Supercapacitor

A range of supercapacitors

Hierarchical classification of supercapacitors and related types

A supercapacitor (SC) (sometimes ultracapacitor, formerly electric double-layer capacitor (EDLC)) is a high-capacity electrochemical capacitor with capacitance values much higher than other capacitors (but lower voltage limits) that bridge the gap between electrolytic capacitors and rechargeable batteries. They typically store 10 to 100 times more energy per unit volume or mass than electrolytic capacitors, can accept and deliver charge much faster than batteries, and tolerate many more charge and discharge cycles than rechargeable batteries. They are however 10 times larger than conventional batteries for a given charge.

Supercapacitors are used in applications requiring many rapid charge/discharge cycles rather than long term compact energy storage: within cars, buses, trains, cranes and elevators, where they are used for regenerative braking, short-term energy storage or burst-mode power delivery. Smaller units are used as memory backup for static random-access memory (SRAM).

Supercapacitors do not use the conventional solid dielectric of ordinary capacitors. They use electrostatic double-layer capacitance or electrochemical pseudocapacitance or a combination of both instead:

• Electrostatic double-layer capacitors use carbon electrodes or derivatives with much higher electrostatic double-layer capacitance than electrochemical pseudocapacitance, achieving separation of charge in a Helmholtz double layer at the interface between the surface of a conductive electrode and an electrolyte. The separation of charge is of the order of a few ångströms (0.3–0.8 nm), much smaller than in a conventional capacitor.
• Electrochemical pseudocapacitors use metal oxide or conducting polymer electrodes with a high amount of electrochemical pseudocapacitance. Pseudocapacitance is achieved by Faradaic electron charge-transfer with redox reactions, intercalation or electrosorption.
• Hybrid capacitors, such as the lithium-ion capacitor, use electrodes with differing characteristics: one exhibiting mostly electrostatic capacitance and the other mostly electrochemical capacitance.

The electrolyte forms a conductive connection between the two electrodes which distinguishes them from electrolytic capacitors where the electrolyte is the second electrode (the cathode). Supercapacitors are polarized by design with asymmetric electrodes, or, for symmetric electrodes, by a potential applied during manufacture.

History

Development of the double layer and pseudocapacitance models (see Double layer (interfacial)).

Evolution of components

In the early 1950s, General Electric engineers began experimenting with porous carbon electrodes, in the design of capacitors, from the design of fuel cells and rechargeable batteries. Activated charcoal is an electrical conductor that is an extremely porous "spongy" form of carbon with a high specific surface area. In 1957 H. Becker developed a "Low voltage electrolytic capacitor with porous carbon electrodes".^[1][2][3] He believed that the energy was stored as a charge in the carbon pores as in the pores of the etched foils of electrolytic capacitors. Because the double layer mechanism was not known by him at the time, he wrote in the patent: "It is not known exactly what is taking place in the component if it is used for energy storage, but it leads to an extremely high capacity."

General Electric did not immediately pursue this work. In 1966 researchers at Standard Oil of Ohio (SOHIO) developed another version of the component as "electrical energy storage apparatus", while working on experimental fuel cell designs.^[4][5] The nature of electrochemical energy storage was not described in this patent. Even in 1970, the electrochemical capacitor patented by Donald L. Boos was registered as an electrolytic capacitor with activated carbon electrodes.^[6]

Early electrochemical capacitors used two aluminum foils covered with activated carbon—the electrodes—which were soaked in an electrolyte and separated by a thin porous insulator. This design gave a capacitor with a capacitance on the order of one farad, significantly higher than electrolytic capacitors of the same dimensions. This basic mechanical design remains the basis of most electrochemical capacitors.

SOHIO did not commercialize their invention, licensing the technology to NEC, who finally marketed the results as "supercapacitors" in 1971, to provide backup power for computer memory.^[5]

Ph.D., Brian Evans Conway within the John Bockris Group At Imperial College, London 1947

Between 1975 and 1980 Brian Evans Conway conducted extensive fundamental and development work on ruthenium oxide electrochemical capacitors. In 1991 he described the difference between "Supercapacitor" and "Battery" behavior in electrochemical energy storage. In 1999 he coined the term supercapacitor to explain the increased capacitance by surface redox reactions with faradaic charge transfer between electrodes and ions.^[7][8] His "supercapacitor" stored electrical charge partially in the Helmholtz double-layer and partially as result of faradaic reactions with "pseudocapacitance" charge transfer of electrons and protons between electrode and electrolyte. The working mechanisms of pseudocapacitors are redox reactions, intercalation and electrosorption (adsorption onto a surface). With his research, Conway greatly expanded the knowledge of electrochemical capacitors.

The market expanded slowly. That changed around 1978 as Panasonic marketed its "Goldcaps” brand.^[9] This product became a successful energy source for memory backup applications.^[5] Competition started only years later. In 1987 ELNA "Dynacap"s entered the market.^[10] First generation EDLC's had relatively high internal resistance that limited the discharge current. They were used for low current applications such as powering SRAM chips or for data backup.

At the end of the 1980s, improved electrode materials increased capacitance values. At the same time, the development of electrolytes with better conductivity lowered the equivalent series resistance (ESR) increasing charge/discharge currents. The first supercapacitor with low internal resistance was developed in 1982 for military applications through the Pinnacle Research Institute (PRI), and were marketed under the brand name "PRI Ultracapacitor". In 1992, Maxwell Laboratories (later Maxwell Technologies) took over this development. Maxwell adopted the term Ultracapacitor from PRI and called them "Boost Caps"^[11] to underline their use for power applications.

Since capacitors' energy content increases with the square of the voltage, researchers were looking for a way to increase the electrolyte's breakdown voltage. In 1994 using the anode of a 200V high voltage tantalum electrolytic capacitor, David A. Evans developed an "Electrolytic-Hybrid Electrochemical Capacitor".^[12][13] These capacitors combine features of electrolytic and electrochemical capacitors. They combine the high dielectric strength of an anode from an electrolytic capacitor with the high capacitance of a pseudocapacitive metal oxide (ruthenium (IV) oxide) cathode from an electrochemical capacitor, yielding a hybrid electrochemical capacitor. Evans' capacitors, coined Capattery,^[14] had an energy content about a factor of 5 higher than a comparable tantalum electrolytic capacitor of the same size.^[15] Their high costs limited them to specific military applications.

Recent developments include lithium-ion capacitors. These hybrid capacitors were pioneered by FDK in 2007.^[16] They combine an electrostatic carbon electrode with a pre-doped lithium-ion electrochemical electrode. This combination increases the capacitance value. Additionally, the pre-doping process lowers the anode potential and results in a high cell output voltage, further increasing energy density.

Research departments active in many companies and universities^[17] are working to improve characteristics such as energy density, power density, and cycle stability and to reduce production costs.

Basics

Basic design

Typical construction of a supercapacitor: 1) Power source, 2) Collector, 3) Polarized electrode, 4) Helmholtz double layer, 5) Electrolyte having positive and negative ions, 6) Separator.

Electrochemical capacitors (supercapacitors) consist of two electrodes separated by an ion-permeable membrane (separator), and an electrolyte ionically connecting both electrodes. When the electrodes are polarized by an applied voltage, ions in the electrolyte form electric double layers of opposite polarity to the electrode's polarity. For example, positively polarized electrodes will have a layer of negative ions at the electrode/electrolyte interface along with a charge-balancing layer of positive ions adsorbing onto the negative layer. The opposite is true for the negatively polarized electrode.

Additionally, depending on electrode material and surface shape, some ions may permeate the double layer becoming specifically adsorbed ions and contribute with pseudocapacitance to the total capacitance of the supercapacitor.

Capacitance distribution

The two electrodes form a series circuit of two individual capacitors C₁ and C₂. The total capacitance C_total is given by the formula

$C_\text{total} = \frac{C_1 \cdot C_2}{C_1 + C_2}$

Supercapacitors may have either symmetric or asymmetric electrodes. Symmetry implies that both electrodes have the same capacitance value, yielding a total capacitance of half the value of each single electrode (if C₁ = C₂, then C_total = 0.5 ⋅ C₁). For asymmetric capacitors, the total capacitance can be taken as that of the electrode with the smaller capacitance (if C₁ >> C₂, then C_total ≈ C₂).

Storage principles

Electrochemical capacitors use the double-layer effect to store electric energy, however, this double-layer has no conventional solid dielectric to separate the charges. There are two storage principles in the electric double-layer of the electrodes that contribute to the total capacitance of an electrochemical capacitor:^[18]

• Double-layer capacitance, electrostatic storage of the electrical energy achieved by separation of charge in a Helmholtz double layer.^[19]
• Pseudocapacitance, electrochemical storage of the electrical energy achieved by faradaic redox reactions with charge-transfer.^[11]

Both capacitances are only separable by measurement techniques. The amount of charge stored per unit voltage in an electrochemical capacitor is primarily a function of the electrode size, although the amount of capacitance of each storage principle can vary extremely.

Practically, these storage principles yield a capacitor with a capacitance value in the order of 1 to 100 farad.

Electrostatic double-layer capacitance

Simplified view of a double-layer of negative ions in the electrode and solvated positive ions in the liquid electrolyte, separated by a layer of polarized solvent molecules.

Every electrochemical capacitor has two electrodes, mechanically separated by a separator, which are ionically connected to each other via the electrolyte. The electrolyte is a mixture of positive and negative ions dissolved in a solvent such as water. At each of the two electrodes surfaces originates an area in which the liquid electrolyte contacts the conductive metallic surface of the electrode. This interface forms a common boundary among two different phases of matter, such as an insoluble solid electrode surface and an adjacent liquid electrolyte. In this interface occurs a very special phenomenon of the double layer effect.^[20]

Applying a voltage to an electrochemical capacitor causes both electrodes in the capacitor to generate electrical double-layers. These double-layers consist of two layers of charges: one electronic layer is in the surface lattice structure of the electrode, and the other, with opposite polarity, emerges from dissolved and solvated ions in the electrolyte. The two layers are separated by a monolayer of solvent molecules, e. g. for water as solvent by water molecules, called inner Helmholtz plane (IHP). Solvent molecules adhere by physical adsorption on the surface of the electrode and separate the oppositely polarized ions from each other, and can be idealised as a molecular dielectric. In the process, there is no transfer of charge between electrode and electrolyte, so the forces that cause the adhesion are not chemical bonds but physical forces (e.g. electrostatic forces). The adsorbed molecules are polarized but, due to the lack of transfer of charge between electrolyte and electrode, suffered no chemical changes.

