Uranium dioxide

Uranium dioxide
Names
IUPAC names
Uranium dioxide
Uranium(IV) oxide
Other names
Urania
Uranous oxide
Identifiers
1344-57-6 YesY
ChemSpider 10454 N
RTECS number YR4705000
Properties
UO2
Molar mass 270.03 g/mol
Appearance black powder
Density 10.97 g/cm3
Melting point 2,865 °C (5,189 °F; 3,138 K)
insoluble
Structure
Fluorite (cubic), cF12
Fm3m, No. 225
a = 574.0 pm [1]
Tetrahedral (O2−); cubic (UIV)
Thermochemistry
78 J·mol−1·K−1[2]
−1084 kJ·mol−1[2]
Hazards
Safety data sheet ICSC 1251
Very toxic (T+)
Dangerous for the environment (N)
R-phrases R26/28, R33, R51/53
S-phrases (S1/2), S20/21, S45, S61
Flash point N/A
Related compounds
Related uranium oxides
 Triuranium octoxide
Uranium trioxide
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
N verify (what is YesYN ?)
Infobox references

Uranium dioxide or uranium(IV) oxide (UO2), also known as urania or uranous oxide, is an oxide of uranium, and is a black, radioactive, crystalline powder that naturally occurs in the mineral uraninite. It is used in nuclear fuel rods in nuclear reactors. A mixture of uranium and plutonium dioxides is used as MOX fuel. Prior to 1960, it was used as yellow and black color in ceramic glazes and glass.

Production

Uranium dioxide is produced by reducing uranium trioxide with hydrogen.

UO3 + H2 → UO2 + H2O at 700 °C (973 K)

This reaction plays an important part in the creation of nuclear fuel through nuclear reprocessing and uranium enrichment.

Chemistry

Structure

The solid is isostructural with (has the same structure as) fluorite (calcium fluoride), where each U is surrounded by eight O nearest neighbors in a cubic arrangement. In addition, the dioxides of cerium, plutonium and neptunium have the same structures. No other elemental dioxides have the fluorite structure. Upon melting, the measured average U-O coordination reduces from 8 in the crystalline solid (UO8 cubes), down to 6.7±0.5 (at 3270 K) in the melt.[3] Models consistent with these measurements show the melt to consist mainly of UO6 and UO7 polyhedral units, where roughly 2/3 of the connections between polyhedra are corner sharing and 1/3 are edge sharing.[3]

Oxidation

Uranium dioxide is oxidized in contact with oxygen to the triuranium octaoxide.

3 UO2 + O2 → U3O8 at 700 °C (970 K)

The electrochemistry of uranium dioxide has been investigated in detail as the galvanic corrosion of uranium dioxide controls the rate at which used nuclear fuel dissolves. See the spent nuclear fuel page for further details. Water increases the oxidation rate of plutonium and uranium metals.[4][5]

Carbonization

Uranium dioxide is carbonized in contact with carbon, forming uranium carbide and carbon monoxide.

UO2 + 4 C → UC2 + 2 CO

This process must be done under an inert gas as uranium carbide is easily oxidized back into uranium oxide.

Uses

Nuclear fuel

UO2 is used mainly as nuclear fuel, specifically as UO2 or as a mixture of UO2 and PuO2 (plutonium dioxide) called a mixed oxide (MOX fuel), in the form of fuel rods in nuclear reactors.

Note that the thermal conductivity of uranium dioxide is very low when compared with uranium, uranium nitride, uranium carbide and zirconium cladding material. This low thermal conductivity can result in localised overheating in the centres of fuel pellets. The graph below shows the different temperature gradients in different fuel compounds. For these fuels the thermal power density is the same and the diameter of all the pellets are the same.

Color for ceramic glaze

Geiger counter (kit without housing) audibly reacting to an orange Fiestaware shard.

Uranium oxide (urania) was used to color glass and ceramics prior to World War II. Urania-based ceramics become green or black when fired in a reducing atmosphere and yellow to orange when fired in an oxidizing atmosphere. Orange-colored Fiestaware is a well-known example of a product with a urania-colored glaze. Urania has also been used in formulations of enamel, uranium glass, and porcelain. It is possible to determine with a Geiger counter if a glaze or glass contains urania.

Other use

Depleted UO2 (DUO2) can be used as a material for radiation shielding. For example, DUCRETE is a "heavy concrete" material where gravel is replaced with uranium dioxide aggregate; this material is investigated for use for casks for radioactive waste. Casks can be also made of DUO2-steel cermet, a composite material made of an aggregate of uranium dioxide serving as radiation shielding, graphite and/or silicon carbide serving as neutron radiation absorber and moderator, and steel as the matrix, whose high thermal conductivity allows easy removal of decay heat.

