Wetsuit

This article is about wetsuits and their use in a range of water sports. For protective clothing specialized for scuba diving, see Diving suit. For the G.I. Joe character, see Wet Suit (G.I. Joe). For The Vaccines song, see Wetsuit / Tiger Blood.
Two women in wetsuits standing on a beach. Left is wearing a shortie suit, also called a "spring suit", which has short legs and sleeves, with boots. Right is wearing a full length one piece suit with back zipper, also called a "steamer".
Spring suit (shorty) and steamer (full suit).
Jacket and trousers of a wetsuit displayed on a cloth, The jacket has a beavertail crotch strap with metal twistlock fasteners.
Beavertail two-piece wetsuit with twistlock fasteners and offset 3/4 zipper

A wetsuit is a garment, usually made of foamed neoprene, which is worn by surfers, divers, windsurfers, canoeists, and others engaged in water sports, providing thermal insulation, abrasion resistance and buoyancy. The insulation properties depend on bubbles of gas enclosed within the material, which reduce its ability to conduct heat. The bubbles also give the wetsuit a low density, providing buoyancy in water.

Hugh Bradner, a University of California, Berkeley physicist invented the modern wetsuit in 1952. Wetsuits became available in the mid-1950s and evolved as the relatively fragile foamed neoprene was first backed, and later sandwiched, with thin sheets of tougher material such as nylon or later Lycra/Spandex. Improvements in the way joints in the wetsuit were made by gluing, taping and blindstitching, helped the suit to remain waterproof and reduce flushing, the replacement of water trapped between suit and body by cold water from the outside.[1] Further improvements in the seals at the neck, wrists and ankles produced a suit known as a "semi-dry".

Different types of wetsuit are made for different uses and for different temperatures.[2] Suits range from a thin (2 mm or less) "shortie", covering just the torso, to a full 8 mm semi-dry, usually complemented by neoprene boots, gloves and hood.

Uses

Wetsuits are used for thermal insulation for activities where the user is likely to be immersed in water, or frequently doused with heavy spray, often approacing from near-horizontal directions, where normal wet-weather clothing is unlikely to keep the water out. Activities include underwater diving, sailing, sea rescue operations, surfing, river rafting, whitewater kayaking and in some circumstances, endurance swimming.

In open water swimming events the use of wetsuits is controversial, as some participants claim that wetsuits are being worn for competitive advantage and not just for warmth.[3]

Unlike triathlons, which allow swimmers to wear wetsuits when the water is below a certain temperature (the standard is 78 °F (26 °C) at the surface or up to 84 °F (29 °C) for unofficial events.[4]), most open water swim races either do not permit the use of wetsuits (usually defined as anything covering the body above the waist or below the knees), or put wetsuit-clad swimmers in a separate category and/or make them ineligible for race awards. This varies by locales and times of the year, where water temperatures are substantially below comfortable.

Insulation

the cuff of a semi-dry suit, showing an inner and outer seal
Semi-dry cuffs are designed to fit close to the skin in order to minimise flushing.

Still water (without currents or convection) conducts heat away from the body by pure thermal diffusion, approximately 20 to 25 times more efficiently than still air.[2][5] Water has a thermal conductivity of 0.58 Wm−1K−1 while still air has a thermal conductivity of 0.024 Wm−1K−1,[6] so an unprotected individual can succumb to hypothermia even in warmish water on a warm day.[7] Wetsuits are made of closed-cell, foam neoprene, a synthetic rubber that contains small bubbles of nitrogen gas when made for use as wetsuit material (neoprene may also be manufactured without foaming for many other applications where insulating qualities are not important). Nitrogen, like most gases, has very low thermal conductivity compared to water or to solids,[note 1] and the small and enclosed nature of the gas bubbles minimizes heat transport through the gas by convection in the same way that cloth fabrics or feathers insulate by reducing convection of enclosed air spaces. The result is that the gas filled cavities force heat to transfer mostly by conduction, and partly through bubbles of entrapped gas, thereby greatly reducing heat transfer from the body (or from the layer of warmed water trapped between the body and the wetsuit) to the colder water surrounding the wetsuit.