The amount of charge in the electrode is matched by the magnitude of counter-charges in outer Helmholtz plane (OHP). This double-layer phenomena store electrical charges as in a conventional capacitor. The double-layer charge forms a static electric field in the molecular layer of the solvent molecules in the IHP that corresponds to the strength of the applied voltage.

Structure and function of an ideal double-layer capacitor. Applying a voltage to the capacitor at both electrodes a Helmholtz double-layer will be formed separating the ions in the electrolyte in a mirror charge distribution of opposite polarity

The double-layer serves approximately as the dielectric layer in a conventional capacitor, albeit with the thickness of a single molecule. Thus, the standard formula for conventional plate capacitors can be used to calculate their capacitance:^[21]

$C= \varepsilon\frac{A}{d}$.

Accordingly, capacitance C is greatest in capacitors made from materials with a high permittivity ε, large electrode plate surface areas A and small distance between plates d. As a result, double-layer capacitors have much higher capacitance values than conventional capacitors, arising from the extremely large surface area of activated carbon electrodes and the extremely thin double-layer distance on the order of a few ångströms (0.3-0.8 nm).^[11][19]

The main drawback of carbon electrodes of double-layer SCs is small values of quantum capacitance ^[22] which act in series ^[23] with capacitance of ionic space charge. Therefore, further increase of density of capacitance in SCs can be connected with increasing of quantum capacitance of carbon electrode nanostructures.^[22]

The amount of charge stored per unit voltage in an electrochemical capacitor is primarily a function of the electrode size. The electrostatic storage of energy in the double-layers is linear with respect to the stored charge, and correspond to the concentration of the adsorbed ions. Also, while charge in conventional capacitors is transferred via electrons, capacitance in double-layer capacitors is related to the limited moving speed of ions in the electrolyte and the resistive porous structure of the electrodes. Since no chemical changes take place within the electrode or electrolyte, charging and discharging electric double-layers in principle is unlimited. Real supercapacitors lifetimes are only limited by electrolyte evaporation effects.

Electrochemical Pseudocapacitance

Simplified view of a double-layer with specifically adsorbed ions which have submitted their charge to the electrode to explain the faradaic charge-transfer of the pseudocapacitance.

Applying a voltage at the electrochemical capacitor terminals moves electrolyte ions to the opposite polarized electrode and forms a double-layer in which a single layer of solvent molecules acts as separator. Pseudocapacitance can originate when specifically adsorbed ions out of the electrolyte pervade the double-layer. This pseudocapacitance stores electrical energy by means of reversible faradaic redox reactions on the surface of suitable electrodes in an electrochemical capacitor with a electric double-layer.^{[7][18][19][24][25]} Pseudocapacitance is accompanied with an electron charge-transfer between electrolyte and electrode coming from a de-solvated and adsorbed ion whereby only one electron per charge unit is participating. This faradaic charge transfer originates by a very fast sequence of reversible redox, intercalation or electrosorption processes. The adsorbed ion has no chemical reaction with the atoms of the electrode (no chemical bonds arise^[26]) since only a charge-transfer take place.

A cyclic voltammogram shows the fundamental differences between static capacitance (rectangular) and pseudocapacitance (curved)

The electrons involved in the faradaic processes are transferred to or from valence electron states (orbitals) of the redox electrode reagent. They enter the negative electrode and flow through the external circuit to the positive electrode where a second double-layer with an equal number of anions has formed. The electrons reaching the positive electrode are not transferred to the anions forming the double-layer, instead they remain in the strongly ionized and "electron hungry" transition-metal ions of the electrode's surface. As such, the storage capacity of faradaic pseudocapacitance is limited by the finite quantity of reagent in the available surface.

A faradaic pseudocapacitance only occurs together with a static double-layer capacitance, and its magnitude may exceed the value of double-layer capacitance for the same surface area by factor 100, depending on the nature and the structure of the electrode because all the pseudocapacitance reactions take place only with de-solvated ions, which are much smaller than solvated ion with their solvating shell.^[7][24] The amount of pseudocapacitance has a linear function within narrow limits determined by the potential-dependent degree of surface coverage of the adsorbed anions.

The ability of electrodes to accomplish pseudocapacitance effects by redox reactions, intercalation or electrosorption strongly depends on the chemical affinity of electrode materials to the ions adsorbed on the electrode surface as well as on the structure and dimension of the electrode pores. Materials exhibiting redox behavior for use as electrodes in pseudocapacitors are transition-metal oxides like RuO₂, IrO₂, or MnO₂ inserted by doping in the conductive electrode material such as active carbon, as well as conducting polymers such as polyaniline or derivatives of polythiophene covering the electrode material.

The amount of electric charge stored in a pseudocapacitance is linearly proportional to the applied voltage. The unit of pseudocapacitance is farad.

Potential distribution

Charge storage principles of different capacitor types and their internal potential distribution

Basic illustration of the functionality of a supercapacitor, the voltage distribution inside of the capacitor and its simplified equivalent DC circuit

The voltage behavior of supercapacitors and batteries during charging/discharging differs clearly

Conventional capacitors (also known as electrostatic capacitors), such as ceramic capacitors and film capacitors, consist of two electrodes which are separated by a dielectric material. When charged, the energy is stored in a static electric field that permeates the dielectric between the electrodes. The total energy increases with the amount of stored charge, which in turn correlates linearly with the potential (voltage) between the plates. The maximum potential difference between the plates (the maximal voltage) is limited by the dielectric's breakdown field strength. The same static storage also applies for electrolytic capacitors in which most of the potential decreases over the anode's thin oxide layer. The somewhat resistive liquid electrolyte (cathode) accounts for a small decrease of potential for "wet" electrolytic capacitors, while electrolytic capacitors with solid conductive polymer electrolyte this voltage drop is negligible.

In contrast, electrochemical capacitors (supercapacitors) consists of two electrodes separated by an ion-permeable membrane (separator) and electrically connected via an electrolyte. Energy storage occurs within the double-layers of both electrodes as a mixture of a double-layer capacitance and pseudocapacitance. When both electrodes have approximately the same resistance (internal resistance), the potential of the capacitor decreases symmetrically over both double-layers, whereby a voltage drop across the equivalent series resistance (ESR) of the electrolyte is achieved. For asymmetrical supercapacitors like hybrid capacitors the voltage drop between the electrodes could be asymmetrically. The maximum potential across the capacitor (the maximal voltage) is limited by the electrolyte decomposition voltage.

Both electrostatic and electrochemical energy storage in supercapacitors are linear with respect to the stored charge, just as in conventional capacitors. The voltage between the capacitor terminals is linear with respect to the amount of stored energy. Such linear voltage gradient differs from rechargeable electrochemical batteries, in which the voltage between the terminals remains independent of the amount of stored energy, providing a relatively constant voltage.

Styles

Supercapacitors are made in different styles such as flat with a single pair of electrodes, wound in a cylindrical case or stacked in a rectangular case. Because they cover a broad range of capacitance values the size of the cases can vary.

• Different styles of supercapacitors
• 

  Flat style of a supercapacitor used for mobile components

• 

  Typical button style supercapacitor for PCB mounting used for memory backup

• 

  Radial style of a supercapacitor for PCB mounting used for industrial applications

Construction details

• Construction details of wound and stacked supercapacitors with activated carbon electrodes
• 

  Schematic construction of a wound supercapacitor
  1.Terminals, 2.Safety vent, 3.Sealing disc, 4.Aluminum can, 5.Positive pole, 6.Separator, 7.Carbon electrode, 8.Collector, 9.Carbon electrode, 10.Negative pole

• 

  Schematic construction of a supercapacitor with stacked electrodes
  1.Positive electrode, 2.Negative electrode, 3.Separator

Supercapacitors are constructed with two metal foils (current collectors), each coated with an electrode material such as activated carbon, which serve as the power connection between the electrode material and the external terminals of the capacitor. Specifically to the electrode material is its very large surface area. In this example the activated carbon is electrochemically etched, so that the surface of the material is about a factor 100,000 larger than the smooth surface. The electrodes are kept apart by an ion-permeable membrane (separator) used as an insulator to protect the electrodes against short circuits. This construction is subsequently rolled or folded into a cylindrical or rectangular shape and can be stacked in an aluminum can or an adaptable rectangular housing. Then the cell is impregnated with a liquid or viscous electrolyte of organic or aqueous type. The electrolyte, an ionic conductor, enters the pores of the electrodes and serves as the conductive connection between the electrodes across the separator. Finally the housing is hermetically sealed to ensure stable behavior over the specified lifetime.

Materials

The properties of supercapacitors come from the interaction of their internal materials. Especially, the combination of electrode material and type of electrolyte determine the functionality and thermal and electrical characteristics of the capacitors.

Supercapacitor types

Family tree of supercapacitor types. Double-layer capacitors and pseudocapacitors as well as hybrid capacitors are defined over their electrode designs.

As described above, electrical energy is stored in supercapacitors via two storage principles: static double-layer capacitance and electrochemical pseudocapacitance; and the distribution of the two types of capacitance depends on the material and structure of the electrodes. There are three types of supercapacitors based on storage principle:^[11][19]

• Double-layer capacitors (EDLCs) – with activated carbon electrodes or derivatives with much higher electrostatic double-layer capacitance than electrochemical pseudocapacitance
• Pseudocapacitors – with transition metal oxide or conducting polymer electrodes with a high electrochemical pseudocapacitance
• Hybrid capacitors – with asymmetric electrodes, one of which exhibits mostly electrostatic and the other mostly electrochemical capacitance, such as lithium-ion capacitors

Electrodes

A micrograph of activated carbon under bright field illumination on a light microscope. Notice the fractal-like shape of the particles hinting at their enormous surface area. Each particle in this image, despite being only around 0.1 mm across, has a surface area of several square meters.

Supercapacitor electrodes are generally thin coatings applied and electrically connected to a conductive, metallic current collector. Electrodes must have good conductivity, high temperature stability, long-term chemical stability (inertness), high corrosion resistance and high surface areas per unit volume and mass. Other requirements include environmental friendliness and low cost.

