Time-of-flight diffraction ultrasonics

A TOFD setup with transmit and receive probes. In this case the receive probe sees four indications: one from the lateral wave that has travelled along the upper surface, one from the wave that has reflected off the far surface, and two from the defect in the test object.

Typical TOFD data, created by aligning the data traces from the above figure vertically and colour-coding them for amplitude. The defect or discontinuity creates a characteristic parabolic indication, due to the apparent change in depth as the probes travel.

Manually-guided TOFD probes.

Time-of-flight diffraction (TOFD) method of ultrasonic testing is a sensitive and accurate method for the nondestructive testing of welds for defects. TOFD originated from tip diffraction techniques which were first published by Silk and Liddington^[1] in 1975 which paved the way for TOFD. Later works on this technique are given in a number of sources which include Harumi et al. (1989), Avioli et al. (1991), and Bray and Stanley (1997).

Bray and Stanley (1997) summarized TOFD as tip-diffraction techniques which utilized the principle that the tips of a crack when struck by a wave will diffract the signals back to the other location on the surface. The depth of these tips can be determined from the diffracted energy.^[2]

TOFD was invented in the UK in the 1970s initially as a research tool.^[3] The use of TOFD enabled crack sizes to be measured more accurately, so that expensive components could be kept in operation as long as possible with minimal risk of failure.

Principle of operation

Measuring the amplitude of reflected signal is a relatively unreliable method of sizing defects because the amplitude strongly depends on the orientation of the crack. Instead of amplitude, TOFD uses the time of flight of an ultrasonic pulse to determine the position and size of a reflector.

In a TOFD system, a pair of ultrasonic probes sits on opposite sides of a weld. One of the probes, the transmitter, emits an ultrasonic pulse that is picked up by the probe on the other side, the receiver. In undamaged pipes, the signals picked up by the receiver probe are from two waves: one that travels along the surface and one that reflects off the far wall. When a crack is present, there is a diffraction of the ultrasonic wave from the tip(s) of the crack. Using the measured time of flight of the pulse, the depth of a crack tips can be calculated automatically by simple trigonometry.

One of the limitation of TOFD is the "dead zone' where discontinuities are shadowed by the lateral wave signal.^[4] The depth of the dead zone depends of the probe separation and probe frequency. Typically the dead zone is 5 mm of the depth from the inspection surface. Calibration blocks with side drilled holes are shown in Reference ^[4] and ISO 10863 used to validate the "dead zone" and sizing accuracy..

Features

• A computerised and automated system for weld inspection.
• Probes are mounted on a buggy that travels along a weld, recording data as it moves.
• Compared to conventional methods of ultrasonic testing, TOFD is sensitive to cracks and measures their dimensions accurately.
• TOFD has two blind zones where it is not sensitive to defects, hence TOFD ought always to be supplemented by a conventional pulse-echo examination of the near and far walls. The pulse echo probes are commonly mounted on the same buggy as the TOFD probes.
• Requires ultrasound technicians with advanced training.

Standards

International Organization for Standardization (ISO)

• ISO/DIS 10863:11, Welding – Use of time-of-flight diffraction technique (TOFD) for examination of welds

European Committee for Standardization (CEN)

• EN 583-6, Non-destructive testing – Ultrasonic examination – Part 6: Time-of-flight diffraction technique as a method for detection and sizing of discontinuities
• EN 15617, Non-destructive testing of welds – Time-of-flight diffraction technique (TOFD) – Acceptance levels

Other sources

• Engineering Applications of Ultrasonic Time-of-Flight Diffraction, 2nd ed., J. P. Charlesworth and J. A. G. Temple, Research Studies Press, 2002.

References

1. M.G. Silk, B.H. Lidington. "The potential of scattered or diffracted ultrasound in the determination of crack depth". Non-Destructive Testing, Volume 8, Issue 3, June 1975, pp. 146–51, ISSN 0029-1021, 10.1016/0029-1021(75)90024-9. Retrieved 23 September 2011.
2. Bray, Don (2003). Ultrasonic Nondestructive Evaluation Engineering and Biological Material Characterization. ISBN 978-0-8493-1462-9.
3. J. P. Charlesworth, J. A. G. Temple (2001). Engineering Applications of Ultrasonic Time-of-Flight Diffraction Second Edition. Research Studies Press LTD. p. 254. ISBN 0-86380-239-7.
4. ASTM, E2373 (2012). Nondestructive Testing Vol 3.03, Standard Practice for Use of Time of Flight Diffraction (TOFD) Technique. West Conshohocken, PA: American Society for Testing of Materials. pp. 1251–62. ISBN 9780803187290.

External links

• TOFD Inspection Systems
• TOFD: – An Alternate Non-Destructive Testing Procedure to Replace Traditional Methods
• NDT.net Database Search returns over 500 hits for the search term 'TOFD'
• TOFD Principles on NDT.net