Nickel titanium

Nickel titanium, also known as nitinol (part of shape memory alloy), is a metal alloy of nickel and titanium, where the two elements are present in roughly equal atomic percentages e.g. Nitinol 55, Nitinol 60.

Nickel Titanium
Material properties
Density 6.45 g/cm3 (0.233 lb/cu in)
Electrical Resistivity (Austenite) 82\times 10^{-6}\Omega \cdot \text{cm}
(Martensite) 76\times 10^{-6}\Omega \cdot \text{cm}
Thermal Conductivity (Austenite) 0.18 W/cm·K
(Martensite) 0.086 W/cm·K
Coefficient of Thermal Expansion (Austenite) 11\times 10^{-6}/\,^\circ\text{C}
(Martensite) 6.6\times 10^{-6}/\,^\circ\text{C}
Magnetic Permeability < 1.002
Magnetic Susceptibility (Austenite) 3.7\times 10^{-6} emu/g
(Martensite) 2.4\times 10^{-6} emu/g
Elastic Modulus (Austenite) 75-83 GPa
(Martensite) 28-40 GPa
Yield Strength (Austenite) 195-690 MPa
(Martensite) 70-140 MPa
Poisson's Ratio 0.33
Hardness value ?
Nitinol properties are particular to the precise composition of the alloy and its processing. These specifications are typical for commercially available shape memory nitinol alloys.

Nitinol alloys exhibit two closely related and unique properties: shape memory effect (SME) and superelasticity (SE) (also called pseudoelasticity (PE)). Shape memory is the ability of nitinol to undergo deformation at one temperature, then recover its original, undeformed shape upon heating above its "transformation temperature". Superelasticity occurs at a narrow temperature range just above its transformation temperature; in this case, no heating is necessary to cause the undeformed shape to recover, and the material exhibits enormous elasticity, some 10-30 times that of ordinary metal.

History

The term nitinol is derived from its composition and its place of discovery: (Nickel Titanium-Naval Ordnance Laboratory). William J. Buehler[1] along with Frederick Wang,[2] discovered its properties during research at the Naval Ordnance Laboratory in 1959.[3][4] William Buehler was attempting to make a better missile nose cone, which could resist fatigue, heat and the force of impact. Having found that a 1:1 alloy of nickel and titanium could do the job, in 1961 he presented a sample at a laboratory management meeting. The sample, folded up like an accordion, was passed around and flexed by the participants. One of them applied heat from his pipe lighter to the sample and, to everyone's surprise, the accordion-shaped strip stretched and took its previous shape.[5]

While the potential applications for nitinol were realized immediately, practical efforts to commercialize the alloy did not take place until a decade later. This delay was largely because of the extraordinary difficulty of melting, processing and machining the alloy. Even these efforts encountered financial challenges that were not readily overcome until the 1990s, when these practical difficulties finally began to be resolved.

The discovery of the shape-memory effect in general dates back to 1932, when Swedish chemist Arne Ölander[6] first observed the property in gold-cadmium alloys. The same effect was observed in Cu-Zn (brass) in the early 1950s.[7]

Mechanism

3D view of Austenite and Martensite structures of the NiTi compound.

Nitinol's unusual properties are derived from a reversible solid-state phase transformation known as a martensitic transformation, between two different martensite crystal phases, requiring 10,000–20,000 psi (69–138 MPa) of mechanical stress.

At high temperatures, nitinol assumes an interpenetrating simple cubic structure referred to as austenite (also known as the parent phase). At low temperatures, nitinol spontaneously transforms to a more complicated body-centered tetragonal crystal structure known as martensite (daughter phase). The temperature at which austenite transforms to martensite is generally referred to as the transformation temperature. More specifically, there are four transition temperatures. When the alloy is fully austenite, martensite begins to form as the alloy cools at the so-called martensite start, or Ms temperature, and the temperature at which the transformation is complete is called the martensite finish, or Mf temperature. When the alloy is fully martensite and is subjected to heating, austenite starts to form at the As temperature, and finishes at the Af temperature.[8]

Thermal hysteresis of nitinol's phase transformation

The cooling/heating cycle shows thermal hysteresis. The hysteresis width depends on the precise nitinol composition and processing. Its typical value is a temperature range spanning about 20-50 K (20-50 °C; 36-90 °F).