The amount of double-layer as well as pseudocapacitance stored per unit voltage in a supercapacitor is predominantly a function of the electrode surface area. Therefore, supercapacitor electrodes are typically made of porous, spongy material with an extraordinarily high specific surface area, such as activated carbon. Additionally, the ability of the electrode material to perform faradaic charge transfers enhances the total capacitance.

Generally the smaller the electrode's pores, the greater the capacitance and energy density. However, smaller pores increase (ESR) and decrease power density. Applications with high peak currents require larger pores and low internal losses, while applications requiring high energy density need small pores.

Electrodes for EDLCs

The most commonly used electrode material for supercapacitors is carbon in various manifestations such as activated carbon (AC), carbon fibre-cloth (AFC), carbide-derived carbon (CDC), carbon aerogel, graphite (graphene), graphane^[27] and carbon nanotubes (CNTs).^[18][28][29]

Carbon-based electrodes exhibit predominantly static double-layer capacitance, even though a small amount of pseudocapacitance may also be present depending on the pore size distribution. Pore sizes in carbons typically range from micropores (less than 2 nm) to mesopores (2-50 nm),^[30] but only micropores (<2 nm) contribute to pseudocapacitance. As pore size approaches the solvation shell size, solvent molecules are excluded and only unsolvated ions fill the pores (even for large ions), increasing ionic packing density and storage capability by faradaic H
2 intercalation.^[18]

Activated carbon

Activated carbon (AC) was the first material chosen for EDLC electrodes. Even though its electrical conductivity is approximately 0.003% that of metals (1,250 to 2,000 S/m), it is sufficient for supercapacitors.^[19][11]

Activated carbon is an extremely porous form of carbon with a high specific surface area — a common approximation is that 1 gram (0.035 oz) (a pencil-eraser-sized amount) has a surface area of roughly 1,000 to 3,000 square metres (11,000 to 32,000 sq ft)^[28][30] — about the size of 4 to 12 tennis courts. The bulk form used in electrodes is low-density with many pores, giving high double-layer capacitance.

Solid activated carbon, also termed consolidated amorphous carbon (CAC) is the most used electrode material for supercapacitors and may be cheaper than other carbon derivatives.^[31] It is produced from activated carbon powder pressed into the desired shape, forming a block with a wide distribution of pore sizes. An electrode with a surface area of about 1000 m²/g results in a typical double-layer capacitance of about 10 μF/cm² and a specific capacitance of 100 F/g.

As of 2010 virtually all commercial supercapacitors use powdered activated carbon made from coconut shells.^[32] Coconut shells produce activated carbon with more micropores than does charcoal made from wood.^[30]

Activated carbon fibres

Activated carbon fibres (ACF) are produced from activated carbon and have a typical diameter of 10 µm. They can have micropores with a very narrow pore-size distribution that can be readily controlled. The surface area of AFC woven into a textile is about 2500 m²/g. Advantages of AFC electrodes include low electrical resistance along the fibre axis and good contact to the collector.^[28]

As for activated carbon, AFC electrodes exhibit predominantly double-layer capacitance with a small amount of pseudocapacitance due to their micropores.

Carbon aerogel

A block of aerogel in hand

Carbon aerogel is a highly porous, synthetic, ultralight material derived from an organic gel in which the liquid component of the gel has been replaced with a gas. It is also called "frozen smoke".

Aerogel electrodes are made via pyrolysis of resorcinol-formaldehyde aerogels^[33] and are more conductive than most activated carbons. They enable thin and mechanically stable electrodes with a thickness in the range of several hundred micrometres (µm) and with uniform pore size. Aerogel electrodes also provide mechanical and vibration stability for supercapacitors used in high-vibration environments.

Researchers have created a carbon aerogel electrode with gravimetric densities of about 400–1200 m²/g and volumetric capacitance of 104 F/cm³, yielding an energy density of 325 kJ/kg (90 Wh/kg) and power density of 20 W/g.^[34][35]

Standard aerogel electrodes exhibit predominantly double-layer capacitance. Aerogel electrodes that incorporate composite material can add a high amount of pseudocapacitance.^[36]

Carbide-derived carbon

Pore size distributions for different carbide precursors.

Carbide-derived carbon (CDC), also known as tunable nanoporous carbon, is a family of carbon materials derived from carbide precursors, such as binary silicon carbide and titanium carbide, that are transformed into pure carbon via physical (e.g., thermal decomposition) or chemical (e.g., halogenation) processes.^[37][38]

Carbide-derived carbons can exhibit high surface area and tunable pore diameters (from micropores to mesopores) to maximize ion confinement, increasing pseudocapacitance by faradaic H
2 adsorption treatment. CDC electrodes with tailored pore design offer as much as 75% greater energy density than conventional activated carbons.

As of 2015, a CDC supercapacitor offered an energy density of 10.1 Wh/kg, 3,500 F capacitance and over one million charge/discharge cycles.^[39]

Graphene

Graphene is an atomic-scale honeycomb lattice made of carbon atoms.

Graphene is a one-atom thick sheet of graphite, with atoms arranged in a regular hexagonal pattern,^[40][41] also called "nanocomposite paper".^[42]

Graphene has a theoretical specific surface area of 2630 m²/g which can theoretically lead to a capacitance of 550 F/g. In addition, an advantage of graphene over activated carbon is its higher electrical conductivity. As of 2012 a new development used graphene sheets directly as electrodes without collectors for portable applications.^[43][44]

In one embodiment, a graphene-based supercapacitor uses curved graphene sheets that do not stack face-to-face, forming mesopores that are accessible to and wettable by ionic electrolytes at voltages up to 4 V. A specific energy density of 85.6 Wh/kg (308 kJ/kg) is obtained at room temperature equaling that of a conventional nickel metal hydride battery, but with 100-1000 times greater power density.^[45][46]

The two-dimensional structure of graphene improves charging and discharging. Charge carriers in vertically oriented sheets can quickly migrate into or out of the deeper structures of the electrode, thus increasing currents. Such capacitors may be suitable for 100/120 Hz filter applications, which are unreachable for supercapacitors using other carbon materials.^[47]

Carbon nanotubes

A scanning tunneling microscopy image of single-walled carbon nanotube

SEM image of carbon nanotube bundles with a surface of about 1500 m²/g

Carbon nanotubes (CNTs), also called buckytubes, are carbon molecules with a cylindrical nanostructure. They have a hollow structure with walls formed by one-atom-thick sheets of graphene. These sheets are rolled at specific and discrete ("chiral") angles, and the combination of chiral angle and radius controls properties such as electrical conductivity, electrolyte wettability and ion access. Nanotubes are categorized as single-walled nanotubes (SWNTs) or multi-walled nanotubes (MWNTs). The latter have one or more outer tubes successively enveloping a SWNT, much like the Russian matryoshka dolls. SWNTs have diameters ranging between 1 and 3 nm. MWNTs have thicker coaxial walls, separated by spacing (0.34 nm) that is close to graphene's interlayer distance.

Nanotubes can grow vertically on the collector substrate, such as a silicon wafer. Typical lengths are 20 to 100 µm.^[48]

Carbon nanotubes can greatly improve capacitor performance, due to the highly wettable surface area and high conductivity.^[49][50]

A SWCNTs-based supercapacitor with aqueous electrolyte was systematically studied at University of Delaware in Prof. Bingqing Wei's group. Li et al.,for the first time, discovered that the ion-size effect and the electrode-electrolyte wettability are the dominant factors affecting the electrochemical behavior of flexible SWCNTs-supercapacitors in different 1 molar aqueous electrolytes with different anions and cations. The experimental results also showed for flexible supercapacitor, it is suggested to put enough pressure between the two electrodes to improve the aqueous electrolyte CNT supercapacitor.^[51]

CNTs can store about the same charge as activated carbon per unit surface area, but nanotubes' surface is arranged in a regular pattern, providing greater wettability. SWNTs have a high theoretical specific surface area of 1315 m²/g, while that for MWNTs is lower and is determined by the diameter of the tubes and degree of nesting, compared with a surface area of about 3000 m²/g of activated carbons. Nevertheless, CNTs have higher capacitance than activated carbon electrodes, e.g., 102 F/g for MWNTs and 180 F/g for SWNTs.^[52]

MWNTs have mesopores that allow for easy access of ions at the electrode–electrolyte interface. As the pore size approaches the size of the ion solvation shell, the solvent molecules are partially stripped, resulting in larger ionic packing density and increased faradaic storage capability. However, the considerable volume change during repeated intercalation and depletion decreases their mechanical stability. To this end, research to increase surface area, mechanical strength, electrical conductivity and chemical stability is ongoing.^[49][53][54]

Electrodes for pseudocapacitors

Pseudocapacitance with faradaic charge transfer also is always present in carbon double-layer electrodes, but the amount of pseudocapacitance in EDLC electrodes is relatively low. Pseudocapacitance electrodes have surfaces able to achieve sufficient faradaic processes to have a majority of pseudocapacitance. Pseudocapacitance electrodes without double-layer capacitance do not exist.^[24]

Metal oxides

B. E. Conway's research^[7][8] described electrodes of transition metal oxides that exhibited high amounts of pseudocapacitance. Oxides of transition metals including ruthenium (RuO
2), iridium (IrO
2), iron (Fe
3O
4), manganese (MnO
2) or sulfides such as titanium sulfide (TiS
2) alone or in combination generate strong faradaic electron–transferring reactions combined with low resistance.^[55] Ruthenium dioxide in combination with H
2SO
4 electrolyte provides specific capacitance of 720 F/g and a high energy density of 26.7 Wh/kg (96.12 kJ/kg).^[56]

Charge/discharge takes place over a window of about 1.2 V per electrode. This pseudocapacitance of about 720 F/g is roughly 100 times higher than for double-layer capacitance using activated carbon electrodes. These transition metal electrodes offer excellent reversibility, with several hundred-thousand cycles. However, ruthenium is expensive and the 2.4 V voltage window for this capacitor limits their applications to military and space applications. Das et al. reported highest capacitance value (1715 F/g) for ruthenium oxide based supercapacitor with electrodeposited ruthenium oxide onto porous single wall carbon nanotube film electrode.^[57] A high specific capacitance of 1715 F/g has been reported which closely approaches the predicted theoretical maximum RuO
2 capacitance of 2000 F/g.

