Yttrium

Yttrium,  ₃₉Y

General properties
Name, symbol	yttrium, Y
Appearance	silvery white
Pronunciation	/ˈɪtriəm/ IT-ree-əm
Yttrium in the periodic table
Sc ↑ Y ↓ Lu strontium ← yttrium → zirconium
Atomic number (Z)	39
Group, block	group 3, d-block
Period	period 5
Element category	transition metal
Standard atomic weight (±) (Ar)	88.90584(2)[1]
Electron configuration	[Kr] 4d^1 5s^2
per shell	2, 8, 18, 9, 2
Physical properties
Phase	solid
Melting point	1799 K ​(1526 °C, ​2779 °F)
Boiling point	3203 K ​(2930 °C, ​5306 °F)
Density near r.t.	4.472 g/cm^3
when liquid, at m.p.	4.24 g/cm^3
Heat of fusion	11.42 kJ/mol
Heat of vaporization	363 kJ/mol
Molar heat capacity	26.53 J/(mol·K)
vapor pressure P (Pa) 1 10 100 1 k 10 k 100 k at T (K) 1883 2075 (2320) (2627) (3036) (3607)
Atomic properties
Oxidation states	3, 2, 1 ​(a weakly basic oxide)
Electronegativity	Pauling scale: 1.22
Ionization energies	1st: 600 kJ/mol 2nd: 1180 kJ/mol 3rd: 1980 kJ/mol
Atomic radius	empirical: 180 pm
Covalent radius	190±7 pm
Miscellanea
Crystal structure	​hexagonal close-packed (hcp)
Speed of sound thin rod	3300 m/s (at 20 °C)
Thermal expansion	α, poly: 10.6 µm/(m·K) (at r.t.)
Thermal conductivity	17.2 W/(m·K)
Electrical resistivity	α, poly: 596 nΩ·m (at r.t.)
Magnetic ordering	paramagnetic[2]
Young's modulus	63.5 GPa
Shear modulus	25.6 GPa
Bulk modulus	41.2 GPa
Poisson ratio	0.243
Brinell hardness	200–589 MPa
CAS Number	7440-65-5
History
Naming	after Ytterby, Sweden and its mineral ytterbite (gadolinite)
Discovery	Johan Gadolin (1794)
First isolation	Carl Gustav Mosander (1840)
Most stable isotopes of yttrium
iso NA half-life DM DE (MeV) DP ^87Y syn 3.35 d ε – ^87Sr γ 0.48, 0.38D – ^88Y syn 106.6 d ε – ^88Sr γ 1.83, 0.89 – ^89Y 100% ^89Y is stable with 50 neutrons ^90Y syn 2.67 d β^− 2.28 ^90Zr γ 2.18 – ^91Y syn 58.5 d β^− 1.54 ^91Zr γ 1.20 –

Yttrium is a chemical element with symbol Y and atomic number 39. It is a silvery-metallic transition metal chemically similar to the lanthanides and it has often been classified as a "rare earth element".^[3] Yttrium is almost always found combined with the lanthanides in rare earth minerals and is never found in nature as a free element. Its only stable isotope, ⁸⁹Y, is also its only naturally occurring isotope.

In 1787, Carl Axel Arrhenius found a new mineral near Ytterby in Sweden and named it ytterbite, after the village. Johan Gadolin discovered yttrium's oxide in Arrhenius' sample in 1789,^[4] and Anders Gustaf Ekeberg named the new oxide yttria. Elemental yttrium was first isolated in 1828 by Friedrich Wöhler.^[5]

The most important use of yttrium is in making phosphors, particularly the red phosphors used in television set cathode ray tube (CRT) displays and in LEDs.^[6] It is also used in the production of electrodes, electrolytes, electronic filters, lasers and superconductors; various medical applications; and the tracing of various materials to enhance their properties. Yttrium has no known biological role, and exposure to yttrium compounds can cause lung disease in humans.^[7]

Characteristics

Properties

Yttrium is a soft, silver-metallic, lustrous and highly crystalline transition metal in group 3. As expected by periodic trends, it is less electronegative than its predecessor in the group, scandium, and less electronegative than the next member of period 5, zirconium; additionally, it is of comparable electronegativity to its successor in its group, lutetium, due to the lanthanide contraction.^[8][9] Yttrium is the first d-block element in the fifth period.

The pure element is relatively stable in air in bulk form, due to passivation resulting from the formation of a protective oxide (Y
2O
3) film on its surface. This film can reach a thickness of 10 µm when yttrium is heated to 750 °C in water vapor.^[10] When finely divided, however, yttrium is very unstable in air; shavings or turnings of the metal can ignite in air at temperatures exceeding 400 °C.^[5] Yttrium nitride (YN) is formed when the metal is heated to 1000 °C in nitrogen.^[10]

Similarity to the lanthanides

The similarities of yttrium to the lanthanides are so strong that the element has historically been grouped with them as a rare earth element,^[3] and is always found in nature together with them in rare earth minerals.^[11]

Chemically, yttrium resembles these elements more closely than its neighbor in the periodic table, scandium,^[12] and if its physical properties were plotted against atomic number then it would have an apparent number of 64.5 to 67.5, placing it between the lanthanides gadolinium and erbium.^[13]

