Roman concrete

The Pantheon in Rome, is an example of Roman concrete construction.

Roman concrete, also called opus caementicium, was a material used in construction during the late Roman Republic through the whole history of the Roman Empire. Roman concrete was based on a hydraulic-setting cement. Recently, it has been found that it materially differs in several ways to modern Portland cement. It is widely acknowledged that Roman concrete is the most durable type of cement of its kind due to its use of volcanic ash. By the middle of the 1st century, the material was used frequently as brick-faced concrete, although variations in aggregate allowed different arrangements of materials. Further innovative developments in the material, called the Concrete Revolution, contributed to structurally complicated forms, such as the Pantheon dome, the world's largest unreinforced concrete dome.[1]

Roman concrete was normally faced with stone or brick, and interiors might be further decorated by stucco, fresco paintings, or thin slabs of fancy coloured marbles. Made up of aggregate and cement, like modern concrete, it differed in that the aggregate pieces were typically far larger than in modern concrete, often amounting to rubble, and as a result it was laid rather than poured.[2] Some Roman concretes were able to be set underwater, which was very useful for bridges and other waterside construction.

It is uncertain when it was developed, but it was clearly in widespread and customary use from about 150 BC, but some scholars believe it was developed a century before that.[3]

Historic references

Caesarea is the earliest known example to have used underwater Roman concrete technology on such a large scale.

Vitruvius, writing around 25 BC in his Ten Books on Architecture, distinguished types of aggregate appropriate for the preparation of lime mortars. For structural mortars, he recommended pozzolana, which are volcanic sands from the sandlike beds of Pozzuoli brownish-yellow-gray in color near Naples and reddish-brown at Rome. Vitruvius specifies a ratio of 1 part lime to 3 parts pozzolana for cements used in buildings and a 1:2 ratio of lime to pulvis Puteolanus for underwater work, essentially the same ratio mixed today for concrete used at sea.[4]

By the middle of the 1st century, the principles of underwater construction in concrete were well known to Roman builders. The city of Caesarea was the earliest known example to have made use of underwater Roman concrete technology on such a large scale.[5]

Rebuilding Rome after the fire in 64 AD, which destroyed large portions of the city, the new building code by Nero consisted of largely brick-faced concrete. This appears to have encouraged the development of the brick and concrete industries.[5]

Example of opus caementicium on a tomb on the ancient Appian Way in Rome. The original covering has been removed.

Material properties

Roman concrete, like any concrete, consists of an aggregate and hydraulic mortar – a binder mixed with water that hardens over time. The aggregate varied, and included pieces of rock, ceramic tile, and brick rubble from the remains of previously demolished buildings. Reinforcing elements, such as steel rebar, were not used.

Gypsum and lime were used as binders. Volcanic dusts, called pozzolana or "pit sand", were favored where they could be obtained. Pozzolana makes the concrete more resistant to salt water than modern-day concrete.[6] The pozzolanic mortar used had a high content of alumina and silica.

Concrete, and in particular, the hydraulic mortar responsible for its cohesion, was a type of structural ceramic whose utility derived largely from its rheological plasticity in the paste state. The setting and hardening of hydraulic cements derived from hydration of materials and the subsequent chemical and physical interaction of these hydration products. This differed from the setting of slaked lime mortars, the most common cements of the pre-Roman world. Once set, Roman concrete exhibited little plasticity, although it retained some resistance to tensile stresses.

The setting of pozzolanic cements has much in common with setting of their modern counterpart, Portland cement. The high silica composition of Roman pozzolana cements is very close to that of modern cement to which blast furnace slag, fly ash, or silica fume have been added.

Compressive strengths for modern Portland cements are typically at the 50 MPa level and have improved almost ten-fold since 1860.[7] There are no comparable mechanical data for ancient mortars, although some information about tensile strength may be inferred from the cracking of Roman concrete domes. These tensile strengths vary substantially from the water/cement ratio used in the initial mix. At present, there is no way of ascertaining what water/cement ratios the Romans used, nor are there extensive data for the effects of this ratio on the strengths of pozzolanic cements.[8]

Seismic technology

For an environment as prone to earthquakes as the Italian peninsula, interruptions and internal constructions within walls and domes created discontinuities in the concrete mass. Portions of the building could then shift slightly when there was movement of the earth to accommodate such stresses, enhancing the overall strength of the structure. It was in this sense that bricks and concrete were flexible. It may have been precisely for this reason that, although many buildings sustained serious cracking from a variety of causes, they continue to stand to this day.[9]