In 2014 a RuO
2 supercapacitor anchored on a graphene foam electrode delivered specific capacitance of 502.78 F/g and areal capacitance of 1.11 F/cm²) leading to an energy density of 39.28 Wh/kg and power density of 128.01 kW/kg over 8,000 cycles with constant performance. The device was a three-dimensional (3D) sub-5 nm hydrous ruthenium-anchored graphene and carbon nanotube (CNT) hybrid foam (RGM) architecture. The graphene foam was conformally covered with hybrid networks of RuO
2 nanoparticles and anchored CNTs.^[58][59]

Less expensive oxides of iron, vanadium, nickel and cobalt have been tested in aqueous electrolytes, but none has been investigated as much as manganese dioxide (MnO
2). However, none of these oxides are in commercial use.^[60]

Conductive polymers

Another approach uses electron-conducting polymers as pseudocapacitive material. Although mechanically weak, conductive polymers have high conductivity, resulting in a low ESR and a relatively high capacitance. Such conducting polymers include polyaniline, polythiophene, polypyrrole and polyacetylene. Such electrodes also employ electrochemical doping or dedoping of the polymers with anions and cations. Electrodes made from or coated with conductive polymers are cost comparable to carbon electrodes.

Conducting polymer electrodes generally suffer from limited cycling stability.^[61] However, polyacene electrodes provide up to 10,000 cycles, much better than batteries.^[62]

Electrodes for hybrid capacitors

All commercial hybrid supercapacitors are asymmetric. They combine an electrode with high amount of pseudocapacitance with an electrode with a high amount of double-layer capacitance. In such systems the faradaic pseudocapacitance electrode with their higher capacitance provides high energy density while the non-faradaic EDLC electrode enables high power density. An advantage of the hybride-type supercapacitors compared with symmetrical EDLC’s is their higher specific capacitance value as well as their higher rated voltage and correspondingly their higher specific energy.^[63]

Composite electrodes

Composite electrodes for hybrid-type supercapacitors are constructed from carbon-based material with incorporated or deposited pseudocapacitive active materials like metal oxides and conducting polymers. As of 2013 most research for supercapacitors explores composite electrodes.

CNTs give a backbone for a homogeneous distribution of metal oxide or electrically conducting polymers (ECPs), producing good pseudocapacitance and good double-layer capacitance. These electrodes achieve higher capacitances than either pure carbon or pure metal oxide or polymer-based electrodes. This is attributed to the accessibility of the nanotubes' tangled mat structure, which allows a uniform coating of pseudocapacitive materials and three-dimensional charge distribution. The process to anchor pseudocapacitve materials usually use hydrothermal process, however, recent researcher, Li et al., from University of Delaware found facile and scalable approach to precipitate MnO2 on SWNTs film to make organic-electrolyte based supercapacitor.^[64]

Another way to enhance CNT electrodes is by doping with a pseudocapacitive dopant as in lithium-ion capacitors. In this case the relatively small lithium atoms intercalate between the layers of carbon.^[65] The anode is made of lithium-doped carbon, which enables lower negative potential with a cathode made of activated carbon. This results in a larger voltage of 3.8-4 V that prevents electrolyte oxidation. As of 2007 they had achieved capacitance of 550 F/g.^[5] and reach an energy density up to 14 Wh/kg (50.4 kJ/kg).^[66]

Battery-type electrodes

Rechargeable battery electrodes influenced the development of electrodes for new hybrid-type supercapacitor electrodes as for lithium-ion capacitors.^[67] Together with an carbon EDLC electrode in an asymmetric construction offers this configuration higher energy density than typical supercapacitors with higher power density, longer cycle life and faster charging and recharging times than batteries.

Asymmetric electrodes (Pseudo/EDLC)

Recently some asymmetric hybrid supercapacitors were developed in which the positive electrode were based on a real pseudocapacitive metal oxide electrode (not a composite electrode), and the negative electrode on an EDLC activated carbon electrode.

An advantage of this type of supercapacitors is their higher voltage and correspondingly their higher specific energy (up to 10-20 Wh/kg (36-72 kJ/kg)).^[68]

As far as known no commercial offered supercapacitors with such kind of asymmetric electrodes are on the market.

Electrolytes

Electrolytes consist of a solvent and dissolved chemicals that dissociate into positive cations and negative anions, making the electrolyte electrically conductive. The more ions the electrolyte contains, the better its conductivity. In supercapacitors electrolytes are the electrically conductive connection between the two electrodes. Additionally, in supercapacitors the electrolyte provides the molecules for the separating monolayer in the Helmholtz double-layer and delivers the ions for pseudocapacitance.

The electrolyte determines the capacitor's characteristics: its operating voltage, temperature range, ESR and capacitance. With the same activated carbon electrode an aqueous electrolyte achieves capacitance values of 160 F/g, while an organic electrolyte achieves only 100 F/g.^[69]

The electrolyte must be chemically inert and not chemically attack the other materials in the capacitor to ensure long time stable behavior of the capacitor’s electrical parameters. The electrolyte's viscosity must be low enough to wet the porous, sponge-like structure of the electrodes. An ideal electrolyte does not exist, forcing a compromise between performance and other requirements.

Aqueous

Water is a relatively good solvent for inorganic chemicals. Treated with acids such as sulfuric acid (H
2SO
4), alkalis such as potassium hydroxide (KOH), or salts such as quaternary phosphonium salts, sodium perchlorate (NaClO
4), lithium perchlorate (LiClO
4) or lithium hexafluoride arsenate (LiAsF
6), water offers relatively high conductivity values of about 100 to 1000 mS/cm. Aqueous electrolytes have a dissociation voltage of 1.15 V per electrode (2,3 V capacitor voltage) and a relatively low operating temperature range. They are used in supercapacitors with low energy density and high power density.

Organic

Electrolytes with organic solvents such as acetonitrile, propylene carbonate, tetrahydrofuran, diethyl carbonate, γ-butyrolactone and solutions with quaternary ammonium salts or alkyl ammonium salts such as tetraethylammonium tetrafluoroborate (N(Et)
4BF
4^[70]) or triethyl (metyl) tetrafluoroborate (NMe(Et)
3BF
4) are more expensive than aqueous electrolytes, but they have a higher dissociation voltage of typically 1.35 V per electrode (2.7 V capacitor voltage), and a higher temperature range. The lower electrical conductivity of organic solvents (10 to 60 mS/cm) leads to a lower power density, but since the energy density increases with the square of the voltage, a higher energy density.

Separators

Separators have to physically separate the two electrodes to prevent a short circuit by direct contact. It can be very thin (a few hundredths of a millimeter) and must be very porous to the conducting ions to minimize ESR. Furthermore, separators must be chemically inert to protect the electrolyte's stability and conductivity. Inexpensive components use open capacitor papers. More sophisticated designs use nonwoven porous polymeric films like polyacrylonitrile or Kapton, woven glass fibers or porous woven ceramic fibres.^[71][72]

Collectors and housing

Current collectors connect the electrodes to the capacitor’s terminals. The collector is either sprayed onto the electrode or is a metal foil. They must be able to distribute peak currents of up to 100 A.

If the housing is made out of a metal (typically aluminum) the collectors should be made from the same material to avoid forming a corrosive galvanic cell.

Electrical parameters

Capacitance

Schematic illustration of the capacitance behavior resulting out of the porous structure of the electrodes

Equivalent circuit with cascaded RC elements

Frequency depending of the capacitance value of a 50 F supercapacitor

Capacitance values for commercial capacitors are specified as "rated capacitance C_R". This is the value for which the capacitor has been designed. The value for an actual component must be within the limits given by the specified tolerance. Typical values are in the range of farads (F), three to six orders of magnitude larger than those of electrolytic capacitors.

The capacitance value results from the energy W of a loaded capacitor loaded via a DC voltage V_DC.

$W=\frac{1}{2}\cdot C_\text{DC} \cdot V_\text{DC}^2$

This value is also called the "DC capacitance".

Measurement

Conventional capacitors are normally measured with a small AC voltage (0.5 V) and a frequency of 100 Hz or 1 kHz depending on the capacitor type. The AC capacitance measurement offers fast results, important for industrial production lines. The capacitance value of a supercapacitor depends strongly on the measurement frequency, which is related to the porous electrode structure and the limited electrolyte's ion mobility. Even at a low frequency of 10 Hz, the measured capacitance value drops from 100 to 20 percent of the DC capacitance value.

This extraordinary strong frequency dependence can be explained by the different distances the ions have to move in the electrode's pores. The area at the beginning of the pores can easily be accessed by the ions. The short distance is accompanied by low electrical resistance. The greater the distance the ions have to cover, the higher the resistance. This phenomenon can be described with a series circuit of cascaded RC (resistor/capacitor) elements with serial RC time constants. These result in delayed current flow, reducing the total electrode surface area that can be covered with ions if polarity changes – capacitance decreases with increasing AC frequency. Thus, the total capacitance is only achieved after longer measuring times.

Illustration of the measurement conditions for measuring the capacitance of supercapacitors

Out of the reason of the very strong frequency dependence of the capacitance this electrical parameter has to be measured with a special constant current charge and discharge measurement, defined in IEC standards 62391-1 and -2.

Measurement starts with charging the capacitor. The voltage has to be applied and after the constant current/constant voltage power supply has achieved the rated voltage, the capacitor has to be charged for 30 minutes. Next, the capacitor has to be discharged with a constant discharge current I_discharge. Then the time t₁ and t₂, for the voltage to drop from 80% (V₁) to 40% (V₂) of the rated voltage is measured. The capacitance value is calculated as:

$C_\text{total} = I_\text{discharge} \cdot \frac{t_2-t_1}{V_1-V_2}$

The value of the discharge current is determined by the application. The IEC standard defines four classes:

• Class 1, Memory backup, discharge current in mA = 1 • C (F)
• Class 2, Energy storage, discharge current in mA = 0,4 • C (F) • V (V)
• Class 3, Power, discharge current in mA = 4 • C (F) • V (V)
• Class 4, Instantaneous power, discharge current in mA = 40 • C (F) • V (V)

The measurement methods employed by individual manufacturers are mainly comparable to the standardized methods.^[73][74]

The standardized measuring method is too time consuming for manufacturers to use during production for each individual component. For industrial produced capacitors the capacitance value is instead measured with a faster low frequency AC voltage and a correlation factor is used to compute the rated capacitance.