It often also falls in the same range for reaction order,^[10] resembling terbium and dysprosium in its chemical reactivity.^[6] Yttrium is so close in size to the so-called 'yttrium group' of heavy lanthanide ions that in solution, it behaves as if it were one of them.^[10][14] Even though the lanthanides are one row farther down the periodic table than yttrium, the similarity in atomic radius may be attributed to the lanthanide contraction.^[15]

One of the few notable differences between the chemistry of yttrium and that of the lanthanides is that yttrium is almost exclusively trivalent, whereas about half of the lanthanides can have valences other than three.^[10]

Compounds and reactions

As a trivalent transition metal, yttrium forms various inorganic compounds, generally in the oxidation state of +3, by giving up all three of its valence electrons.^[16] A good example is yttrium(III) oxide (Y
2O
3), also known as yttria, a six-coordinate white solid.^[17]

Yttrium forms a water-insoluble fluoride, hydroxide, and oxalate, but its bromide, chloride, iodide, nitrate and sulfate are all soluble in water.^[10] The Y³⁺ ion is colorless in solution because of the absence of electrons in the d and f electron shells.^[10]

Water readily reacts with yttrium and its compounds to form Y
2O
3.^[11] Concentrated nitric and hydrofluoric acids do not rapidly attack yttrium, but other strong acids do.^[10]

With halogens, yttrium forms trihalides such as yttrium(III) fluoride (YF
3), yttrium(III) chloride (YCl
3), and yttrium(III) bromide (YBr
3) at temperatures above roughly 200 °C.^[7] Similarly, carbon, phosphorus, selenium, silicon and sulfur all form binary compounds with yttrium at elevated temperatures.^[10]

Organoyttrium chemistry is the study of compounds containing carbon–yttrium bonds. A few of these are known to have yttrium in the oxidation state 0.^[18][19] (The +2 state has been observed in chloride melts,^[20] and +1 in oxide clusters in the gas phase.^[21]) Some trimerization reactions were observed by using organoyttrium compounds as catalysts.^[19] These compounds use YCl
3 as a starting material, which in turn is obtained from Y
2O
3 and concentrated hydrochloric acid and ammonium chloride.^[22][23]

Hapticity is how a group of contiguous atoms of a ligand are coordinated to a central atom; it is indicated by the Greek character eta, η. Yttrium complexes were the first examples of complexes where carboranyl ligands were bound to a d⁰-metal center through a η⁷-hapticity.^[19] Vaporization of the graphite intercalation compounds graphite–Y or graphite–Y
2O
3 leads to the formation of endohedral fullerenes such as Y@C₈₂.^[6] Electron spin resonance studies indicated the formation of Y³⁺ and (C₈₂)³⁻ ion pairs.^[6] The carbides Y₃C, Y₂C, and YC₂ can each hydrolyze to form hydrocarbons.^[10]

Nucleosynthesis and isotopes

Yttrium in the Solar System was created through stellar nucleosynthesis, mostly by the s-process (≈72%), but also by the r-process (≈28%).^[24] The r-process consists of rapid neutron capture of lighter elements during supernova explosions. The s-process is a slow neutron capture of lighter elements inside pulsating red giant stars.^[25]

Mira is an example of the type of red giant star where most of the yttrium in the solar system was created

Yttrium isotopes are among the most common products of the nuclear fission of uranium occurring in nuclear explosions and nuclear reactors. In terms of nuclear waste management, the most important isotopes of yttrium are ⁹¹Y and ⁹⁰Y, with half-lives of 58.51 days and 64 hours, respectively.^[26] Though ⁹⁰Y has the short half-life, it exists in secular equilibrium with its long-lived parent isotope, strontium-90 (⁹⁰Sr) with a half-life of 29 years.^[5]

All group 3 elements have an odd atomic number, and therefore they have few stable isotopes.^[8] Scandium has one stable isotope, and yttrium itself has only one stable isotope, ⁸⁹Y, which is also its only naturally occurring one. However, the lanthanide rare earths contain elements of even atomic number and many stable isotopes. Yttrium-89 is thought to be more abundant than it otherwise would be, due in part to the s-process, which allows enough time for isotopes created by other processes to decay by electron emission (neutron → proton).^{[25][note 1]} Such a slow process tends to favor isotopes with atomic mass numbers (A = protons + neutrons) around 90, 138 and 208, which have unusually stable atomic nuclei with 50, 82, and 126 neutrons, respectively.^{[25][note 2][5] 89}Y has a mass number close to 90 and has 50 neutrons in its nucleus.