Crucial to nitinol properties are two key aspects of this phase transformation. First is that the transformation is "reversible", meaning that heating above the transformation temperature will revert the crystal structure to the simpler austenite phase. The second key point is that the transformation in both directions is instantaneous.

Martensite's crystal structure (known as a monoclinic, or B19' structure) has the unique ability to undergo limited deformation in some ways without breaking atomic bonds. This type of deformation is known as twinning, which consists of the rearrangement of atomic planes without causing slip, or permanent deformation. It is able to undergo about 6–8% strain in this manner. When martensite is reverted to austenite by heating, the original austenitic structure is restored, regardless of whether the martensite phase was deformed. Thus the name "shape memory" refers to the fact that the shape of the high temperature austenite phase is "remembered," even though the alloy is severely deformed at a lower temperature.[9]

2D view of nitinol's crystalline structure during cooling/heating cycle

A great deal of pressure can be produced by preventing the reversion of deformed martensite to austenite — from 35,000 psi to, in many cases, more than 100,000 psi (689 MPa). One of the reasons that nitinol works so hard to return its original shape is that it is not just an ordinary metal alloy, but what is known as an intermetallic compound. In an ordinary alloy, the constituents are randomly positioned on the crystal lattice; in an ordered intermetallic compound, the atoms (in this case, nickel and titanium) have very specific locations in the lattice.[10] The fact that nitinol is an intermetallic is largely responsible for the difficulty in fabricating devices made from the alloy.

The effect of nitinol composition on the Ms temperature.

The scenario described above (cooling austenite to form martensite, deforming the martensite, then heating to revert to austenite, thus returning the original, undeformed shape) is known as the thermal shape memory effect. To fix the original "parent shape," the alloy must be held in position and heated to about 500 °C (932 °F). A second effect, called superelasticity or pseudoelasticity, is also observed in nitinol. This effect is the direct result of the fact that martensite can be formed by applying a stress as well as by cooling. Thus in a certain temperature range, one can apply a stress to austenite, causing martensite to form while at the same time changing shape. In this case, as soon as the stress is removed, the nitinol will spontaneously return to its original shape. In this mode of use, nitinol behaves like a super spring, possessing an elastic range 10–30 times greater than that of a normal spring material. There are, however, constraints: the effect is only observed about 0-40 K (0-40 °C; 0-72 °F) above the Af temperature.

Nitinol is typically composed of approximately 50 to 51% nickel by atomic percent (55 to 56% weight percent).[10][11] Making small changes in the composition can change the transition temperature of the alloy significantly. One can control the Af temperature in nitinol to some extent, but convenient superelastic temperature ranges are from about −20 °C to +60 °C.

One often-encountered complication regarding nitinol is the so-called R-phase. The R-phase is another martensitic phase that competes with the martensite phase mentioned above. Because it does not offer the large memory effects of the martensite phase, it is, more often than not, an annoyance.

Manufacturing process

Nitinol is exceedingly difficult to make, due to the exceptionally tight compositional control required, and the tremendous reactivity of titanium. Every atom of titanium that combines with oxygen or carbon is an atom that is robbed from the NiTi lattice, thus shifting the composition and making the transformation temperature that much lower. There are two primary melting methods used today:

While both methods have advantages, there are no substantive data showing that material from one process is better than the other. Other methods are also used on a boutique scale, including plasma arc melting, induction skull melting, and e-beam melting. Physical vapour deposition is also used on a laboratory scale.

Hot working of nitinol is relatively easy, but cold working is difficult because the enormous elasticity of the alloy increases die or roll contact, leading to tremendous frictional resistance and tool wear. For similar reasons, machining is extremely difficult—to make things worse, the thermal conductivity of nitinol is poor, so heat is difficult to remove. Grinding (abrasive cutting), Electrical discharge machining (EDM) and laser cutting are all relatively easy.

