Flux method
Flux method is a method of crystal growth where the components of the desired substance are dissolved in a solvent (flux). The method is particularly suitable for crystals needing to be free from thermal strain. It takes place in a crucible made of highly stable, non-reactive material. For production of oxide crystals, metals such as platinum, tantalum, and niobium are common. Production of metallic crystals generally uses crucibles made from ceramics such as alumina, zirconia, and boron nitride. The crucibles and their contents are often isolated from the air for reaction, either by sealing them in a quartz ampoule or by using a furnace with atmosphere control. A saturated solution is prepared by keeping the constituents of the desired crystal and the flux at a temperature slightly above the saturation temperature long enough to form a complete solution. Then the crucible is cooled in order to allow the desired material to precipitate. Crystal formation can begin by spontaneous nucleation or may be encouraged by the use of a seed. As material precipitates out of the solution, the amount of solute in the flux decreases and the temperature at which the solution is saturated lowers. This process repeats itself as the furnace continues to cool until the solution reaches its melting point or the reaction is stopped artificially.
One advantage of this method is that the crystals grown often display natural facets, which often makes preparing crystals for measurement significantly easier. A disadvantage is that most flux method syntheses produce relatively small crystals. However, some materials such as the "115" heavy fermion superconductors (CeXIn5, X=Co,Ir,Rh) may grow up to a few centimeters.
External links
See also
- Crystallography
- Verneuil Process
- Czochralski process
- Epitaxy
- Crystal growth
- Chemical vapor deposition
- Hydrothermal synthesis
- Micro-pulling-down