At least 32 synthetic isotopes of yttrium have been observed, and these range in atomic mass number from 76 to 108.^[26] The least stable of these is ¹⁰⁶Y with a half-life of >150 ns (⁷⁶Y has a half-life of >200 ns) and the most stable is ⁸⁸Y with a half-life of 106.626 days.^[26] Besides the isotopes ⁹¹Y, ⁸⁷Y, and ⁹⁰Y, with half-lives of 58.51 days, 79.8 hours, and 64 hours, respectively, all the other isotopes have half-lives of less than a day and most of those have half-lives of less than an hour.^[26]

Yttrium isotopes with mass numbers at or below 88 decay primarily by positron emission (proton → neutron) to form strontium (Z = 38) isotopes.^[26] Yttrium isotopes with mass numbers at or above 90 decay primarily by electron emission (neutron → proton) to form zirconium (Z = 40) isotopes.^[26] Isotopes with mass numbers at or above 97 are also known to have minor decay paths of β⁻ delayed neutron emission.^[27]

Yttrium has at least 20 metastable or excited isomers ranging in mass number from 78 to 102.^{[26][note 3]} Multiple excitation states have been observed for ⁸⁰Y and ⁹⁷Y.^[26] While most of yttrium's isomers are expected to be less stable than their ground state, ^78mY, ^84mY, ^85mY, ^96mY, ^98m1Y, ^100mY, and ^102mY have longer half-lives than their ground states, as these isomers decay by beta decay rather than isomeric transition.^[27]

History

In 1787, army lieutenant and part-time chemist Carl Axel Arrhenius found a heavy black rock in an old quarry near the Swedish village of Ytterby (now part of the Stockholm Archipelago).^[4] Thinking that it was an unknown mineral containing the newly discovered element tungsten,^[28] he named it ytterbite^{[note 4]} and sent samples to various chemists for further analysis.^[4]

Johan Gadolin discovered yttrium oxide

Johan Gadolin at the University of Åbo identified a new oxide or "earth" in Arrhenius' sample in 1789, and published his completed analysis in 1794.^{[29][note 5]} Anders Gustaf Ekeberg confirmed this in 1797 and named the new oxide yttria.^[30] In the decades after Antoine Lavoisier developed the first modern definition of chemical elements, it was believed that earths could be reduced to their elements, meaning that the discovery of a new earth was equivalent to the discovery of the element within, which in this case would have been yttrium.^{[note 6]}

In 1843, Carl Gustaf Mosander found that samples of yttria contained three oxides: white yttrium oxide (yttria), yellow terbium oxide (confusingly, this was called 'erbia' at the time) and rose-colored erbium oxide (called 'terbia' at the time).^[31] A fourth oxide, ytterbium oxide, was isolated in 1878 by Jean Charles Galissard de Marignac.^[32] New elements would later be isolated from each of those oxides, and each element was named, in some fashion, after Ytterby, the village near the quarry where they were found (see ytterbium, terbium, and erbium).^[33] In the following decades, seven other new metals were discovered in "Gadolin's yttria".^[4] Since yttria was a mineral after all and not an oxide, Martin Heinrich Klaproth renamed it gadolinite in honor of Gadolin.^[4]

Yttrium metal was first isolated in 1828 when Friedrich Wöhler heated anhydrous yttrium(III) chloride with potassium:^[34][35]

YCl₃ + 3 K → 3 KCl + Y

Until the early 1920s, the chemical symbol Yt was used for the element, after which Y came into common use.^[36]

In 1987, yttrium barium copper oxide was found to achieve high-temperature superconductivity.^[37] It was only the second material known to exhibit this property,^[37] and it was the first known material to achieve superconductivity above the (economically important) boiling point of nitrogen.^{[note 7]}

Occurrence

Xenotime crystals contain yttrium

Abundance

Yttrium is found in most rare earth minerals,^[9] as well as some uranium ores, but is never found in nature as a free element.^[38] About 31 ppm of the Earth's crust is yttrium,^[6] making it the 28th most abundant element there, and 400 times more common than silver.^[39] Yttrium is found in soil in concentrations between 10 and 150 ppm (dry weight average of 23 ppm) and in sea water at 9 ppt.^[39] Lunar rock samples collected during the American Apollo Project have a relatively high content of yttrium.^[33]

Yttrium has no known biological role, though it is found in most, if not all, organisms and tends to concentrate in the liver, kidney, spleen, lungs, and bones of humans.^[40] There is normally as little as 0.5 milligrams found within the entire human body; human breast milk contains 4 ppm.^[41] Yttrium can be found in edible plants in concentrations between 20 ppm and 100 ppm (fresh weight), with cabbage having the largest amount.^[41] With up to 700 ppm, the seeds of woody plants have the highest known concentrations.^[41]

Production

The chemical similarity of yttrium with the lanthanides leads it to being enriched by the same processes and ends up in ores containing lanthanides, forming rare earth minerals. A slight separation is recognized between the light (LREE) and the heavy rare earth elements (HREE) but this separation is never complete. Yttrium is concentrated in the HREE group by virtue of its ionic size even though it has a lower atomic mass.^[42][43]

A piece of yttrium. Yttrium is difficult to separate from other rare earth elements.