Another technology used to improve the strength and stability of concrete was its gradation in domes. One example included the Pantheon, where the aggregate of the upper dome region consisted of alternating layers of light tuff and pumice, giving the concrete a density of 1,350 kg/m3. The foundation of the structure used travertine as an aggregate, having a much higher density of 2,200 kg/m3.[10]

Modern use

Recent scientific breakthroughs examining Roman concrete are gathering media and industry attention.[11][12] Because of its unusual durability, longevity and lessened environmental footprint, corporations and municipalities are starting to explore the use of Roman-style concrete in North America, substituting the volcanic ash with coal fly ash that has similar properties. Proponents claim that concrete made with fly ash can save up to 60% of the cost because of less aggregate use, lessen the environmental footprint by having a lower cooking temperature, with a much longer lifespan.[13] Usable examples of Roman concrete exposed to harsh marine environments have been found to be 2000 years old with little or no wear.[14]

See also

Literature

References

  1. ↑ Moore, David (February 1993). "The Riddle of Ancient Roman Concrete". S Dept. of the Interior, Bureau of Reclamation, Upper Colorado Region. www.romanconcrete.com. Retrieved 20 May 2013.
  2. ↑ Henig, Martin (ed), A Handbook of Roman Art, p. 30, Phaidon, 1983, ISBN 0714822140
  3. ↑ Boëthius, Axel, Ling, Roger, Rasmussen, Tom, Etruscan and Early Roman Architecture, pp. 128-129, Yale/Pelican history of art, 1978, Yale University Press, ISBN 0300052901, 9780300052909, google books
  4. ↑ Heather Lechtman and Linn Hobbs "Roman Concrete and the Roman Architectural Revolution", Ceramics and Civilization Volume 3: High Technology Ceramics: Past, Present, Future, edited by W.D. Kingery and published by the American Ceramics Society, 1986; and Vitruvius, Book II:v,1; Book V:xii2
  5. 1 2 Lechtman and Hobbs "Roman Concrete and the Roman Architectural Revolution"
  6. ↑ Wayman, Erin. “The Secrets of Ancient Rome’s Buildings.” Smithsonian.com. 16 November 2011. Retrieved 24 April 2012.
  7. ↑ N. B. Eden and J.E. Bailey, "Mechanical Properties and Tensile Failure Mechanism of a High Strength Polymer Modified Portland Cement," J. Mater. Sci., 19, 2677–85 (1984); and Lechtman and Hobbs "Roman Concrete and the Roman Architectural Revolution"
  8. ↑ Lechtman and Hobbs "Roman Concrete and the Roman Architectural Revolution"; see also: C. A. Langton and D. M. Roy, "Longevity of Borehole and Shaft Sealing Materials: Characterization of Ancient Cement Based Building Materials," Mat. Res. Soc. SYmp. Proc. 26, 543–49 (1984); and Topical Report ONWI-202, Battelle Memorial Institute, Office of Nuclear Waste Isolation, Distribution Category UC-70, National Technical Information Service, U.S. Department of Commerce, 1982.)
  9. ↑ W. L. MacDonald, The Architecture of the Roman Empire, rev. ed. Yale University Press, New Haven, 1982, fig. 131B; Lechtman and Hobbs "Roman Concrete and the Roman Architectural Revolution"
  10. ↑ K. de Fine Licht, The Rotunda in Rome: A Study of Hadrian's Pantheon. Jutland Archaeological Society, Copenhagen, 1968, pp. 89–94, 134–35; and Lechtman and Hobbs "Roman Concrete and the Roman Architectural Revolution"
  11. ↑ Sezen Soyer-Uzun, Sejung Rosie Chae, Chris J. Benmore, Hans-Rudolf Wenk, Paulo J. M. Monteiro, "Compositional Evolution of Calcium Silicate Hydrate (C-S-H) Structures by Total X-Ray Scattering", Journal of the American Ceramic Society, Volume: 95 Issue: 2 Pages: 793-798, FEB 2012
  12. ↑ "Fixing Canada’s Infrastructure with Volcanoes". Trebuchet Capital Partners Research.
  13. ↑ Compositional Evolution of Calcium Silicate Hydrate (C-S-H) Structures by Total X-Ray Scattering
  14. ↑ M. D. Jackson, S. R. Chae, R. Taylor, C. Meral, J. Moon, S. Yoon, P. Li, A. M. Emwas, G. Vola, H.-R. Wenk, and P. J. M. Monteiro, Unlocking the secrets of Al-tobermorite in Roman seawater concrete, American Mineralogist, Volume 98, pages 1669–1687, 2013.

External links


This article is issued from Wikipedia - version of the Sunday, March 27, 2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.