This frequency dependence affects capacitor operation. Rapid charge and discharge cycles mean that neither the rated capacitance value nor energy density are available. In this case the rated capacitance value is recalculated for each application condition.

Operating voltage

A 5.5 volt supercapacitor is constructed out of two single cells, each rated to at least 2.75 volts, in series connection

Supercapacitors are low voltage components. Safe operation requires that the voltage remain within specified limits. The rated voltage U_R is the maximum DC voltage or peak pulse voltage that may be applied continuously and remain within the specified temperature range. Capacitors should never be subjected to voltages continuously in excess of the rated voltage.

The rated voltage includes a safety margin against the electrolyte's breakdown voltage at which the electrolyte decomposes. The breakdown voltage decomposes the separating solvent molecules in the Helmholtz double-layer, f. e. water splits into hydrogen and oxide. The solvent molecules then cannot separate the electrical charges from each other. Higher voltages than rated voltage cause hydrogen gas formation or a short circuit.

Standard supercapacitors with aqueous electrolyte normally are specified with a rated voltage of 2.1 to 2.3 V and capacitors with organic solvents with 2.5 to 2.7 V. Lithium-ion capacitors with doped electrodes may reach a rated voltage of 3.8 to 4 V, but have a lower voltage limit of about 2.2 V.

Operating supercapacitors below the rated voltage improves the long-time behavior of the electrical parameters. Capacitance values and internal resistance during cycling are more stable and lifetime and charge/discharge cycles may be extended.^[74]

Supercapacitors rated voltages are generally lower than applications require. Higher application voltages require connecting cells in series. Since each component has a slight difference in capacitance value and ESR, it is necessary to actively or passively balance them to stabilize the applied voltage. Passive balancing employs resistors in parallel with the supercapacitors. Active balancing may include electronic voltage management above a threshold that varies the current.

Internal resistance

The internal DC resistance can be calculated out of the voltage drop obtained from the intersection of the auxiliary line extended from the straight part and the time base at the time of discharge start

Charging/discharging a supercapacitor is connected to the movement of charge carriers (ions) in the electrolyte across the separator to the electrodes and into their porous structure. Losses occur during this movement that can be measured as the internal DC resistance.

With the electrical model of cascaded, series-connected RC (resistor/capacitor) elements in the electrode pores, the internal resistance increases with the increasing penetration depth of the charge carriers into the pores. The internal DC resistance is time dependent and increases during charge/discharge. In applications often only the switch-on and switch-off range is interesting. The internal resistance R_i can be calculated from the voltage drop ΔV₂ at the time of discharge, starting with a constant discharge current I_discharge. It is obtained from the intersection of the auxiliary line extended from the straight part and the time base at the time of discharge start (see picture right). Resistance can be calculated by:

$R_\text{i}= \frac{\Delta V_2}{I_\text{discharge}}$

The discharge current I_discharge for the measurement of internal resistance can be taken from the classification according to IEC 62391-1.

This internal DC resistance R_i should not be confused with the internal AC resistance called Equivalent Series Resistance (ESR) normally specified for capacitors. It is measured at 1 kHz. ESR is much smaller than DC resistance. ESR is not relevant for calculating superconductor inrush currents or other peak currents.

R_i determines several supercapacitor properties. It limits the charge and discharge peak currents as well as charge/discharge times. R_i and the capacitance C results in the time constant $\tau$

$\tau = R_\text{i} \cdot C$

This time constant determines the charge/discharge time. A 100 F capacitor with an internal resistance of 30 mΩ for example, has a time constant of 0.03 • 100 = 3 s. After 3 seconds charging with a current limited only by internal resistance, the capacitor has 63.2% of full charge (or is discharged to 36.8% of full charge).

Standard capacitors with constant internal resistance fully charge during about 5 τ. Since internal resistance increases with charge/discharge, actual times cannot be calculated with this formula. Thus, charge/discharge time depends on specific individual construction details.

Current load and cycle stability

Because supercapacitors operate without forming chemical bonds, current loads, including charge, discharge and peak currents are not limited by reaction constraints. Current load and cycle stability can be much higher than for rechargeable batteries. Current loads are limited only by internal resistance, which may be substantially lower than for batteries.

Internal resistance "R_i" and charge/discharge currents or peak currents "I" generate internal heat losses "P_loss" according to:

$P_\text{loss} = R_\text{i} \cdot I^2$

This heat must be released and distributed to the ambient environment to maintain operating temperatures below the specified maximum temperature.

Heat generally defines capacitor lifetime because of electrolyte diffusion. The heat generation coming from current loads should be smaller than 5 to 10 K at maximum ambient temperature (which has only minor influence on expected lifetime). For that reason the specified charge and discharge currents for frequent cycling are determined by internal resistance.

The specified cycle parameters under maximal conditions include charge and discharge current, pulse duration and frequency. They are specified for a defined temperature range and over the full voltage range for a defined lifetime. They can differ enormously depending on the combination of electrode porosity, pore size and electrolyte. Generally a lower current load increases capacitor life and increases the number of cycles. This can be achieved either by a lower voltage range or slower charging and discharging.^[74]

Supercapacitors (except those with polymer electrodes) can potentially support more than one million charge/discharge cycles without substantial capacity drops or internal resistance increases. Beneath the higher current load is this the second great advantage of supercapacitors over batteries. The stability results from the dual electrostatic and electrochemical storage principles.

The specified charge and discharge currents can be significantly exceeded by lowering the frequency or by single pulses. Heat generated by a single pulse may be spread over the time until the next pulse occurs to ensure a relatively small average heat increase. Such a "peak power current" for power applications for supercapacitors of more than 1000 F can provide a maximum peak current of about 1000 A.^[75] Such high currents generate high thermal stress and high electromagnetic forces that can damage the electrode-collector connection requiring robust design and construction of the capacitors.

Energy capacity

Ragone chart showing power density vs. energy density of various capacitors and batteries

Supercapacitors occupy the gap between high power/low energy electrolytic capacitors and low power/high energy rechargeable batteries. The energy W_max that can be stored in a capacitor is given by the formula

$W_\text{max}=\frac{1}{2}\cdot C_\text{total} \cdot V_\text{loaded}^2$

This formula describes the amount of energy stored and is often used to describe new research successes. However, only part of the stored energy is available to applications, because the voltage drop and the time constant over the internal resistance mean that some of the stored charge is inaccessible. The effective realized amount of energy W_eff is reduced by the used voltage difference between V_max and V_min and can be represented as:^[76]

$W_\text{eff}=\frac{1}{2}\ C \cdot\ ( V_\text{max}^2 - V_\text{min}^2 )$

This formula also represents the energy asymmetric voltage components such as lithium ion capacitors.

Energy density and power density

The amount of energy that can be stored in a capacitor per mass of that capacitor is called its specific energy. Specific energy is measured gravimetrically (per unit of mass) in watt-hours per kilogram (Wh/kg).

The amount of energy can be stored in a capacitor per volume of that capacitor is called its energy density. Energy density is measured volumetrically (per unit of volume) in watt-hours per litre (Wh/l).

As of 2013 commercial specific energies range from around 0.5 to 15 Wh/kg. For comparison, an aluminum electrolytic capacitor stores typically 0.01 to 0.3 Wh/kg, while a conventional lead-acid battery stores typically 30 to 40 Wh/kg and modern lithium-ion batteries 100 to 265 Wh/kg. Supercapacitors can therefore store 10 to 100 times more energy than electrolytic capacitors, but only one tenth as much as batteries. For reference, petrol fuel has an specific energy density of 44.4 MJ/kg or 12300 Wh/kg(in vehicle propulsion, the efficiency of energy conversions should be considered resulting in 3700 Wh/kg considering a typical 30% internal combustion engine efficiency).

Commercial volumetric energy densities vary widely but in general range from around 5 to 8 Wh/l. Units of liters and dm³ can be used interchangeably. In comparison, petrol fuel has a volumetric energy density of 32.4 MJ/l.

Although the energy densities of supercapacitors are insufficient compared with batteries, capacitors have the important advantage of the power density. Power density describes the speed at which energy can be delivered to/absorbed from the load. The maximum power is given by the formula:^[76]

$P_\text{max}=\frac{1}{4}\cdot\frac{V^2}{R_i}$

with V = voltage applied and R_i, the internal DC resistance of the capacitor.

Power density is measured either gravimetrically in kilowatts per kilogram (kW/kg) or volumetrically in kilowatts per litre (kW/l).

The described maximum power P_max specifies the power of a theoretical rectangular single maximum current peak of a given voltage. In real circuits the current peak is not rectangular and the voltage is smaller, caused by the voltage drop. IEC 62391–2 established a more realistic effective power P_eff for supercapacitors for power applications:

$P_\text{eff}=\frac{1}{8}\cdot\frac{V^2}{R_i}$

Supercapacitor power density is typically 10 to 100 times greater than for batteries and can reach values up to 15 kW/kg.

Ragone charts relate energy to power and are a valuable tool for characterizing and visualizing energy storage components. With such a diagram, the position of power density and energy density of different storage technologies is easily to compare, see diagram.^[77][78]

Lifetime

The lifetime of supercapacitors depends mainly on the capacitor temperature and the voltage applied

Supercapacitors exhibit a much longer lifetime than batteries. Since supercapacitors do not rely on chemical changes in the electrodes (except for those with polymer electrodes) lifetimes depend mostly on the rate of evaporation of the liquid electrolyte. This evaporation in general is a function of temperature, of current load, current cycle frequency and voltage. Current load and cycle frequency generate internal heat, so that the evaporation-determining temperature is the sum of ambient and internal heat. This temperature is measurable as core temperature in the center of a capacitor body. The higher the core temperature the faster the evaporation and the shorter the lifetime.

Evaporation generally results in decreasing capacitance and increasing internal resistance. According to IEC/EN 62391-2 capacitance reductions of over 30% or internal resistance exceeding four times its data sheet specifications are considered "wear-out failures", implying that the component has reached end-of-life. The capacitors are operable, but with reduced capabilities. Whether the aberration of the parameters have any influence on the proper functionality or not depends on the application of the capacitors.