There are four main sources for REEs:^[44]

• Carbonate and fluoride containing ores such as the LREE bastnäsite ([(Ce, La, etc.)(CO₃)F]) contain an average of 0.1%^[5][42] of yttrium compared to the 99.9% for the 16 other REEs.^[42] The main source for bastnäsite from the 1960s to the 1990s was the Mountain Pass rare earth mine in California, making the United States the largest producer of REEs during that period.^[42][44]
• Monazite ([(Ce, La, etc.)PO₄]), which is mostly phosphate, is a placer deposit of sand that is created by the transportation and gravitational separation of eroded granite. Monazite as a LREE ore contains 2%^[42] (or 3%)^[45] of yttrium. The largest deposits were found in India and Brazil in the early 20th century, making these two countries the largest producers of yttrium in the first half of that century.^[42][44]
• Xenotime, a REE phosphate, is the main HREE ore containing up to 60% of yttrium as yttrium phosphate (YPO₄).^[42] The largest mine for this mineral is the Bayan Obo deposit in China, making China the largest exporter for HREE since the closure of the Mountain Pass mine in the 1990s.^[42][44]
• Ion absorption clays or Lognan clays are the weathering products of granite and contain only 1% of REEs.^[42] The final ore concentrate can contain up to 8% of yttrium. Ion absorption clays are mostly mined in southern China.^[42][44][46] Yttrium is also found in samarskite and fergusonite.^[39]

One method to obtain pure yttrium from the mixed oxide ores is to dissolve the oxide in sulfuric acid and fractionate it by ion exchange chromatography. With the addition of oxalic acid, the yttrium oxalate precipitates. The oxalate is converted into the oxide by heating under oxygen. By reacting the resulting yttrium oxide with hydrogen fluoride, yttrium fluoride is obtained.^[47] Using quaternary ammonium salts as extractants, yttrium prefers to remain in the aqueous phase: when the counter-ion is nitrate, the light lanthanides are removed, but when the counter-ion is thiocyanate, the heavy lanthanides are removed. Yttrium salts of 99.999% purity are obtained. In the usual situation, where yttrium is two-thirds of a heavy-lanthanide mixture, there is an advantage to getting it out of the system as quickly as possible, to ease the separation of the remaining elements.

Annual world production of yttrium oxide had reached 600 tonnes by 2001, with reserves estimated at 9 million tonnes.^[39] In 2013 it was 7100 tonnes of Y
2O
3.^[48] Only a few tonnes of yttrium metal are produced each year by reducing yttrium fluoride to a metal sponge with calcium magnesium alloy. The temperature of an arc furnace of above 1,600 °C is sufficient to melt the yttrium.^[39][47]

Applications

Consumer

Yttrium is one of the elements used to make the red color in CRT televisions

Yttria (Y
2O
3) can serve as host lattice for doping with Eu³⁺ cations as well as reactant to gain doped yttrium orthovanadate YVO₄:Eu³⁺ or yttrium oxide sulfide Y
2O
2S:Eu³⁺ phosphors that give the red color in color television picture tubes,^{[5][6][note 8]} though the red color itself is actually emitted from the europium while the yttrium collects energy from the electron gun and passes it to the phosphor.^[49] Yttrium compounds can serve as host lattices for doping with different lanthanide cations. Besides Eu³⁺ also Tb³⁺ can be used as a doping agent leading to green luminescence. Yttria is also used as a sintering additive in the production of porous silicon nitride^[50] and as a common starting material for both material science and for producing other compounds of yttrium.

Yttrium compounds are used as a catalyst for ethylene polymerization.^[5] As a metal, it is used on the electrodes of some high-performance spark plugs.^[51] Yttrium is also used in the manufacturing of gas mantles for propane lanterns as a replacement for thorium, which is radioactive.^[52]

Developing uses include yttrium-stabilized zirconia in particular as a solid electrolyte and as an oxygen sensor in automobile exhaust systems.^[6]

Garnets

Nd:YAG laser rod 0.5 cm in diameter

Yttrium is used in the production of a large variety of synthetic garnets,^[53] and yttria is used to make yttrium iron garnets (Y
3Fe
5O
12 or YIG), which are very effective microwave filters.^[5] Yttrium, iron, aluminium, and gadolinium garnets (e.g. Y₃(Fe,Al)₅O₁₂ and Y₃(Fe,Ga)₅O₁₂) have important magnetic properties.^[5] YIG is also very efficient as an acoustic energy transmitter and transducer.^[54] Yttrium aluminium garnet (Y
3Al
5O
12 or YAG) has a hardness of 8.5 and is also used as a gemstone in jewelry (simulated diamond).^[5] Cerium-doped yttrium aluminium garnet (YAG:Ce) crystals are used as phosphors to make white LEDs.^[55][56][57]

YAG, yttria, yttrium lithium fluoride (LiYF
4), and yttrium orthovanadate (YVO
4) are used in combination with dopants such as neodymium, erbium, ytterbium in near-infrared lasers.^[58][59] YAG lasers have the ability to operate at high power and are used for drilling into and cutting metal.^[45] The single crystals of doped YAG are normally produced by the Czochralski process.^[60]

Material enhancer

Small amounts of yttrium (0.1 to 0.2%) have been used to reduce the grain sizes of chromium, molybdenum, titanium, and zirconium.^[61] It is also used to increase the strength of aluminium and magnesium alloys.^[5] The addition of yttrium to alloys generally improves workability, adds resistance to high-temperature recrystallization and significantly enhances resistance to high-temperature oxidation (see graphite nodule discussion below).^[49]