Uncompressed foam neoprene has a typical thermal conductivity in the region of 0.054 Wm−1K−1, which produces about twice the heat loss of still air, or one-tenth the loss of water. However at a depth of 15 metres (50 ft) of water, the thickness of the neoprene will be halved and its conductivity will be increased by 50%, allowing heat to be lost at three times the rate at the surface.[8]

A wetsuit must have a snug fit to work efficiently when immersed; too loose a fit, particularly at the openings (wrists, ankles, neck and overlaps) will allow cold water from the outside to enter continuously.[1] Flexible seals at the suit cuffs aid in preventing heat loss in this fashion.

Foamed neoprene is very buoyant, helping swimmers to stay afloat, and for this reason divers need to carry extra weight based on the volume of their suit to achieve neutral buoyancy near the surface.[2] However, the suit loses buoyancy and thermal protection as the bubbles in the neoprene are compressed at depth[9][note 2] and this can be corrected by inflation of the buoyancy compensator.

Semi-dry suits

Detail of the zipper of a semi-dry wetsuit, showing one end of an open zipper and the neoprene flaps that cover it on the inside and outside of the suit to protect the zipper, improve comfort, and reduce leakage through the closed zip.
Detail showing zipper attachment, internal flap and cover flap of semi-dry suit

Semi-dry suits are effectively a wetsuit with reasonably effective seals at wrist, neck and ankles and zipper. The seals limit the amount of water entering and leaving the suit. The wearer gets wet in a semi-dry suit but the water that enters is soon warmed up and does not leave the suit readily, so the wearer remains warm. The trapped layer of water does not add significantly to the suit's insulating ability. Any residual water circulation past the seals still causes heat loss. Semi-dry suits are cheap and simple compared to dry suits. They are usually made from thick Neoprene, which provides good thermal protection at shallow depth, but lose buoyancy and thermal protection as the gas bubbles in the Neoprene compress at depth. Semi-dry suits can come in various configurations including a one-piece full-body suit or two pieces, made of 'long johns' and a separate 'jacket'. The zipper is commonly across the shoulders on the back, but other arrangements have been used. Semi dry suits do not usually include boots, so a separate pair of wetsuit boots are worn. They are most suitable for use where the water temperature is between 10 and 20 °C (50 and 68 °F).

Heated suits

Electrically heated wetsuits are also available on the market. These suits have special heating panels integrated in the back of the wetsuit. The power for heating comes from batteries also integrated into the wetsuit.[10] Even more versatile is the heated neoprene vest that functions the same as the heated wetsuit but can be worn under any type of wetsuit.

Wetsuits heated by a flow of hot water piped from the surface are standard equipment for commercial diving in cold water, particularly where the heat loss from the diver is increased by use of helium based breathing gases.[11] Hot water suits are a loose fit as there is a constant supply of heated water piped into the suit which must escape to allow even flow distribution. Flushing with cold water is prevented by the constant outflow of heating water.

History

Origins

Woman wearing "smoothskin" wetsuit with "beavertail" and twistlock fasteners
See also: Diving suit

In 1952, UC Berkeley and subsequent UC San Diego SIO physicist Hugh Bradner, who is considered to be the original inventor[12] and "father of the modern wetsuit,"[12] had the insight that a thin layer of trapped water could be tolerated between the suit fabric and the skin, so long as insulation was present in the fabric in the form of trapped bubbles. In this case, the water would quickly reach skin temperature and the air in the fabric would continue to act as the thermal insulation to keep it that way. In the popular mind, the layer of water between skin and suit has been credited with providing the insulation. But as his letter notes, Dr. Bradner clearly understood the suit did not need to be wet because it isn't the water that provides the insulation but rather the gas in the suit fabric.[12][13] He initially sent his ideas to Lauriston C. "Larry" Marshall. Marshall was involved in a U.S. Navy/National Research Council Panel on Underwater Swimmers.[14] However, it was Willard Bascom, an engineer at the Scripps Institution of Oceanography in La Jolla, California, who suggested neoprene as a feasible material to Bradner.[13]

However, Bradner and Bascom were not overly interested in profiting from their design and were unable to successfully market a version to the public.[13] They attempted to patent their neoprene wetsuit design, but their application was rejected because the design was viewed as too similar to a flight suit.[13] The United States Navy also turned down Bradner's and Bascom's offer to supply its swimmers and frogmen with the new wetsuits due to concerns that the gas in the neoprene component of the suits might make it easier for naval divers to be detected by underwater sonar.[13] The first written documentation of Bradner's invention was in a letter to Marshall, dated June 21, 1951.[14]

Jack O'Neill started using closed-cell neoprene foam which was shown to him by his bodysurfing friend, Harry Hind, who knew of it as an insulating material in his laboratory work. After experimenting with the material and finding it superior to other insulating foams, O'Neill founded the successful wetsuit manufacturing company called O'Neill in a garage in 1952, later relocating to Santa Cruz, California[15] in 1959 with the motto "It's Always Summer on the Inside".[16][17] Bob and Bill Meistrell, from Manhattan Beach, California, also started experimenting with neoprene around 1953. They started a company which would later be named Body Glove.