Such large changes of electrical parameters specified in IEC/EN 62391-2 are usually unacceptable for high current load applications. Components that support high current loads use much smaller limits, e.g., 20% loss of capacitance or double the internal resistance.^[79] The narrower definition is important for such applications, since heat increases linearly with increasing internal resistance and the maximum temperature should not be exceeded. Temperatures higher than specified can destroy the capacitor.

The real application lifetime of supercapacitors, also called "service life", "life expectancy" or "load life", can reach 10 to 15 years or more at room temperature. Such long periods cannot be tested by manufacturers. Hence, they specify the expected capacitor lifetime at the maximum temperature and voltage conditions. The results are specified in datasheets using the notation "tested time (hours)/max. temperature (°C)", such as "5000 h/65 °C". With this value and expressions derived from historical data, lifetimes can be estimated for lower temperature conditions.

Datasheet lifetime specification is tested by the manufactures using an accelerated aging test called "endurance test" with maximum temperature and voltage over a specified time. For a "zero defect" product policy during this test no wear out or total failure may occur.

The lifetime specification from datasheets can be used to estimate the expected lifetime for a given design. The "10-degrees-rule" used for electrolytic capacitors with non-solid electrolyte is used in those estimations and can be used for supercapacitors. This rule employs the Arrhenius equation, a simple formula for the temperature dependence of reaction rates. For every 10 °C reduction in operating temperature, the estimated life doubles.

$L_x =L_0\cdot 2^\frac{T_0-T_x}{10}$

With

• L_x = estimated lifetime
• L₀ = specified lifetime
• T₀ = upper specified capacitor temperature
• T_x = actual operating temperature of the capacitor cell

Calculated with this formula, capacitors specified with 5000 h at 65 °C, have an estimated lifetime of 20,000 h at 45 °C.

Lifetimes are also dependent on the operating voltage, because the development of gas in the liquid electrolyte depends on the voltage. The lower the voltage the smaller the gas development and the longer the lifetime. No general formula relates voltage to lifetime. The voltage dependent curves shown from the picture are an empirical result from one manufacturer.

Life expectancy for power applications may be also limited by current load or number of cycles. This limitation has to be specified by the relevant manufacturer and is strongly type dependent.

Self-discharge

Storing electrical energy in the double-layer separates the charge carriers by distance within the pores by distances in the range of molecules. Over this short distance irregularities can occur, leading to a small exchange of charge carriers and gradual discharge. This self-discharge is called leakage current. Leakage depends on capacitance, voltage, temperature and the chemical stability of the electrode/electrolyte combination. At room temperature leakage is so low that it is specified as time to self-discharge. Supercapacitor self-discharge time is specified in hours, days or weeks. As an example, a 5.5 V/F Panasonic "Goldcapacitor" specifies a voltage drop at 20 °C from 5.5 V to 3 V in 600 hours (25 days or 3.6 weeks) for a double cell capacitor.^[80]

Polarity

A negative bar on the insulating sleeve indicates the cathode terminal of the capacitor

Since the anode and cathode of symmetric supercapacitors consist of the same material, theoretically supercapacitors have no true polarity and catastrophic failure does not normally occur. However reverse-charging a supercapacitor lowers its capacity, so it is recommended practice to maintain the polarity resulting from the formation of the electrodes during production. Asymmetric supercapacitors are inherently polar.

Supercapacitors may not be operated with reverse polarity, precluding their use in AC operation.

A bar in the insulating sleeve identifies the cathode terminal in a polarized component.

The terms "anode" and "cathode" can lead to confusion, because the polarity changes depending on whether a component is considered as a generator or as a consumer of current. For an accumulator or a battery the cathode has a positive polarity (+) and the anode has negative polarity (-). For capacitors the cathode has negative polarity (-) and the anode has positive polarity (+). This requires special attention if supercapacitors are substituted or used in parallel with batteries.

Comparison of technical parameters

The range of electrodes and electrolytes available yields a variety of components suitable for diverse applications. The development of low-ohmic electrolyte systems, in combination with electrodes with high pseudocapacitance, enable many more technical solutions.

The following table shows differences among capacitors of various manufacturers in capacitance range, cell voltage, internal resistance (ESR, DC or AC value) and volumetric and gravimetric energy density.

In the table, ESR refers to the component with the largest capacitance value of the respective manufacturer. Roughly, they divide supercapacitors into two groups. The first group offers greater ESR values of about 20 milliohms and relatively small capacitance of 0.1 to 470 F. These are "double-layer capacitors" for memory back-up or similar applications. The second group offers 100 to 10,000 F with a significantly lower ESR value under 1 milliohm. These components are suitable for power applications. A correlation of some supercapacitor series of different manufacturers to the various construction features is provided in Pandolfo and Hollenkamp.^[28]

Electrical parameter of supercapacitor series of different manufacturers (date: December 2015)

Manufacturer	Series name	Capacitance range (F)	Cell voltage (V)	Volumetric energy density (Wh/dm^3)	Gravimetric energy density (Wh/kg)	Remarks
APowerCap[81]	APowerCap	4…550	2.7	–	≤4.5	–
AVX[82]	BestCap®	0.05…0.56	3.6	≤0.13	–	Modules up to 20 V
Cap-XX[83]	Cap-XX	0.17…2.4	2.5	≤2.2	-	–
CDE[84]	Ultracapacitor	0.1…1.0	3.6	-	-	–
Cooper[85]	PowerStor	0.22…3000	2.5/2.7	¬	–	Modules up to 62 V
Elna[86]	DYNACAP POWERCAP	0.047…1500	2.5/3.6	-	–	–
Evans[87]	Capattery	0.001…10	5.5…125	–	–	Hybrid capacitors
FastCAP Systems[88]	EEx	340-460	1-3	≤10.5	–	–
Green Tech[89]	Super Capacitor	2…600	2.7/2.8	-	-	Modules up to 64 V
Illinois[90]	Supercapacitor	0.3800	2.3/2.7	≤8.6	≤6.6	–
Ioxus[91]	Ultracapacitor	100…3000	2.7	≤8.7	≤6.4	Modules up to 130 V
JSR Micro[92]	Ultimo	1100…3300	3.8	≤20	≤12	Li-Ion-capacitors
Korchip[93]	STARCAP	0.02…400	2.5/2.7	≤7.0	≤6.1	-
LS Mtron[94]	Ultracapacitor	100…3400	2.7/2.8	-	-	Modules up to 130 V
Maxwell[95]	Boostcap®	1…3400	2.2/2.8	-	≤6.0	Modules up to 160 V
Murata[96]	EDLC	0.22…1.0	4.2/5.5	≤2.7	≤3.1	2 cells in series
NEC Tokin[97]	Supercapacitor	0.047…200	2.7	–	–	–
Nesscap[98]	EDLC. Pseudocapacitor	3…50 50…300	2.7 2.3	≤7.1 ≤12.9	≤4.5 ≤8.7	Modules up to 125 V
Nichicon[99]	EVerCAP®	1.0…6000	2.5/2.7	-	-	-
NCC, ECC[100]	DLCCAP	350…2300	2.5	-	-	-
Panasonic[101]	Goldcap	0.1…70	2.3/2.5	-	-	Modules up to 15 V
Samwha[102]	Green-Cap® ESD-SCAP	3…7500	2.5/2.7	≤7.6	≤7.0	-
Skeleton[103]	SkelCap	250…4500	2.85	≤14.1	≤10.1	Modules up to 350 V
Taiyo Yuden[104]	PAS Capacitor LIC Capacitor	0.5…20 0.5…270	2.5/3.0 3.8	– –	– –	Pseudocapacitors Li-Ion-capacitors
VinaTech[105]	Hy-Cap	1.0…500	2.3/3.0	≤8.7	≤6.3	–
Vishay[106]	ENYCAP	4...15	1.4	-	-	Modules up to 8.4 V
WIMA[107]	SuperCap	100…3000	2.5	-	-	Modules up to 28 V
YEC[108]	Kapton capacitor	0.5…400	2.7	-	-	–
Yunasko[109]	Ultracapacitor	480…1700	2.7	-	-	Modules up to 48 V

Parametric comparison of technologies

Supercapacitors compete with electrolytic capacitors and rechargeable batteries especially lithium-ion batteries. The following table compares the major parameters of the three main supercapacitor families with electrolytic capacitors and batteries.

Parameters of supercapacitors compared with electrolytic capacitors and lithium-ion batteries

Parameter	Aluminum electrolytic capacitors	Supercapacitors			Lithium-ion batteries
		Double-layer capacitors for memory backup	Super-capacitors for power applications	Pseudo and Hybrid capacitors (Li-Ion capacitors)
Temperature range (°C)	−40 to 125	−20 to +70	−20 to +70	−20 to +70	−20 to +60
Cell voltage (V)	4 to 550	1.2 to 3.3	2.2 to 3.3	2.2 to 3.8	2.5 to 4.2
Charge/discharge cycles	unlimited	10^5 to 10^6	10^5 to 10^6	2 • 10^4 to 10^5	500 to 10^4
Capacitance range (F)	≤ 1	0.1 to 470	100 to 12000	300 to 3300	—
Energy density (Wh/kg)	0.01 to 0.3	1.5 to 3.9	4 to 9	10 to 15	100 to 265
Power density (kW/kg)	> 100	2 to 10	3 to 10	3 to 14	0.3 to 1.5
Self discharge time at room temperature	short (days)	middle (weeks)	middle (weeks)	long (month)	long (month)
Efficiency (%)	99	95	95	90	90
Life time at room temperature (years)	> 20	5 to 10	5 to 10	5 to 10	3 to 5

Electrolytic capacitors feature unlimited charge/discharge cycles, high dielectric strength (up to 550 V) and good frequency response as AC resistance in the lower frequency range. Supercapacitors can store 10 to 100 times more energy than electrolytic capacitors but they do not support AC applications.

With regards to rechargeable batteries supercapacitors feature higher peak currents, low cost per cycle, no danger of overcharging, good reversibility, non-corrosive electrolyte and low material toxicity, while batteries offer, lower purchase cost, stable voltage under discharge, but they require complex electronic control and switching equipment, with consequent energy loss and spark hazard given a short.