Heat treating nitinol is delicate and critical. It is the essential tool in fine-tuning the transformation temperature. Aging time and temperature controls the precipitation of various Ni-rich phases, and thus controls how much nickel resides on the NiTi lattice; by depleting the matrix of nickel, aging increases the transformation temperature. The combination of heat treatment and cold working is essential in controlling the properties of nitinol.[12]

Limitations

Fatigue failures of nitinol devices are a constant subject of discussion. Because it is the material of choice for applications requiring enormous flexibility and motion (e.g., peripheral stents and heart valves), it is necessarily exposed to much greater fatigue strains than are other metals. While the strain-controlled fatigue performance of nitinol is superior to all other known metals, fatigue failures have been observed in the most demanding applications. There is a great deal of effort underway trying to better understand and define the durability limits of nitinol.

Nitinol is half nickel, and thus there has been a great deal of concern in the medical industry regarding the release of nickel, a known allergen and possible carcinogen.[12] (Nickel is also present in substantial amounts in stainless steel and cobalt-chrome alloys.) When properly treated (via electropolishing and/or passivation), nitinol forms a very stable protective TiO2 layer that acts as a very effective and self-healing barrier against ion exchange. It has been repeatedly shown that nitinol releases nickel at a slower pace than stainless steel, for example. With that said, very early medical devices were made without electropolishing, and corrosion was observed. Today's nitinol vascular self-expandable metallic stents, for example, show no evidence of corrosion or nickel release, and the outcomes in patients with and without nickel allergies are indistinguishable.

There are constant and long-running discussions regarding inclusions in nitinol, both TiC and Ti2NiOx. All metals contain inclusions, and nitinol cannot be melted without inclusions—they are omnipresent. The size, distribution and type of inclusions can be controlled to some extent. Theoretically, smaller, rounder and few inclusions should lead to increased fatigue durability. All studies done to date, however, have failed to show measurable differences.[13][14]

A major limitation to further use of nitinol has been its difficulty to weld, both to itself and other materials. Laser welding nitinol to itself is a relatively routine process. More recently, strong joints between NiTi wires and stainless steel wires have been made using nickel filler.[15] Laser[16] and Tungsten Inert Gas (TIG)[17] welds have been made between NiTi tubes and stainless steel tubes . More research is ongoing into other processes and other metals to which nitinol can be welded.

Another crucial limitation is the low frequency (typically 3 Hz) or actuation speed of nitinol due to poor heat rejection performance. Numerous methods are used to increase the cooling performance, such as forced air,[18] flowing liquids,[19] thermoelectric modules (i.e. Peltier or semiconductor heat pumps),[20] heat sinks,[21] conductive materials[22] and higher surface-to-volume ratio[23](improvement up to 100 Hz with thinfilm nitinol[24]). The fastest Nitinol actuation recorded was carried by a high voltage capacitor discharge which heated an SMA wire in a manner of microseconds, and resulted in a complete phase transformation (and high velocities) in a few milliseconds.[25]

Recent advances have shown that processing of Nitinol can expand thermomechanical capabilities, allowing for multiple shape memories to be embedded within a monolithic structure[26] .[27] Research on multi-memory technology is on-going and promises to deliver enhanced shape memory devices in the near future[28] ,[29] and the application of new materials and material structures, such hybrid shape memory materials (SMMs) and shape memory composites (SMCs).[30]

Applications

There are four commonly used types of applications for nitinol.

In 1989 a survey was conducted in the United States and Canada that involved seven organizations. The survey focused on predicting the future technology, market, and applications of SMAs. The companies predicted the following uses of nitinol in a decreasing order of importance: (1) Couplings, (2) Biomedical and medical, (3) Toys, demonstration, novelty items, (4) Actuators, (5) Heat Engines, (6) Sensors, (7) Cryogenically activated die and bubble memory sockets, and finally (8) lifting devices.[31]