Neoprene was not the only material used in early wetsuits, particularly in Europe. The French-made Pêche-Sport Suit and the UK-made Siebe Gorman Swimsuit were both made out of sponge rubber. The Heinke Dolphin Suit of the same period, also made in England, came in a green male and a white female version, both manufactured from natural rubber lined with stockinet.

Development of suit design

Originally, wetsuits were made only with raw sheets of foam-rubber neoprene that did not have any backing material. This type of suit required extra caution while pulling it on because the raw foam-rubber by itself is both fragile and sticky against bare skin. Stretching and pulling excessively easily caused these suits to be torn in half. This was somewhat remedied by thoroughly powdering the suit and the diver's body with talc to help the rubber slide on more easily.

Backing materials first arrived in the form of nylon sheeting applied to one side of the neoprene. This allowed a swimmer to pull on the suit relatively easily since the tough nylon took most of the strain of pulling on the suit, but the suit still had the black sheet rubber exposed on the outside and the nylon was very stiff and rigid, limiting flexibility. A small strip reversed with the rubber against the skin could help provide a sealing surface to keep water out around the neck, wrists, and ankles.

In the early 1960s, the British Dunlop Sports Company brought out its yellow Aquafort neoprene wetsuit, whose high visibility was designed to improve diver safety. However, the line was discontinued after a short while and wetsuits reverted to their black uniformity. The colorful wetsuits seen today first arrived in the 1970s when double-backed neoprene was developed. Now the foam-rubber was sandwiched between two protective fabric outer layers, greatly increasing the tear-resistance of the material. An external layer also meant that decorative colors, logos, and patterns could be made with panels and strips sewn into various shapes. This growth from bare flat black rubber to full color took off in the 1980s with brilliant fluorescent colors common on many suits.

Improvements in suit assembly

The first suits used traditional sewing methods to simply overlap two strips of rubber and sew them together. In a rubber wetsuit this does not work well for a number of reasons, the main one being that punching holes straight through both layers of foam for the thread opens up passages for water to flow in and out of the suit. The second problem is that the stretching of the foam tended to enlarge the needle holes when the suit was worn. This meant that a wetsuit could be very cold all along the seams of the suit. And although the sewn edge did hold the two pieces together, it could also act as a perforated tear edge, making the suit easier to tear along the seams when putting it on and taking it off.

When nylon-backed neoprene appeared, the problem of the needle weakening the foam was solved, but still the needle holes leaked water along the seams.

Seam taping

To deal with all these early sewing problems, taping of seams was developed. The tape is a strong nylon cloth with a very thin but solid waterproof rubber backing. The tape is applied across the seam and bonded either with a chemical solvent or with a hot rolling heat-sealer to melt the tape into the neoprene.

With this technology, the suit could be sewn and then taped, and the tape would cover the sewing holes as well as providing some extra strength to prevent tearing along the needle holes.

When colorful double-backed designer suits started appearing, taping moved primarily to the inside of the suit because the tape was usually very wide, jagged, black, and ugly, and was hidden within the suit and out of sight.

Many 1960s and 1970s wetsuits were black with visible yellow seam taping. The yellow made the divers more easily seen in dark low-visibility water. To avoid this problem O'Neill fabricators developed a seam-tape which combined a thin nylon layer with a polyester hemming tape. Applied over the interior of the glued & sewn seam, then anneal bonded with a hand held teflon heating iron produced a seam that was both securely sealed and much stronger.

Seam gluing

Another alternative to sewing was to glue the edges of the suit together. This created a smooth, flat surface that did not necessarily need taping, but unfortunately raw foam glued to foam is not a strong bond and still prone to tearing.

Most early wetsuits were fabricated completely by hand, which could lead to sizing errors in the cutting of the foam sheeting. If the cut edges did not align correctly or the gluing was not done well, there might still be water leakage along the seam.

Initially suits could be found as being sewn only, glued only, taped only, then also sewn and taped, or glued and taped, or perhaps all three.