Standards

Classification of supercapacitors into classes regarding to IEC 62391-1, IEC 62567and BS EN 61881-3 standards

Supercapacitors vary sufficiently that they are rarely interchangeable, especially those with higher energy densities. Applications range from low to high peak currents, requiring standardized test protocols.^[110]

Test specifications and parameter requirements are specified in the generic specification

• IEC/EN 62391–1, Fixed electric double layer capacitors for use in electronic equipment.

The standard defines four application classes, according to discharge current levels:

• Class 1: Memory backup
• Class 2: Energy storage, mainly used for driving motors require a short time operation,
• Class 3: Power, higher power demand for a long time operation,
• Class 4: Instantaneous power, for applications that requires relatively high current units or peak currents ranging up to several hundreds of amperes even with a short operating time

Three further standards describe special applications:

• IEC 62391–2, Fixed electric double-layer capacitors for use in electronic equipment - Blank detail specification - Electric double-layer capacitors for power application
• IEC 62576, Electric double-layer capacitors for use in hybrid electric vehicles. Test methods for electrical characteristics
• BS/EN 61881-3, Railway applications. Rolling stock equipment. Capacitors for power electronics. Electric double-layer capacitors

Applications

Supercapacitors do not support AC applications.

Supercapacitors have advantages in applications where a large amount of power is needed for a relatively short time, where a very high number of charge/discharge cycles or a longer lifetime is required. Typical applications range from milliamp currents or milliwatts of power for up to a few minutes to several amps current or several hundred kilowatts power for much shorter periods.

The time t a supercapacitor can deliver a constant current I can be calculated as:

$t=\frac{C\cdot (U_\text{charge}-U_\text{min}) }{I}$

as the capacitor voltage decreases from U_charge down to U_min.

If the application needs a constant power P for a certain time t this can be calculated as:

$t=\frac{1}{2 P}\cdot C\cdot(U_\text{charge}^2-U_\text{min}^2).$

wherein also the capacitor voltage decreases from U_charge down to U_min.

General

Consumer electronics

In applications with fluctuating loads, such as laptop computers, PDA’s, GPS, portable media players, hand-held devices,^[111] and photovoltaic systems, supercapacitors can stabilize the power supply.

Supercapacitors deliver power for photographic flashes in digital cameras and for LED life flashlights that can be charged in, e.g., 90 seconds.^[112]

As of 2013, portable speakers powered by supercapacitors were offered to the market.^[113]

Tools

A cordless electric screwdriver with supercapacitors for energy storage has about half the run time of a comparable battery model, but can be fully charged in 90 seconds. It retains 85% of its charge after three months left idle.^[114]

Grid power buffer

A group of EVs and HEVs during their charging process draw very high current for a short duration of time which creates power pulsation on the grid.^[115] Power pulsation not only reduces the efficiency of the grid and cause voltage drop in the common coupling bus, but it can cause considerable frequency fluctuation in the entire system. To overcome this problem, supercapacitors can be implemented as an interface between the charging station and the grid to buffer the grid from the high pulse power drawn from the charging station.^[116][117]

Low-power equipment power buffer

Supercapacitors provide backup or emergency shutdown power to low-power equipment such as RAM, SRAM, micro-controllers and PC Cards. They are the sole power source for low energy applications such as automated meter reading (AMR)^[118] equipment or for event notification in industrial electronics.

Supercapacitors buffer power to and from rechargeable batteries, mitigating the effects of short power interruptions and high current peaks. Batteries kick in only during extended interruptions, e.g., if the mains power or a fuel cell fails, which lengthens battery life.

Uninterruptible power supplies (UPS), where supercapacitors have replaced much larger banks of electrolytic capacitors. This combination reduces the cost per cycle, saves on replacement and maintenance costs, enables the battery to be downsized and extends battery life.^{[119][120][121]} A disadvantage is the need for a special circuit to reconcile the differing behaviors.

Rotor with wind turbine pitch system

Supercapacitors provide backup power for actuators in wind turbine pitch systems, so that blade pitch can be adjusted even if the main supply fails.^[122]

Voltage stabilizer

Supercapacitors can stabilize voltage for powerlines. Wind and photovoltaic systems exhibit fluctuating supply evoked by gusting or clouds that supercapacitors can buffer within milliseconds. This helps stabilize grid voltage and frequency, balance supply and demand of power and manage real or reactive power.^{[123][124][125]}

Energy harvesting

Supercapacitors are suitable temporary energy storage devices for energy harvesting systems. In energy harvesting systems the energy is collected from the ambient or renewable sources, e.g. mechanical movement, light or electromagnetic fields, and converted to electrical energy in an energy storage device. For example, it was demonstrated that energy collected from RF (radio frequency) fields (using an RF antenna as an appropriate rectifier circuit) can be stored to a printed supercapacitor. The harvested energy was then used to power an application-specific integrated circuit (ASIC) circuit for over 10 hours.^[126]

Incorporation into batteries

The UltraBattery is a hybrid rechargeable lead-acid battery and a supercapacitor invented by Australia’s national science organisation CSIRO. Its cell construction contains a standard lead-acid battery positive electrode, standard sulphuric acid electrolyte and a specially prepared negative carbon-based electrode that store electrical energy with double-layer capacitance. The presence of the supercapacitor electrode alters the chemistry of the battery and affords it significant protection from sulfation in high rate partial state if charge use, which is the typical failure mode of valve regulated lead-acid cells used this way. The resulting cell performs with characteristics beyond either a lead-acid cell or a supercapacitor, with charge and discharge rates, cycle life, efficiency and performance all enhanced. UltraBattery has been installed in kW and MW scale applications in Australia, Japan and the U.S.A. in frequency regulation, solar smoothing and shifting, wind smoothing and other applications.^[127]

Street lights

Street light combining a solar cell power source with LED lamps and supercapacitors for energy storage

Sado City, in Japan's Niigata Prefecture, has street lights that combine a stand-alone power source with solar cells and LEDs. Supercapacitors store the solar energy and supply 2 LED lamps, providing 15 W power consumption overnight. The supercapacitors can last more than 10 years and offer stable performance under various weather conditions, including temperatures from +40 to below -20 °C.^[128]

Medical

Supercapacitors are used in defibrillators where they can deliver 500 joules to shock the heart back into sinus rhythm.^[129]

Transport

Aviation

In 2005, aerospace systems and controls company Diehl Luftfahrt Elektronik GmbH chose supercapacitors to power emergency actuators for doors and evacuation slides used in airliners, including the Airbus 380.^[122]

Military

Supercapacitors' low internal resistance supports applications that require short-term high currents. Among the earliest uses were motor startup (cold engine starts, particularly with diesels) for large engines in tanks and submarines.^[130] Supercapacitors buffer the battery, handling short current peaks, reducing cycling and extending battery life.

Further military applications that require high power density are phased array radar antennae, laser power supplies, military radio communications, avionics displays and instrumentation, backup power for airbag deployment and GPS-guided missiles and projectiles.^[131][132]

Automotive

Toyota's Yaris Hybrid-R concept car uses a supercapacitor to provide bursts of power. PSA Peugeot Citroën has started using supercapacitors as part of its stop-start fuel-saving system, which permits faster initial acceleration.^[133]

Bus/tram

Maxwell Technologies, an American supercapacitor-maker, claimed that more than 20,000 hybrid buses use the devices to increase acceleration, particularly in China. Guangzhou, In 2014 China began using trams powered with supercapacitors that are recharged in 30 seconds by a device positioned between the rails, storing power to run the tram for up to 4 km — more than enough to reach the next stop, where the cycle can be repeated.^[133]

Energy recovery

A primary challenge of all transport is reducing energy consumption and reducing CO
2 emissions. Recovery of braking energy (recuperation or regeneration) helps with both. This requires components that can quickly store and release energy over long times with a high cycle rate. Supercapacitors fulfill these requirements and are therefore used in a lot of applications in all kinds of transportation.

Railway

Green Cargo operates TRAXX locomotives from Bombardier Transportation

Supercapacitors can be used to supplement batteries in starter systems in diesel railroad locomotives with diesel-electric transmission. The capacitors capture the braking energy of a full stop and deliver the peak current for starting the diesel engine and acceleration of the train and ensures the stabilization of catenary voltage. Depending on the driving mode up to 30% energy saving is possible by recovery of braking energy. Low maintenance and environmentally friendly materials encouraged the choice of supercapacitors.^[134][135]

Cranes, forklifts and tractors

Container Yard with Rubber Tyre Gantry Crane

Mobile hybrid diesel-electric rubber tyred gantry cranes move and stack containers within a terminal. Lifting the boxes requires large amounts of energy. Some of the energy could be recaptured while lowering the load resulting in improved efficiency.^[136]

A triple hybrid forklift truck uses fuel cells and batteries as primary energy storage and supercapacitors to buffer power peaks by storing braking energy. They provide the fork lift with peak power over 30 kW. The triple-hybrid system offers over 50% energy savings compared with diesel or fuel-cell systems.^[137]

Supercapacitor-powered terminal tractors transport containers to warehouses. They provide an economical, quiet and pollution-free alternative to diesel terminal tractors.^[138]

Light-rails and trams

Supercapacitors make it possible not only to reduce energy but to replace catenary overhead lines in historical city areas, so preserving the city’s architectural heritage. This approach may allow many new LRV city lines to replace overhead wires that are too expensive to fully route.

Light rail vehicle in Mannheim

In 2003 Mannheim adopted a prototype light-rail vehicle (LRV) using the MITRAC Energy Saver system from Bombardier Transportation to store mechanical braking energy with a roof-mounted supercapacitor unit.^[139][140] It contains several units each made of 192 capacitors with 2700 F /2.7 V interconnected in three parallel lines. This circuit results in a 518 V system with an energy content of 1.5 kWh. For acceleration when starting this "on-board-system" can provided the LRV with 600 kW and can drive the vehicle up to 1 km without catenary supply integrating the LRV into the urban environment by driving without catenary lines. Compared to conventional LRVs or Metro vehicles that return energy into the grid, onboard energy storage saves up to 30% and reduces peak grid demand by up to 50%.^[141]

Supercapacitors are used to power the Paris T3 tram line on sections without catenary overhead wires and to recover energy during braking.