Yttrium can be used to deoxidize vanadium and other non-ferrous metals.^[5] Yttria is used to stabilize the cubic form of zirconia for use in jewelry.^[62]

Yttrium has been studied for possible use as a nodulizer in making nodular cast iron, which has increased ductility (the graphite forms compact nodules instead of flakes to form nodular cast iron).^[5] Yttrium oxide can also be used in ceramic and glass formulas, since it has a high melting point and imparts shock resistance and low thermal expansion characteristics.^[5] It is therefore used in camera lenses.^[39]

Medical

The radioactive isotope yttrium-90 is used in drugs such as Yttrium Y 90-DOTA-tyr3-octreotide and Yttrium Y 90 ibritumomab tiuxetan for the treatment of various cancers, including lymphoma, leukemia, liver, ovarian, colorectal, pancreatic and bone cancers.^[41] It works by adhering to monoclonal antibodies, which in turn bind to cancer cells and kill them via intense β-radiation from the yttrium-90 (see Monoclonal antibody therapy).^[63]

In [(Hepatocellular carcinoma)] a technique called radioembolization is used. Radioembolization is a low toxicity, targeted liver cancer therapy that consists of millions of tiny beads made of glass or resin that contain radioactive yttrium-90. The radioactive microspheres are delivered directly to the blood vessels feeding specific liver tumors/segments or lobes. It is minimally invasive and patients can usually be discharged after a few hours. This procedure may not eliminate all tumors throughout the entire liver, but works on one segment or one lobe at a time and may require multiple procedures. ^[64]

Also see Radioembolization in the case of combined cirrhosis and Hepatocellular carcinoma.

Needles made of yttrium-90, which can cut more precisely than scalpels, have been used to sever pain-transmitting nerves in the spinal cord,^[28] and yttrium-90 is also used to carry out radionuclide synovectomy in the treatment of inflamed joints, especially knees, in sufferers of conditions such as rheumatoid arthritis.^[65]

A neodymium-doped yttrium-aluminium-garnet laser has been used in an experimental, robot-assisted radical prostatectomy in canines in an attempt to reduce collateral nerve and tissue damage,^[66] whilst the erbium-doped ones are starting to be used in cosmetic skin resurfacing.^[6]

Superconductors

YBCO superconductor

Yttrium was used in the yttrium barium copper oxide (YBa₂Cu₃O₇, aka 'YBCO' or '1-2-3') superconductor developed at the University of Alabama and the University of Houston in 1987.^[37] This superconductor operated at 93 K, notable because this is above liquid nitrogen's boiling point (77.1 K).^[37] As the price of liquid nitrogen is lower than that of liquid helium, which must be used for the metallic superconductors, the operating costs would decrease.

The actual superconducting material is often written as YBa₂Cu₃O_7–d, where d must be less than 0.7 for the material to superconduct. The reason for this is still not clear, but it is known that the vacancies occur only in certain places in the crystal, the copper oxide planes and chains, giving rise to a peculiar oxidation state of the copper atoms, which somehow leads to the superconducting behavior.

The theory of low temperature superconductivity has been well understood since the BCS theory was put forward in 1957. It is based on a peculiarity of the interaction between two electrons in a crystal lattice. However, the BCS theory does not explain high temperature superconductivity, and its precise mechanism is still a mystery. What is known is that the composition of the copper-oxide materials must be precisely controlled if superconductivity is to occur.^[67]

The created material was a black and green, multi-crystal, multi-phase mineral. Researchers are studying a class of materials known as perovskites that are alternative mixtures of these elements, hoping to eventually develop a practical high-temperature superconductor.^[45]

Precautions

Yttrium currently has no biological role, and it can be highly toxic to humans and other animals.^[7]

Water-soluble compounds of yttrium are considered mildly toxic, while its insoluble compounds are non-toxic.^[41] In experiments on animals, yttrium and its compounds caused lung and liver damage, though toxicity varies with different yttrium compounds. In rats, inhalation of yttrium citrate caused pulmonary edema and dyspnea, while inhalation of yttrium chloride caused liver edema, pleural effusions, and pulmonary hyperemia.^[7]

Exposure to yttrium compounds in humans may cause lung disease.^[7] Workers exposed to airborne yttrium europium vanadate dust experienced mild eye, skin, and upper respiratory tract irritation—though this may have been caused by the vanadium content rather than the yttrium.^[7] Acute exposure to yttrium compounds can cause shortness of breath, coughing, chest pain, and cyanosis.^[7] The Occupational Safety and Health Administration (OSHA) has set the legal limit (permissible exposure limit) for yttrium exposure in the workplace as 1 mg/m³ over an 8-hour workday. The National Institute for Occupational Safety and Health (NIOSH) has set a recommended exposure limit (REL) of 1 mg/m³ over an 8-hour workday. At levels of 500 mg/m³, yttrium is immediately dangerous to life and health.^[68] Yttrium dust is flammable.^[7]

See also

Listen to this article (info/dl)

This audio file was created from a revision of the "Yttrium" article dated 2011-07-12, and does not reflect subsequent edits to the article. (Audio help)