Depleted uranium dioxide can be also used as a catalyst, e.g. for degradation of volatile organic compounds in gaseous phase, oxidation of methane to methanol, and removal of sulfur from petroleum. It has high efficiency and long-term stability when used to destroy VOCs when compared with some of the commercial catalysts, such as precious metals, TiO2, and Co3O4 catalysts. Much research is being done in this area, DU being favoured for the uranium component due to its low radioactivity.[6]

The use of uranium dioxide as a material for rechargeable batteries is being investigated. The batteries could have high power density and potential of 4.7 V per cell. Another investigated application is in photoelectrochemical cells for solar-assisted hydrogen production where UO2 is used as a photoanode. In earlier times, uranium dioxide was also used as heat conductor for current limitation (URDOX-resistor), which was the first use of its semiconductor properties.

Semiconductor properties

The band gap of uranium dioxide is comparable to these of silicon and gallium arsenide, near the optimum for efficiency vs band gap curve for absorption of solar radiation, suggesting its possible use for very efficient solar cells based on Schottky diode structure; it also absorbs at five different wavelengths, including infrared, further enhancing its efficiency. Its intrinsic conductivity at room temperature is about the same as of single crystal silicon.[7]

The dielectric constant of uranium dioxide is about 22, which is almost twice as high as of silicon (11.2) and GaAs (14.1). This is an advantage over Si and GaAs in construction of integrated circuits, as it may allow higher density integration with higher breakdown voltages and with lower susceptibility to the CMOS tunneling breakdown.

The Seebeck coefficient of uranium dioxide at room temperature is about 750 µV/K, a value significantly higher than the 270 µV/K of thallium tin telluride (Tl2SnTe5) and thallium germanium telluride (Tl2GeTe5) and of bismuth-tellurium alloys, other materials promising for thermoelectric power generation applications and Peltier elements.

The radioactive decay impact of the235U and238U on its semiconducting properties was not measured as of 2005. Due to the slow decay rate of these isotopes, it should not meaningfully influence the properties of uranium dioxide solar cells and thermoelectric devices, but it may become an important factor for VLSI chips. Use of depleted uranium oxide is necessary for this reason. The capture of alpha particles emitted during radioactive decay as helium atoms in the crystal lattice may also cause gradual long-term changes in its properties.

The stoichiometry of the material dramatically influences its electrical properties. For example, the electrical conductivity of UO1.994 is orders of magnitude lower at higher temperatures than the conductivity of UO2.001.

Uranium dioxide, like U3O8, is a ceramic material capable of withstanding high temperatures (about 2300 °C, in comparison with at most 200 °C for silicon or GaAs), making it suitable for high-temperature applications like thermophotovoltaic devices.

Uranium dioxide is also resistant to radiation damage, making it useful for rad-hard devices for special military and aerospace applications.

A Schottky diode of U3O8 and a p-n-p transistor of UO2 were successfully manufactured in a laboratory.[8]

Toxicity

Uranium dioxide is known to be absorbed by phagocytosis in the lungs.[9]

See also

References

  1. ↑ http://www.sckcen.be/microstructure/Infrastructure/XRD/Infrastructure_XRD_XPert_Powder_UO2%20lattice%20param.htm. Missing or empty |title= (help)
  2. 1 2 Zumdahl, Steven S. (2009). Chemical Principles 6th Ed. Houghton Mifflin Company. p. A23. ISBN 0-618-94690-X.
  3. 1 2 Skinner, Lawrie B (2014). "Molten uranium dioxide structure and dynamics". Science 346: 984–7. Bibcode:2014Sci...346..984S. doi:10.1126/science.1259709.
  4. ↑ Haschke, John M; Allen, Thomas H; Morales, Luis A (1999). "Reactions of Plutonium Dioxide with Water and Oxygen-Hydrogen Mixtures: Mechanisms for Corrosion of Uranium and Plutonium" (PDF). Retrieved 2009-06-06.
  5. ↑ Haschke, John M; Allen, Thomas H; Morales, Luis A (2001). "Reactions of plutonium dioxide with water and hydrogen–oxygen mixtures: Mechanisms for corrosion of uranium and plutonium". Journal of Alloys and Compounds 314: 78. doi:10.1016/S0925-8388(00)01222-6.
  6. ↑ Hutchings GJ; Heneghan, Catherine S.; Hudson, Ian D.; Taylor, Stuart H. (1996). "A Uranium-Oxide-Based Catalysts for the Destruction of Volatile Chloro-Organic compounds". Nature 384 (6607): 341–343. Bibcode:1996Natur.384..341H. doi:10.1038/384341a0.
  7. ↑ An, Y.Q.; et al. (2011). "Ultrafast Hopping Dynamics of 5f Electrons in the Mott Insulator UO(2) Studied by Femtosecond Pump-Probe Spectroscopy". Phys. Rev. Lett. 107 (20): 207402. Bibcode:2011PhRvL.106t7402A. doi:10.1103/PhysRevLett.106.207402. PMID 22181773.
  8. ↑ Meek, Thomas T.; Roedern, B. von (2008). "Semiconductor devices fabricated from actinide oxides". Vacuum 83 (1): 226–228. Bibcode:2008Vacuu..83..226M. doi:10.1016/j.vacuum.2008.04.005.
  9. ↑ Principles of Biochemical Toxicology. Timbrell, John. PA 2008 ISBN 0-8493-7302-6

Further reading

External links

This article is issued from Wikipedia - version of the Saturday, April 30, 2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.