Blindstitch revolution

Sometime after nylon-backed neoprene appeared, the blind stitch method was developed. A blindstitch sewing machine uses a curved needle, which does not go all the way through the neoprene but just shallowly dips in behind the fabric backing, crosses the glue line, and emerges from the surface on the same side of the neoprene.[1] This is similar to the overlock stitching used for teeshirts and other garments made from knitted fabrics.

The curved needle allows the fabric backing to be sewn together without punching a hole completely through the neoprene, and thereby eliminating the water-leakage holes along the seam. Blindstitch seams also lay flat, butting up the edge of one sheet against another, allowing the material to lay flatter and closer to the skin. For these reasons blindstitching rapidly became the primary method of sewing wetsuits together, with other methods now used mainly for decorative or stylistic purposes.

Further advances in suit design

Highly elastic fabrics such as Lycra/Spandex have mostly replaced raw nylon backing, since the nylon by itself cannot be stretched and makes the neoprene very stiff. Incorporating Lycra into the backing permits a large amount of stretching that does not damage the suit, and allowed suits to become closer fitting.

After the development of double-backed neoprene, singled-backed neoprene still had its uses for various specific purposes. For example a thin strip of single-backed wrapped around the leg, neck, and wrist openings of the suit creates a seal that greatly reduces the flushing of water in and out of the suit as the person's body moves. But since the strip is very narrow, it does not drag on the skin of the wearer and thus makes the suit easy to put on and remove.

As wetsuit manufacturers continued to design suits, they found ways that the materials could be further optimized and customized. The O'Neill Animal Skin created in 1974 by then Director of Marketing, E.J. Armstrong, was one of the first designs combining a turtle-neck based on the popular Sealsuit with a flexible lightweight YKK horizontal zipper across the back shoulders similar in concept to the inflatable watertight Supersuit ( developed by Jack O'Neill in the late 1960s ). The Animal Skin eventually evolved molded rubber patterns bonded onto the exterior of the neoprene sheeting ( a technique E.J. Armstrong perfected for application of the moulded raised rubber Supersuit logo to replace the standard flat decals ). This has been carried on as stylized reinforcing pads of rubber on the knees and elbows to protect the suit from wear, and allows logos to be directly bonded onto raw sheet rubber. Additionally, the Animal Skin's looser fit allowed for the use of a supplemental vest in extreme conditions.

In the early 1970s Gul Wetsuits pioneered the one-piece wetsuit named as the steamer. Its name was given because of the steam given off from the suit once taken off allowing heat and water held inside to escape. Today one-piece wetsuits are still sometimes referred to as 'Steamers'.[18]

In recent years, manufacturers have experimented by combining various materials with neoprene to lend additional warmth or flexibility to their suits. These include, but are not limited to, Spandex, and wool.

Precision computer-controlled cutting and assembly methods, such as water-jet cutting, have allowed ever greater levels of seam precision, permitting designers to use many small individual strips of different colors while still keeping the suit free of bulging and ripples from improper cutting and sewing. Further innovations in CAD (Computer Aided Design) technology allow precision cutting for custom-fit wetsuits.

Return of single-backed neoprene

As wetsuits continued to evolve, their use was explored in other sports such as open-water swimming and triathlons. Although double-backed neoprene is strong, the cloth backing is rough and creates a large amount of drag in the water, slowing down the swimmer. A single-backed suit meanwhile has a very smooth, slick exterior permitting water to slide easily over the bare neoprene.[1] With the advances of elastic Lycra backings and blindstitching, single-backed neoprene suits could now be made that outperformed the early cousins from the 1970s. Other developments in single-backed wetsuits include the suits designed for free-diving and spearfishing. Single lined neoprene is more flexible than double lined. To achieve flexibility and low bulk for a given warmth of suit, they are unlined inside, and the smooth surface of the neoprene is removed mechanically to reveal a rougher "open cell" surface which adheres closely to the skin and reduces flushing of the suit. The lined outer surface may be printed with camouflage patterns for spearfishing.

Some triathlon wetsuits go further, and use rubber-molding and texturing methods to roughen up the surface of the suit on the forearms, to increase forward drag and help pull the swimmer forwards through the water. Extremely thin 1 mm neoprene is also often used in the under-arm area, to decrease stretch resistance and reduce strain on the swimmer when they extend their arms out over their head.

Wetsuits used for caving are often single-backed with a textured surface known as "sharkskin" which is a thin layer where the neoprene is less expanded. This makes it more abrasion resistant for squeezing between rocks and doesn't get torn in the way that fabric does.