Heat engines

Biocompatible applications

References

  1. Buehler, W. J.; Gilfrich, J. W.; Wiley, R. C. (1963). "Effects of Low-Temperature Phase Changes on the Mechanical Properties of Alloys Near Composition TiNi". Journal of Applied Physics 34 (5): 1475–1477. doi:10.1063/1.1729603.
  2. Wang, F. E.; Buehler, W. J.; Pickart, S. J. (1965). "Crystal Structure and a Unique Martensitic Transition of TiNi". Journal of Applied Physics 36 (10): 3232–3239. doi:10.1063/1.1702955.
  3. "The Alloy That Remembers", Time, 1968-09-13
  4. Kauffman, G. B.; Mayo, I. (1997). "The Story of Nitinol: The Serendipitous Discovery of the Memory Metal and Its Applications". The Chemical Educator 2 (2): 1–21. doi:10.1007/s00897970111a.
  5. Withers, N. (2014). "Magnificent Molecules - Nitinol" (PDF). The Mole (RSC) 2014 (2): 4.
  6. Ölander, A. (1932). "An Electrochemical Investigation of Solid Cadmium-Gold Alloys". Journal of the American Chemical Society 54 (10): 3819–3833. doi:10.1021/ja01349a004.
  7. Hornbogen, E.; Wassermann, G. (1956). "Über den Einfluβ von Spannungen und das Auftreten von Umwandlungsplastizität bei β1-β-Umwandlung des Messings". Zeitschrift für Metallkunde 47: 427–433.
  8. "Nitinol facts". Nitinol.com. 2013.
  9. Funakubo, Hiroyasu (1984), Shape memory alloys, University of Tokyo, pp. 7, 176.
  10. 1 2 "Nitinol SM495 Wire" (properties, PDF). 2013.
  11. "Nitinol SE508 Wire" (properties, PDF). 2013.
  12. 1 2 Pelton, A.; Russell, S.; DiCello, J. (2003). "The Physical Metallurgy of Nitinol for Medical Applications". JOM 55 (5): 33–37. doi:10.1007/s11837-003-0243-3.
  13. Morgan, N.; Wick, A.; DiCello, J.; Graham, R. (2006). "Carbon and Oxygen Levels in Nitinol Alloys and the Implications for Medical Device Manufacture and Durability". SMST-2006 Proceedings of the International Conference on Shape Memory and Superelastic Technologies (PDF). ASM International. pp. 821–828. doi:10.1361/cp2006smst821. ISBN 978-0-87170-862-5. LCCN 2009499204.
  14. Miyazaki, S.; Sugaya, Y.; Otsuka, K. (1989). "Mechanism of Fatigue Crack Nucleation in Ti-Ni Alloys". Shape memory materials : May 31-June 3, 1988, Sunshine City, Ikebukuro, Tokyo, Japan. Proceedings of the MRS International Meeting on Advanced Materials 9. Materials Research Society. pp. 257–262. ISBN 1-55899-038-0. LCCN 90174266.
  15. US patent 6875949, Hall, P. C., "Method of Welding Titanium and Titanium Based Alloys to Ferrous Metals"
  16. Hahnlen, Ryan; Fox, Gordon (October 29, 2012). "Fusion welding of nickel–titanium and 304 stainless steel tubes: Part I: laser welding". Journal of Intelligent Material Systems and Structures 24 (8).
  17. Fox, Gordon; Hahnlen, Ryan (October 29, 2012). "Fusion welding of nickel–titanium and 304 stainless steel tubes: Part II: tungsten inert gas welding". Journal of Intelligent Material Systems and Structures 24 (8).
  18. Tadesse Y; Thayer N; Priya S (2010). "Tailoring the response time of shape memory alloy wires through active cooling and pre-stress". Journal of Intelligent Material Systems and Structures 21: 19–40.
  19. Wellman PS; Peine WJ; Favalora G; Howe RD (1997). "Mechanical Design and Control of a High-Bandwidth Shape Memory Alloy Tactile Display". International Symposium on Experimental Robotics.
  20. Romano R; Tannuri EA (2009). "Modeling, control and experimental validation of a novel actuator based on shape memory alloys". Mechatronics 19: 1169–1177.
