iron battery

Nickel–iron battery

Nickel–iron batteries manufactured between 1972 and 1975 under the "Exide" brand originally developed in 1901 by Thomas Edison.
Specific energy 19-25 [1] Wh/kg
Energy density 30[2] Wh/l
Specific power 100[3] W/kg
Charge/discharge efficiency 65%–80%[4]
Energy/consumer-price 1.5[2] – 6.6[3] Wh/US$
Self-discharge rate 20%[2][3] – 30%[3]/month
Time durability 30[4] – 50 years[2][5]
Cycle durability Repeated deep discharge does not reduce life significantly.[2][4]
Nominal cell voltage 1.2 V[3]
Charge temperature interval min. −40 °C – max.46 °C[6]

The nickel–iron battery (NiFe battery) is a rechargeable battery having nickel(III) oxide-hydroxide positive plates and iron negative plates, with an electrolyte of potassium hydroxide. The active materials are held in nickel-plated steel tubes or perforated pockets. It is a very robust battery which is tolerant of abuse, (overcharge, overdischarge, and short-circuiting) and can have very long life even if so treated.[7] It is often used in backup situations where it can be continuously charged and can last for more than 20 years. Due to its low specific energy, poor charge retention, and high cost of manufacture, other types of rechargeable batteries have displaced the nickel–iron battery in most applications.[8]

Uses

Nickel–iron batteries have long been used in European mining operations because of their ability to withstand vibration, high temperatures and other physical stress. They are being examined again for use in wind and solar power systems where battery weight is not important.

Many railway vehicles use Ni–Fe batteries.[9][10] Some examples are London underground electric locomotives and New York City Subway car – R62A.

The technology has regained popularity for off-the-grid applications where daily charging makes it an appropriate technology.[11][12][13]

Durability

The ability of these batteries to survive frequent cycling is due to the low solubility of the reactants in the electrolyte. The formation of metallic iron during charge is slow because of the low solubility of the ferrous hydroxide. While the slow formation of iron crystals preserves the electrodes, it also limits the high rate performance: these cells charge slowly, and are only able to discharge slowly.[7] Nickel–iron cells should not be charged from a constant voltage supply since they can be damaged by thermal runaway; the cell internal voltage drops as gassing begins, raising temperature, which increases current drawn and so further increases gassing and temperature.

Electrochemistry

The half-cell reaction at the positive plate:

2 NiOOH + 2 H2O + 2 e ↔ 2 Ni(OH)2 + 2 OH

and at the negative plate:

Fe + 2 OH ↔ Fe(OH)2 + 2 e

(Discharging is read left to right, charging is from right to left.)[14]

The open-circuit voltage is 1.4 volts, dropping to 1.2 volts during discharge.[7] The electrolyte mixture of potassium hydroxide and lithium hydroxide is not consumed in charging or discharging, so unlike a lead-acid battery the electrolyte specific gravity does not indicate state of charge.[7] The voltage required to charge the Ni-Fe battery is equal to or greater than 1.6 Volts per cell. [15] Lithium hydroxide improves the performance of the cell. The equalization charge voltage is 1.65 volts.

History

Swedish inventor Waldemar Jungner invented the nickel–cadmium battery in 1899. Jungner experimented with substituting iron for the cadmium in varying proportions, including 100% iron. Jungner discovered that the main advantage over the nickel–cadmium chemistry was cost, but due to the lower efficiency of the charging reaction and more pronounced formation of hydrogen (gassing), the nickeliron technology was found wanting and abandoned. Jungner had several patents for the iron version of his battery (Swedish pat.Nos 8.558/1897, 10.177/1899, 11.132/1899, 11.487/1899 and German Patent No.110.210 /1899). Moreover he had one patent for NiCd battery: Swed.pat No. 15.567/1899.[16]

Edison Storage Battery Company

Thomas Edison invented and commercialed NiFe in 1901 and offered it as the energy source for electric vehicles, such as the Detroit Electric and Baker Electric. Edison claimed the nickel–iron design to be, "far superior to batteries using lead plates and acid" (lead–acid battery). Edison had several patents: U.S. Patent 678,722/1901, U.S. Patent 692,507/1902, and German patent No 157.290/1901.[16]

Edison was disappointed that his battery was not adopted for starting internal combustion engines, and that electric vehicles went out of production only a few years after his battery was introduced. He developed the battery to be the battery of choice for electric vehicles which were the preferred transportation mode in the early 1900s (followed by gasoline and steam). Edison's batteries had a significantly higher energy density than the lead–acid batteries in use at the time, and could be charged in half the time, however they performed poorly at low temperatures and were more expensive.

Jungner's work was largely unknown in the US until the 1940s, when nickel–cadmium batteries went into production there. A 50 volt nickel–iron battery was the main power supply in the World War II German V-2 rocket (together with two 16 volt batteries which powered the four gyroscopes). A smaller version was used in the V-1 flying bomb. (viz. 1946 Operation Backfire blueprints.)

Edison's batteries were profitably made from about 1903 to 1972 by the Edison Storage Battery Company in East Orange, NJ. In 1972 the battery company was sold to the Exide Battery Corporation, which discontinued the product in 1975. The battery was widely used for railroad signaling, fork lift, and standby power applications.

Nickel–iron cells were made with capacities from 5 to 1250 Ah. Many of the original manufacturers no longer make nickel iron cells,[7] but production by new companies has started in several countries.