Another reason to eliminate the external textile backing is to reduce water retention which can increase evaporative cooling and wind chill in suits used mainly out of the water.

Types

Sleeveless tunic in thin but abrasion resistant neoprene, with integral hood, two cargo pochets on the sides of the thighs, cross-chest zip closure, front pocket on the torso and opening for access to a dry-suit inflation valve. The tunic is suitable for wearing over most one-piece wetsuits for extra insulation, but mainly to support the cargo pockets and hood.
Hooded tunic with cargo pockets

Different shapes of wetsuit are available, in order of coverage:

Some suits are arranged in two parts; the jacket and long johns can be worn separately in mild conditions or worn together to provide two layers of insulation around the torso in cold conditions. Typically, two-piece cold water wetsuits have 10 to 14 mm of material around the torso and 5 to 7 mm for the extremities.

Thickness

Wetsuits are available in different thicknesses depending on the conditions for which they are intended.[2] The thicker the suit, the warmer it will keep the wearer, but the more it will restrict movement. Because wetsuits offer significant protection from jellyfish, coral, sunburn and other hazards, many divers opt to wear a thin suit which provides minimal insulation (often called a "bodysuit") even when the water is warm enough to comfortably forego insulating garments.[2] A thick suit will restrict mobility, and as the thickness is increased the suit may become impractical, depending on the application. This is one reason why drysuits may be preferable for some applications. A wetsuit is normally specified in terms of its thickness and style. For instance, a wetsuit with a torso thickness of 5 mm and a limb thickness of 3 mm will be described as a "5/3". With new technologies the neoprene is getting more flexible. Modern 4/3 wetsuits, for instance, may feel as flexible as a 3/2 of only a few years ago. Some suits have extra layers added for key areas such as the lower back. Improved flexibility may come at the cost of greater compressibility, which reduces insulation at depth, but this is only important for diving.

Surface finish

A specialized kind of wetsuit, with a very smooth (and somewhat delicate) outer surface is used for long distance swimming and triathlon. These are designed to maximize the mobility of the limbs while providing both warmth and buoyancy.[1]

Closures

Zippers are often used for closure or for providing a close fit at the wrists and ankles, but they also provide leakage points for water. Jackets may have a full or partial front zipper, or none at all. Full body suits may have a vertical back zipper, a cross-shoulder zipper or a vertical front zipper. Each of these arrangements has some advantages and some disadvantages:

Sizing and fit

Wetsuits that fit too tightly can cause difficulty breathing or even acute cardiac failure,[2] and a loose fit allows considerable flushing which reduces effectiveness of insulation, so a proper fit is important. The quality of fit is most important for diving as this is where the thickest suits are used and the heat loss is potentially greatest. A diving wetsuit should touch the skin over as much of the body that it covers as comfortably possible, both when the wearer is relaxed and when exercising. This is difficult to achieve and the details of style and cut can affect the quality of fit. Gaps where the suit does not touch the skin will vary in volume as the diver moves and this is a major cause of flushing.

Wetsuits are made in several standard adult sizes and for children. Custom fitted suits are produced by many manufacturers to provide a better fit for people for whom a well fitting off-the shelf suit is not available.

Accessories

A pair of neoprene wetsuit gloves
Neoprene wetsuit gloves
A pair of wetsuit boots showing hard soles and reinforcement in high-wear areas at the toe and heel, and side zipper closure with a thin neoprene gusset behind the zipper to reduce leakage.
Hard soled wetsuit boots with zip fasteners

Usually a wetsuit has no covering for the feet, hands or head, and the diver must wear separate neoprene booties, gloves and hood for additional insulation and environmental protection. Other accessories to the basic suit include pockets for holding small items and equipment, and knee-pads, to protect the knee area from abrasion and tearing, usually used by working divers. Suits may have abrasion protection pads in other areas depending on the application.

Using hoods: in the thermal balance of the human body, the heat loss over the head is at least 20% of the whole balance. Thus, for the sake of thermal protection of the diver, wearing a well-fitting hood is useful, even at fairly moderate water temperatures. Hoods have been reported to cause claustrophobia[2] in a minority of users, sometimes due to poor fit. The hood should not fit too tightly round the neck. Flushing in the neck area can be reduced by using a hood attached to the top part of the suit, or by having sufficient overlap between the hood and the top part of the suit to constrain flow between the two parts. This can be achieved by tucking a circular flap at the base of the neck of the hood under the top of the suit before closing the zip, or by having a high neck on the suit.