More spoken articles

Notes

1. Essentially, a neutron becomes a proton while an electron and antineutrino are emitted.
2. See: magic number. This stability is thought to result from their very low neutron-capture cross-section. (Greenwood 1997, pp. 12–13). Electron emission of isotopes with those mass numbers is simply less prevalent due to this stability, resulting in them having a higher abundance.
3. Metastable isomers have higher-than-normal energy states than the corresponding non-excited nucleus and these states last until a gamma ray or conversion electron is emitted from the isomer. They are designated by an 'm' being placed next to the isotope's mass number.
4. Ytterbite was named after the village it was discovered near, plus the -ite ending to indicate it was a mineral.
5. Stwertka 1998, p. 115 says that the identification occurred in 1789 but is silent on when the announcement was made. Van der Krogt 2005 cites the original publication, with the year 1794, by Gadolin.
6. Earths were given an -a ending and new elements are normally given an -ium ending
7. T_c for YBCO is 93 K and the boiling point of nitrogen is 77 K.
8. Emsley 2001, p. 497 says that "Yttrium oxysulfide, doped with europium (III), is used as the standard red component in colour televisions", and Jackson and Christiansen (1993) state that 5–10 g yttrium oxide and 0.5–1 g europium oxide are required to produce a single TV screen, as quoted in Gupta and Krishnamurthy.