Three banks of plates inside a modern Nickel Iron battery

Plates

The active material of the battery plates is contained in a number of filled tubes or pockets, securely mounted in a supporting and conducting frame or grid. The support is in good electrical contact with the tubes. The grid is a light skeleton frame, stamped from thin sheet steel, with reinforcing width at the top. The grids – as also all metallic parts of the cells – are nickel plated to prevent corrosion. The elements must remain covered with electrolyte; if they dry out, the negative plates oxidize and require a very long charge.[15]

The elements of a nickel iron (NiFe) cell

The active material of the positive plates is a form of nickel hydrate. The tube retainers are made of thin steel ribbon, finely perforated and nickel plated, about 4 in. long and 1/4 in. and 1/8in. in diameter. The ribbon is spirally wound, with lapped seams, and the tubes reinforced at about 1/2 in. intervals with small steel rings. Into these tubes nickel hydrate and pure flake nickel are loaded in thin, alternating layers (about 350 layers of each to a tube) and are tightly packed or rammed. The purpose of the flake nickel is to make good contact between the nickel hydrate and the tubes, and thereby provide conductivity. The tubes, when filled and closed, are then mounted vertically into the grids.[15]

The Positive Plate is filled with nickel hydrate.

The active material of the negative plates is iron oxide. The retainer pockets are made of thin, finely perforated nickel-plated steel, of rectangular shape, 1/2 in. wide, 3 in long and 1/8 in. maximum thickness. The iron oxide, in finely powdered form is tightly rammed into these pockets, after which they are mounted into the grids. After mounting they are pressed, forcing them into close contact with the grids. This corrugates the sides of the pockets to provide a spring contact of the pocket with the active material.[15]

The active material of the negative plates iron oxide.

Charge

Charge/discharge involves the transfer of oxygen from one electrode to the other (from one group of plates to the other). Hence this type of cell is sometimes called an oxygenlift cell. In a charged cell the active material of the positive plates is superoxidized, and that of the negative plates is in a spongy or reduced state.[15]

If the normal capacity of the cell is insufficient, short intermediate high rate charges can be given provided that the temperature of the electrolyte does not exceed 115˚ F / 46˚ C. These short charges are very efficient and cause no injury. Rates up to three times normal can be employed for periods of 30 minutes.[15]

Fully charging a NiFe cell consists of seven hours at the normal cell rate. In service the amount of charge given is governed by the extent of the previous discharge. For example, a battery discharged one-half, allows a 3.5 hour normal rate charge. Overcharging wastes current and causes rapid evaporation of the water in the electrolyte.

For tapering rates of charge, an average of 1.67 volts should be maintained across the cell terminals throughout the charge. The current value at the start of the charge varies according to the electrical resistance. Absent resistance, the starting rate will be about twice normal and the finishing rate about 40% of normal.[15]

Discharge

Under discharge the positive plates are reduced ("deoxidized"); the oxygen, with its natural affinity for iron, goes to the negative plates, oxidizing them. It is permissible to discharge continuously at any rate up to 25% above normal, and for short periods at up to six times normal. When the normal discharge rate exceeds this value, abnormal voltage drops will occur.[15]

Electrolyte

The electrolyte does not enter into chemical combination to perform the functions of the cell, acting as a conveyor. Its specific gravity is unaffected during charge and discharge other than through evaporation and changes in temperature. Considerable variation in specific gravity is permissible, having influence only on battery efficiency.[15]

Environmental impact

Nickel–iron batteries do not have the lead or cadmium of the lead–acid and nickel–cadmium batteries, which require treatment as hazardous materials.

See also

References

  1. "Energy Density from NREL Testing by Iron Edison" (PDF). Retrieved 25 March 2014.
  2. 1 2 3 4 5 A description of the Chinese nickel–iron battery from BeUtilityFree
  3. 1 2 3 4 5 mpoweruk.com: Accumulator and battery comparisons (pdf)
  4. 1 2 3 Mpower: Nickel Iron Batteries
  5. "Nickel Iron Battery Frequently Asked Questions" BeUtilityFree
  6. Web archive backup: Edison Battery Booklet original instruction book for the Edison battery
  7. 1 2 3 4 5 David Linden, Thomas B. Reddy (ed). Handbook Of Batteries 3rd Edition, McGraw-Hill, New York, 2002 ISBN 0-07-135978-8, Chapter 25
  8. Ian Soutar (1 July 2010). "Nickel Iron Battery Association HomePage". Retrieved 30 October 2011.
  9. "Systematic design of an autonomous hybrid locomotive | EUrailmag". eurailmag.com. Retrieved 2013-04-17.
  10. "Magma #10 Project". azrymuseum.org. 2012-05-15. Retrieved 2013-04-17.
  11. Mother Earth News Issue #62 – March/April 1980
  12. http://www.nickel-iron-battery.com/
  13. Home Power Magazine Issue #80 December 2000/Jan 2001
  14. Electrochemistry Edison Cell (Iron-Nickel-Battery) – Model
  15. 1 2 3 4 5 6 7 8 9 "Manual of Storage Battery Practice" (pdf). The Committee on Electric Storage Batteries. Association of Edison Illuminating Companies. Retrieved 5 July 2012.
  16. 1 2 Journal of Power Sources, 12 (1984). pp 177–192.

External links