  21. Russell RA;Gorbet RB (1995). "Improving the response of SMA actuators". Robotics and Automation 3: 2299–304.
  22. Chee Siong L;Yokoi H;Arai T (2005). "Improving heat sinking in ambient environment for the shape memory alloy (SMA)". Intelligent Robots and Systems: 3560–3565.
  23. An L;Huang WM;Fu YQ;Guo NQ (2008). "A note on size effect in actuating NiTi shape memory alloys by electrical current". Materials & Design 29: 1432–1437.
  24. Winzek B;Schmitz S;Rumpf H;Sterzl T;Ralf Hassdorf;Thienhaus S (2004). "Recent developments in shape memory thin film technology". Materials Science and Engineering: A 378: 40–46.
  25. Vollach, Shahaf, and D. Shilo. "The mechanical response of shape memory alloys under a rapid heating pulse." Experimental Mechanics 50.6 (2010): 803-811.
  26. Khan, M. I.; Zhou Y. N. (2011), Methods and Systems for Processing Materials, Including Shape Memory Materials, WO Patent WO/2011/014,962 Cite uses deprecated parameter |coauthors= (help)
  27. Daly, M.; Pequegnat, A.; Zhou, Y.; Khan, M. I. (2012), "Enhanced thermomechanical functionality of a laser processed hybrid NiTi–NiTiCu shape memory alloy", Smart Materials and Structures 21 (4): 045018, doi:10.1088/0964-1726/21/4/045018
  28. Daly, M.; Pequegnat, A.; Zhou, Y. N.; Khan, M. I. (2012), "Fabrication of a novel laser-processed NiTi shape memory microgripper with enhanced thermomechanical functionality", Journal of Intelligent Material Systems and Structures 24 (8): 984–990, doi:10.1177/1045389X12444492
  29. Pequegnat, A.; Daly, M.; Wang, J.; Zhou, Y.; Khan, M. I. (2012), "Dynamic actuation of a novel laser-processed NiTi linear actuator", Smart Materials and Structures 21 (9): 094004, doi:10.1088/0964-1726/21/9/094004
  30. Tao T;Liang Y-C;Taya M (2006). "Bio-inspired actuating system for swimming using shape memory alloy composites". Int J Automat Comput. 3page=366-373.
  31. Miller, R. K.; Walker, T. (1989). Survey on Shape Memory Alloys. Survey Reports 89. Future Technology Surveys. p. 17. ISBN 9781558651005. OCLC 38076438.
  32. Brady, G. S.; Clauser, H. R.; Vaccari, J. A. (2002). Materials Handbook (15th ed.). McGraw-Hill Professional. p. 633. ISBN 978-0-07-136076-0. Retrieved 2009-05-09.
  33. Sang, D.; Ellis, P.; Ryan, L.; Taylor, J.; McMonagle, D.; Petheram, L.; Godding, P. (2005). Scientifica. Nelson Thornes. p. 80. ISBN 0-7487-7996-5. Retrieved 2009-05-09.
  34. Jones, G.; Falvo, M. R.; Taylor, A. R.; Broadwell, B. P. (2007). "Nanomaterials: Memory Wire". Nanoscale Science. NSTA Press. p. 109. ISBN 1-933531-05-3. Retrieved 2009-05-09.
  35. "Nitinol Heat Engine Kit". Images Scientific Instruments. 2007. Retrieved 2011.
  36. Banks, R. (1975). "The Banks Engine". Die Naturwissenschaften 62 (7): 305–308. doi:10.1007/BF00608890.
  37. Vimeo posting of "The Individualist", documentary on Ridgway Banks
  38. "Single wire nitinol engine", Ridgway M. Banks, US Patent
  39. "Metals that Remember", Popular Science, January 1988
  40. "Engine Uses No Fuel", Milwaukee Journal, December 5, 1973
  41. Alejandra Martins (2014-10-02). "The inventions of the Bolivian doctor who saved thousands of children". BBC Mundo. Retrieved 2015-03-30.

Further reading

A process of making parts and forms of Type 60 Nitinol having a shape memory effect, comprising: selecting a Type 60 Nitinol. Inventor G,Julien CEO of Nitinol Technologies, Inc. (Washington State)

External links

Wikimedia Commons has media related to Nickel titanium.

Science Digest articles - Miracle Metal 1982 - PDF