References

1. Standard Atomic Weights 2013. Commission on Isotopic Abundances and Atomic Weights
2. Lide, D. R., ed. (2005). "Magnetic susceptibility of the elements and inorganic compounds". CRC Handbook of Chemistry and Physics (PDF) (86th ed.). Boca Raton (FL): CRC Press. ISBN 0-8493-0486-5.
3. IUPAC contributors (2005). Connelly N G; Damhus T; Hartshorn R M; Hutton A T, eds. Nomenclature of Inorganic Chemistry: IUPAC Recommendations 2005 (PDF). RSC Publishing. p. 51. ISBN 0-85404-438-8. Retrieved 2007-12-17.
4. Van der Krogt 2005
5. CRC contributors (2007–2008). "Yttrium". In Lide, David R. CRC Handbook of Chemistry and Physics 4. New York: CRC Press. p. 41. ISBN 978-0-8493-0488-0.
6. Cotton, Simon A. (2006-03-15). "Scandium, Yttrium & the Lanthanides: Inorganic & Coordination Chemistry". Encyclopedia of Inorganic Chemistry. doi:10.1002/0470862106.ia211. ISBN 0-470-86078-2.
7. OSHA contributors (2007-01-11). "Occupational Safety and Health Guideline for Yttrium and Compounds". United States Occupational Safety and Health Administration. Archived from the original on March 2, 2013. Retrieved 2008-08-03. (public domain text)
8. Greenwood 1997, p. 946
9. Hammond, C. R. "Yttrium". The Elements (PDF). Fermi National Accelerator Laboratory. pp. 4–33. ISBN 0-04-910081-5. Archived from the original (pdf) on June 26, 2008. Retrieved 2008-08-26.
10. Daane 1968, p. 817
11. Emsley 2001, p. 498
12. Daane 1968, p. 810
13. Daane 1968, p. 815
14. Greenwood 1997, p. 945
15. Greenwood 1997, p. 1234
16. Greenwood 1997, p. 948
17. Greenwood 1997, p. 947
18. Cloke, F. Geoffrey N. (1993). "Zero Oxidation State Compounds of Scandium, Yttrium, and the Lanthanides". Chem. Soc. Rev. 22: 17–24. doi:10.1039/CS9932200017.
19. Schumann, Herbert; Fedushkin, Igor L. (2006). "Scandium, Yttrium & The Lanthanides: Organometallic Chemistry". Encyclopedia of Inorganic Chemistry. doi:10.1002/0470862106.ia212. ISBN 0-470-86078-2.
20. Nikolai B., Mikheev; Auerman, L N; Rumer, Igor A; Kamenskaya, Alla N; Kazakevich, M Z (1992). "The anomalous stabilisation of the oxidation state 2+ of lanthanides and actinides". Russian Chemical Reviews 61 (10): 990–998. Bibcode:1992RuCRv..61..990M. doi:10.1070/RC1992v061n10ABEH001011.
21. Kang, Weekyung; E. R. Bernstein (2005). "Formation of Yttrium Oxide Clusters Using Pulsed Laser Vaporization". Bull. Korean Chem. Soc. 26 (2): 345–348. doi:10.5012/bkcs.2005.26.2.345.
22. Turner, Jr., Francis M.; Berolzheimer, Daniel D.; Cutter, William P.; Helfrich, John (1920). The Condensed Chemical Dictionary. New York: Chemical Catalog Company. p. 492. Retrieved 2008-08-12.
23. Spencer, James F. (1919). The Metals of the Rare Earths. New York: Longmans, Green, and Co. p. 135. Retrieved 2008-08-12.
24. Pack, Andreas; Sara S. Russell; J. Michael G. Shelley & Mark van Zuilen (2007). "Geo- and cosmochemistry of the twin elements yttrium and holmium". Geochimica et Cosmochimica Acta 71 (18): 4592–4608. Bibcode:2007GeCoA..71.4592P. doi:10.1016/j.gca.2007.07.010.
25. Greenwood 1997, pp. 12–13
26. NNDC contributors (2008). Alejandro A. Sonzogni (Database Manager), ed. "Chart of Nuclides". Upton, New York: National Nuclear Data Center, Brookhaven National Laboratory. Retrieved 2008-09-13.
27. Audi, Georges; Bersillon, O.; Blachot, J.; Wapstra, A.H. (2003). "The NUBASE Evaluation of Nuclear and Decay Properties". Nuclear Physics A (Atomic Mass Data Center) 729: 3–128. Bibcode:2003NuPhA.729....3A. doi:10.1016/j.nuclphysa.2003.11.001.
28. Emsley 2001, p. 496
29. Gadolin 1794
30. Greenwood 1997, p. 944
31. Mosander, Carl Gustaf (1843). "Ueber die das Cerium begleitenden neuen Metalle Lathanium und Didymium, so wie über die mit der Yttererde vorkommen-den neuen Metalle Erbium und Terbium". Annalen der Physik und Chemie (in German) 60 (2): 297–315. Bibcode:1843AnP...136..297M. doi:10.1002/andp.18431361008.
32. Britannica contributors (2005). "Ytterbium". Encyclopaedia Britannica (Encyclopædia Britannica, Inc.).
33. Stwertka 1998, p. 115
34. Heiserman, David L. (1992). "Element 39: Yttrium". Exploring Chemical Elements and their Compounds. New York: TAB Books. pp. 150–152. ISBN 0-8306-3018-X.
35. Wöhler, Friedrich (1828). "Ueber das Beryllium und Yttrium". Annalen der Physik 89 (8): 577–582. Bibcode:1828AnP....89..577W. doi:10.1002/andp.18280890805.
36. Coplen, Tyler B.; Peiser, H. S. (1998). "History of the Recommended Atomic-Weight Values from 1882 to 1997: A Comparison of Differences from Current Values to the Estimated Uncertainties of Earlier Values (Technical Report)". Pure Appl. Chem. (IUPAC's Inorganic Chemistry Division Commission on Atomic Weights and Isotopic Abundances) 70 (1): 237–257. doi:10.1351/pac199870010237.
37. Wu, M. K.; et al. (1987). "Superconductivity at 93 K in a New Mixed-Phase Y-Ba-Cu-O Compound System at Ambient Pressure". Physical Review Letters 58 (9): 908–910. Bibcode:1987PhRvL..58..908W. doi:10.1103/PhysRevLett.58.908. PMID 10035069.
38. Lenntech contributors. "yttrium". Lenntech. Retrieved 2008-08-26.
39. Emsley 2001, p. 497
40. MacDonald, N. S.; Nusbaum, R. E.; Alexander, G. V. (1952). "The Skeletal Deposition of Yttrium" (PDF). Journal of Biological Chemistry 195 (2): 837–841. PMID 14946195.
41. Emsley 2001, p. 495
42. Morteani, Giulio (1991). "The rare earths; their minerals, production and technical use". European Journal of Mineralogy 3 (4): 641–650.
43. Kanazawa, Yasuo; Kamitani, Masaharu (2006). "Rare earth minerals and resources in the world". Journal of Alloys and Compounds. 408–412: 1339–1343. doi:10.1016/j.jallcom.2005.04.033.
44. Naumov, A. V. (2008). "Review of the World Market of Rare-Earth Metals". Russian Journal of Non-Ferrous Metals 49 (1): 14–22. doi:10.1007/s11981-008-1004-6.
45. Stwertka 1998, p. 116
46. Zheng, Zuoping; Lin Chuanxian (1996). "The behaviour of rare-earth elements (REE) during weathering of granites in southern Guangxi, China". Chinese Journal of Geochemistry 15 (4): 344–352. doi:10.1007/BF02867008.
47. Holleman, Arnold F.; Wiberg, Egon; Wiberg, Nils (1985). Lehrbuch der Anorganischen Chemie (91–100 ed.). Walter de Gruyter. pp. 1056–1057. ISBN 3-11-007511-3.
48. "Mineral Commodity Summaries" (PDF). minerals.usgs.gov. Retrieved 2014-07-17.
49. Daane 1968, p. 818
50. US patent 5935888, "Porous silicon nitride with rodlike grains oriented", issued 1999-08-10, assigned to Agency Ind Science Techn (JP) and Fine Ceramics Research Ass (JP) 
51. Carley, Larry (December 2000). "Spark Plugs: What's Next After Platinum?". Counterman (Babcox). Archived from the original on 2008-05-01. Retrieved 2008-09-07.
52. US patent 4533317, Addison, Gilbert J., "Yttrium oxide mantles for fuel-burning lanterns", issued 1985-08-06, assigned to The Coleman Company, Inc. 
53. Jaffe, H.W. (1951). "The role of yttrium and other minor elements in the garnet group" (pdf). American Mineralogist: 133–155. Retrieved 2008-08-26.
54. Vajargah, S. Hosseini; Madaahhosseini, H; Nemati, Z (2007). "Preparation and characterization of yttrium iron garnet (YIG) nanocrystalline powders by auto-combustion of nitrate-citrate gel". Journal of Alloys and Compounds 430 (1–2): 339–343. doi:10.1016/j.jallcom.2006.05.023.
55. US patent 6409938, Comanzo Holly Ann, "Aluminum fluoride flux synthesis method for producing cerium doped YAG", issued 2002-06-25, assigned to General Electrics 
56. GIA contributors (1995). GIA Gem Reference Guide. Gemological Institute of America. ISBN 0-87311-019-6.
57. Kiss, Z. J.; Pressley, R. J. (1966). "Crystalline solid lasers". Proceedings of the IEEE 54 (10): 1236. doi:10.1109/PROC.1966.5112.
58. Kong, J.; Tang, D. Y.; Zhao, B.; Lu, J.; Ueda, K.; Yagi, H. & Yanagitani, T. (2005). "9.2-W diode-pumped Yb:Y₂O₃ ceramic laser". Applied Physics Letters 86 (16): 116. Bibcode:2005ApPhL..86p1116K. doi:10.1063/1.1914958.
59. Tokurakawa, M.; Takaichi, K.; Shirakawa, A.; Ueda, K.; Yagi, H.; Yanagitani, T. & Kaminskii, A. A. (2007). "Diode-pumped 188 fs mode-locked Yb³⁺:Y₂O₃ ceramic laser". Applied Physics Letters 90 (7): 071101. Bibcode:2007ApPhL..90g1101T. doi:10.1063/1.2476385.
60. Golubović, Aleksandar V.; Nikolić, Slobodanka N.; Gajić, Radoš; Đurić, Stevan; Valčić, Andreja (2002). "The growth of Nd: YAG single crystals". Journal of the Serbian Chemical Society 67 (4): 91–300. doi:10.2298/JSC0204291G.
61. "Yttrium". Periodic Table of Elements: LANL. Los Alamos National Security.
62. Berg, Jessica. "Cubic Zirconia". Emporia State University. Retrieved 2008-08-26.
63. Adams, Gregory P.; et al. (2004). "A Single Treatment of Yttrium-90-labeled CHX-A–C6.5 Diabody Inhibits the Growth of Established Human Tumor Xenografts in Immunodeficient Mice". Cancer Research 64 (17): 6200–6206. doi:10.1158/0008-5472.CAN-03-2382. PMID 15342405.
64. http://www.cghjournal.org/article/S1542-3565(13)00097-9/pdf
65. Fischer, M.; Modder, G. (2002). "Radionuclide therapy of inflammatory joint diseases". Nuclear Medicine Communications 23 (9): 829–831. doi:10.1097/00006231-200209000-00003. PMID 12195084.
66. Gianduzzo, Troy; Colombo Jr., Jose R.; Haber, Georges-Pascal; Hafron, Jason; Magi-Galluzzi, Cristina; Aron, Monish; Gill, Inderbir S.; Kaouk, Jihad H. (2008). "Laser robotically assisted nerve-sparing radical prostatectomy: a pilot study of technical feasibility in the canine model". BJU International (Cleveland: Glickman Urological Institute) 102 (5): 598–602. doi:10.1111/j.1464-410X.2008.07708.x. PMID 18694410.
67. "Yttrium Barium Copper Oxide – YBCO". Imperial College. Retrieved 2009-12-20.
68. "CDC - NIOSH Pocket Guide to Chemical Hazards - Yttrium". www.cdc.gov. Retrieved 2015-11-27.

