Niobium dioxide
 | |
| Names | |
|---|---|
| IUPAC name
niobium(IV) oxide, niobium dioxide | |
| Other names
niobium(IV) oxide, columbium dioxide | |
| Identifiers | |
12034-59-2  | |
| EC Number | 234-809-7 |
| Jmol interactive 3D | Image |
| PubChem | 82839 |
| |
| |
| Properties | |
| NbO2 | |
| Molar mass | 124.91 g/mol |
| Appearance | bluish black |
| Melting point | 1,915 °C (3,479 °F; 2,188 K)[1] |
| Structure | |
| Tetragonal, tI96 | |
| I41/a, No. 88 | |
| Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa). | |
verify (what is  ?) | |
| Infobox references | |
Niobium dioxide, is the chemical compound with the formula NbO2. It is a bluish black non-stoichiometric solid with a composition range of NbO1.94-NbO2.09[1] It can be prepared by reacting Nb2O5 with H2 at 800–1350 °C.[1] An alternative method is reaction of Nb2O5 with Nb powder at 1100 °C.[2]
The room temperature form NbO2 has a tetragonal, rutile-like structure with short Nb-Nb distances indicating Nb-Nb bonding.[3] High temp form also has a rutile-like structure with short Nb-Nb distances.[4] Two high pressure phases have been reported one with a rutile-like structure, again with short Nb-Nb distances, and a higher pressure with baddeleyite-related structure.[5]
NbO2 is insoluble in water and is a powerful reducing agent, reducing carbon dioxide to carbon and sulfur dioxide to sulfur.[1] In an industrial process for the production of niobium metal, NbO2 is produced as an intermediate, by the hydrogen reduction of Nb2O5.[6] The NbO2 is subsequently reacted with magnesium vapour to produce niobium metal.[7]
References
- 1 2 3 4 C. K. Gupta, A. K. Suri, S Gupta, K Gupta (1994), Extractive Metallurgy of Niobium, CRC Press, ISBN 0-8493-6071-4
- ↑ Pradyot Patnaik (2002), Handbook of Inorganic Chemicals,McGraw-Hill Professional, ISBN 0-07-049439-8
- ↑ Wells A.F. (1984) Structural Inorganic Chemistry 5th edition Oxford Science Publications ISBN 0-19-855370-6
- ↑ Bolzan, A; Fong, Celesta; Kennedy, Brendan J.; Howard, Christopher J. (1994). "A Powder Neutron Diffraction Study of Semiconducting and Metallic Niobium Dioxide". Journal of Solid State Chemistry 113: 9. Bibcode:1994JSSCh.113....9B. doi:10.1006/jssc.1994.1334.
- ↑ Haines, J.; Léger, J. M.; Pereira, A. S. (1999). "High-pressure structural phase transitions in semiconducting niobium dioxide". Physical Review B 59 (21): 13650. Bibcode:1999PhRvB..5913650H. doi:10.1103/PhysRevB.59.13650.
- ↑ Patent EP1524252, Sintered bodies based on niobium suboxide, Schnitter C, Wötting G
- ↑ Method for producing tantallum/niobium metal powders by the reduction of their oxides by gaseous magnesium, US patent 6171363 (2001), Shekhter L.N., Tripp T.B., Lanin L.L. (H. C. Starck, Inc.)
| ||||||