See also

Notes

  1. Nitrogen has a thermal conductivity of 0.024 Wm−1K−1, the same as air – "Thermal conductivity of some common materials". The Engineering ToolBox. 2005. Retrieved August 12, 2009.
  2. Non-foamed solid neoprene has a thermal conductivity between 0.15 Wm−1K−1 and 0.45 Wm−1K−1 depending on type, not very different from water – Elert, Glenn (2008). "Conduction". The Physics Hypertextbook. Retrieved April 27, 2014.

References

Wikimedia Commons has media related to Wetsuits.
Look up wetsuit in Wiktionary, the free dictionary.
  1. 1 2 3 4 5 "How Wetsuits Work". Lomo Watersport. Retrieved February 20, 2010.
  2. 1 2 3 4 5 6 7 Williams, Guy; Acott, Chris J (2003). "Exposure suits: a review of thermal protection for the recreational diver". South Pacific Underwater Medicine Society journal 33 (1). ISSN 0813-1988. OCLC 16986801. Retrieved 2011-04-13.
  3. Kent, Hazen The Rap on Wetsuits in Triathlon trinewbies.com
  4. http://triathlonwetsuitstore.com/at-what-temps-can-you-use-a-wetsuit/
  5. Ross Tucker, PhD; Jonathan Dugas, PhD (January 29, 2008). "Exercise in the Cold: Part II A physiological trip through cold water exposure". The Science of Sport. Retrieved November 26, 2009. Cite uses deprecated parameter |coauthors= (help)
  6. "Thermal conductivity of some common materials". The Engineering ToolBox. 2005. Retrieved August 12, 2009.
  7. Robert A. Clark; et al. Open Water Diver manual (in Dutch) (1st ed.). Scuba Schools International GmbH. pp. 1–9. ISBN 1-880229-95-1.
  8. Bardy, Erik; Mollendorf, Joseph; Pendergast, David (October 21, 2005). "Thermal conductivity and compressive strain of foam neoprene insulation under hydrostatic pressure". Journal of Physics D: Applied Physics 38 (20): 3832–3840. doi:10.1088/0022-3727/38/20/009.
  9. Monji K, Nakashima K, Sogabe Y, Miki K, Tajima F, Shiraki K (1989). "Changes in insulation of wetsuits during repetitive exposure to pressure". Undersea Biomed Res 16 (4): 313–9. PMID 2773163. Retrieved 2011-04-13.
  10. Leckart, Steven (2010-04-15). "Rip Curl H-Bomb: Heated Wetsuit Stokes Your Fanny When Hanging 10". Wired (website). Retrieved 2013-06-16.
  11. Bevan, John, ed. (2005). "Section 5.4". The Professional Divers's Handbook (second ed.). 5 Nepean Close, Alverstoke, GOSPORT, Hampshire PO12 2BH: Submex Ltd. p. 242. ISBN 978-0950824260.
  12. 1 2 3 Taylor, Michael (May 11, 2008). "Hugh Bradner, UC's inventor of wetsuit, dies". San Francisco Chronicle. Retrieved May 23, 2008.
  13. 1 2 3 4 5 Taylor, Michael (May 21, 2008). "Hugh Bradner, Physicist who worked on the Manhattan Project and invented the neoprene wetsuit". The Times (London). Retrieved May 23, 2008.
  14. 1 2 Rainey, C. "Wet Suit Pursuit: Hugh Bradner's Development of the First Wet Suit" (PDF). UC San Diego, Scripps Institution of Oceanography Archives, Scripps Institution of Oceanography. Retrieved December 24, 2009.
  15. "Steamer Lane and Some Surf History". Santa Cruz Waves. Retrieved June 27, 2014.
  16. Kampion, Drew; Marcus, Ben (December 2000). "Jack O'Neill – Surfing A to Z". Surfline/Wavetrak, Inc. Retrieved December 7, 2008.
  17. "Oneill – Know Jack". O'Neill Inc. Archived from the original on February 19, 2008. Retrieved December 7, 2008.
  18. "Gul History". History. 17 May 2014. Retrieved 17 May 2014.
  19. "Steamer Wetsuit". History. 17 May 2014. Retrieved 17 May 2014.


This article is issued from Wikipedia - version of the Thursday, March 03, 2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.