Bibliography

• Daane, A. H. (1968). "Yttrium". In Hampel, Clifford A. The Encyclopedia of the Chemical Elements. New York: Reinhold Book Corporation. pp. 810–821. LCCN 68029938. OCLC 449569.
• Emsley, John (2001). "Yttrium". Nature's Building Blocks: An A–Z Guide to the Elements. Oxford, England, UK: Oxford University Press. pp. 495–498. ISBN 0-19-850340-7.
• Gadolin, Johan (1794). "Undersökning af en svart tung Stenart ifrån Ytterby Stenbrott i Roslagen". Kongl. Vetenskaps Academiens Nya Handlingar 15: 137–155.
• Greenwood, N. N.; Earnshaw, A. (1997). Chemistry of the Elements (2nd ed.). Oxford: Butterworth-Heinemann. ISBN 0-7506-3365-4.
• Gupta, C. K.; Krishnamurthy, N. (2005). "Ch. 1.7.10 Phosphors". Extractive metallurgy of rare earths (PDF). CRC Press. ISBN 0-415-33340-7.
• Stwertka, Albert (1998). "Yttrium". Guide to the Elements (Revised ed.). Oxford University Press. pp. 115–116. ISBN 0-19-508083-1.
• van der Krogt, Peter (2005-05-05). "39 Yttrium". Elementymology & Elements Multidict. Retrieved 2008-08-06.

Further reading

• US patent 5734166, Czirr John B., "Low-energy neutron detector based upon lithium lanthanide borate scintillators", issued 1998-03-31, assigned to Mission Support Inc. 
• EPA contributors (2008-07-31). "Strontium: Health Effects of Strontium-90". US Environmental Protection Agency. Retrieved 2008-08-26.

External links

• Yttrium at The Periodic Table of Videos (University of Nottingham)