In 2009 supercapacitors enabled LRV's to operate in the historical city area of Heidelberg without catenary overhead wires preserving the city’s architectural heritage. The SC equipment cost an additional €270,000 per vehicle, which was expected to be recovered over the first 15 years of operation. The supercapacitors are charged at stop-over stations when the vehicle is at a scheduled stop. This approach may allow many LRV city lines to serve catenary overhead wires that are too expensive to fully route installation. In April 2011 German regional transport operator Rhein-Neckar, responsible for Heidelberg, ordered a further 11 units.^[142]

In 2009 in Paris a tram on route T3 operates with an energy recovery system of the manufacturer Alstom called "STEEM".^[143] The system is fitted with 48 roof-mounted supercapacitors to store braking energy provides tramways with a high level of energy autonomy by enabling them to run without catenary power on parts of its route, recharging while traveling on powered stop-over stations. During the tests, the tramset used an average of approximately 16% less energy.^[144]

Light rail vehicle in Hong Kong

In 2012 tram operator Geneva Public Transport began tests of an LRV equipped with a prototype roof-mounted supercapacitor unit to recover braking energy.^[145]

Siemens is delivering supercapacitor-enhanced light-rail transport systems that include mobile storage.^[146]

Hong Kong's South Island metro line is to be equipped with two 2 MW energy storage units that are expected to reduce energy consumption by 10%.^[147]

In August 2012 the CSR Zhuzhou Electric Locomotive corporation of China presented a prototype two-car light metro train equipped with a roof-mounted supercapacitor unit. The train can travel up 2 km without wires, recharging in 30 seconds at stations via a ground mounted pickup. The supplier claimed the trains could be used in 100 small and medium-sized Chinese cities.^[148]

In 2012, in Lyon (France), the SYTRAL (Lyon public transportation administration) started experiments of a "way side regeneration" system built by Adetel Group which has developed its own energy saver named ″NeoGreen″ for LRV, LRT and metros.^[149]

Seven trams (street cars) powered by supercapacitors were scheduled to go into operation in 2014 in Guangzhou, China. The supercapacitors are recharged in 30 seconds by a device positioned between the rails. That powers the tram for up to 4 kilometres (2.5 mi).^[150]

Buses

MAN Ultracapbus in Nuremberg, Germany

The first hybrid bus with supercapacitors in Europe came in 2001 in Nuremberg, Germany. It was MAN's so-called "Ultracapbus", and was tested in real operation in 2001/2002. The test vehicle was equipped with a diesel-electric drive in combination with supercapacitors. The system was supplied with 8 Ultracap modules of 80 V, each containing 36 components. The system worked with 640 V and could be charged/discharged at 400 A. Its energy content was 0.4 kWh with a weight of 400 kg.

The supercapacitors recaptured braking energy and delivered starting energy. Fuel consumption was reduced by 10 to 15% compared to conventional diesel vehicles. Other advantages included reduction of CO
2 emissions, quiet and emissions-free engine starts, lower vibration and reduced maintenance costs.^[151][152]

Electric bus at EXPO 2010 in Shanghai (Capabus) recharging at the bus stop

As of 2002 in Luzern, Switzerland an electric bus fleet called TOHYCO-Rider was tested. The supercapacitors could be recharged via an inductive contactless high-speed power charger after every transportation cycle, within 3 to 4 minutes.^[153][154]

In early 2005 Shanghai tested a new form of electric bus called capabus that runs without powerlines (catenary free operation) using large onboard supercapacitors that partially recharge whenever the bus is at a stop (under so-called electric umbrellas), and fully charge in the terminus. In 2006, two commercial bus routes began to use the capabuses; one of them is route 11 in Shanghai. It was estimated that the supercapacitor bus was cheaper than a lithium-ion battery bus, and one of its buses had one-tenth the energy cost of a diesel bus with lifetime fuel savings of $200,000.^[155]

A hybrid electric bus called tribrid was unveiled in 2008 by the University of Glamorgan, Wales, for use as student transport. It is powered by hydrogen fuel or solar cells, batteries and ultracapacitors.^[156][157]

Motor racing

World champion Sebastian Vettel in Malaysia 2010

Toyota TS030 Hybrid at 2012 24 Hours of Le Mans motor race

The FIA, a governing body for motor racing events, proposed in the Power-Train Regulation Framework for Formula 1 version 1.3 of 23 May 2007 that a new set of power train regulations be issued that includes a hybrid drive of up to 200 kW input and output power using "superbatteries" made with batteries and supercapacitors connected in parallel (KERS).^[158][159] About 20% tank-to-wheel efficiency could be reached using the KERS system.

The Toyota TS030 Hybrid LMP1 car, a racing car developed under Le Mans Prototype rules, uses a hybrid drivetrain with supercapacitors.^[160][161] In the 2012 24 Hours of Le Mans race a TS030 qualified with a fastest lap only 1.055 seconds slower (3:24.842 versus 3:23.787)^[162] than the fastest car, an Audi R18 e-tron quattro with flywheel energy storage. The supercapacitor and flywheel components, whose rapid charge-discharge capabilities help in both braking and acceleration, made the Audi and Toyota hybrids the fastest cars in the race. In the 2012 Le Mans race the two competing TS030s, one of which was in the lead for part of the race, both retired for reasons unrelated to the supercapacitors. The TS030 won three of the 8 races in the 2012 FIA World Endurance Championship season. In 2014 the Toyota TS040 Hybrid used a supercapacitor to add 480 horsepower from two electric motors.^[150]

Hybrid electric vehicles

Mazda2 (since 2010)

Supercapacitor/battery combinations in electric vehicles (EV) and hybrid electric vehicles (HEV) are well investigated.^{[110][163][164]} A 20 to 60% fuel reduction has been claimed by recovering brake energy in EVs or HEVs. The ability of supercapacitors to charge much faster than batteries, their stable electrical properties, broader temperature range and longer lifetime are suitable, but weight, volume and especially cost mitigate those advantages.

Supercapacitors lower energy density makes them unsuitable for use as a stand-alone energy source for long distance driving.^[165] The fuel economy improvement between a capacitor and a battery solution is about 20% and is available only for shorter trips. For long distance driving the advantage decreases to 6%. Vehicles combining capacitors and batteries run only in experimental vehicles.^[166]

As of 2013 all automotive manufacturers of EV or HEVs have developed prototypes that uses supercapacitors instead of batteries to store braking energy in order to improve driveline efficiency. The Mazda 6 is the only production car that uses supercapacitors to recover braking energy. Branded as i-eloop, the regenerative braking is claimed to reduce fuel consumption by about 10%.^[167]

Russian Yo-cars Ё-mobile series was a concept and crossover hybrid vehicle working with a gas driven Wankel motor and an electric generator for driving. A supercapacitor with relatively low capacitance recovers brake energy to power the electric motor when accelerating from a stop.^[168]

Toyota's Yaris Hybrid-R concept car uses a supercapacitor to provide quick bursts of power.^[150]

PSA Peugeot Citroën fit supercapacitors to some of its cars as part of its stop-start fuel-saving system, as this permits faster start-ups when the traffic lights turn green.^[150]

Gondolas

Aerial lift in Zell am See, Austria

In Zell am See, Austria, an aerial lift connects the city with Schmittenhöhe mountain. The gondolas sometimes run 24 hours per day, using electricity for lights, door opening and communication. The only available time for recharging batteries at the stations is during the brief intervals of guest loading and unloading, which is too short to recharge batteries. Supercapacitors offer a fast charge, higher number of cycles and longer life time than batteries.

Emirates Air Line (cable car), also known as the Thames cable car, is a 1-kilometre (0.62 mi) gondola line that crosses the Thames from the Greenwich Peninsula to the Royal Docks. The cabins are equipped with a modern infotainment system, which is powered by supercapacitors.^[169][170]

Developments

As of 2013 commercially available lithium-ion supercapacitors offered the highest gravimetric energy density to date, reaching 15 Wh/kg (54 kJ/kg). Research focuses on improving energy density, reducing internal resistance, expanding temperature range, increasing lifetimes and reducing costs.^[17] Projects include tailored-pore-size electrodes, pseudocapacitive coating or doping materials and improved electrolytes.

Announcements

Development	Date	Energy density^[A]	Power density	Cycles	Capacitance	Notes
Graphene sheets compressed by capillary compression of a volatile liquid[171]	2013	60 Wh/l				Subnanometer scale electrolyte integration created a continuous ion transport network.
Vertically aligned carbon nanotubes electrodes[5][50]	2007 2009 2013	13.50 Wh/kg	37.12 W/g	300,000		First realization[172]
Curved graphene sheets[45][46]	2010	85.6 Wh/kg			550 F/g	Single-layers of curved graphene sheets that do not restack face-to-face, forming mesopores that are accessible to and wettable by environmentally friendly ionic electrolytes at a voltage up to 4 V.
KOH restructured graphite oxide[173][174]	2011	85 Wh/kg		>10,000	200 F/g	Potassium hydroxide restructured the carbon to make a three dimensional porous network
Activated graphene-based carbons as supercapacitor electrodes with macro- and mesopores[175]	2013	74 Wh/kg				Three-dimensional pore structures in graphene-derived carbons in which mesopores are integrated into macroporous scaffolds with a surface area of 3290 m^2/g
Conjugated microporous polymer[176][177]	2011	53 Wh/kg		10,000		Aza-fused π-conjugated microporous framework
SWNT composite electrode[178]	2011		990 W/kg			A tailored meso-macro pore structure held more electrolyte, ensuring facile ion transport
Nickel hydroxide nanoflake on CNT composite electrode[179]	2012	50.6 Wh/kg			3300 F/g	Asymmetric supercapacitor using the Ni(OH)2/CNT/NF electrode as the anode assembled with an activated carbon (AC) cathode achieving a cell voltage of 1.8 V
Battery-electrode nanohybrid[67]	2012	40 Wh/l	7.5 W/l	10,000		Li 4Ti 5O 12 (LTO) deposited on carbon nanofibres (CNF) anode and an activated carbon cathode
Nickel cobaltite deposited on mesoporous carbon aerogel[180]	2012	53 Wh/kg	2.25 W/kg		1700 F/g	Nickel cobaltite, a low cost and an environmentally friendly supercapacitive material
Manganese dioxide intercalated nanoflakes[181]	2013	110 Wh/kg			1000 F/g	Wet electrochemical process intercalated Na(+) ions into MnO 2 interlayers. The nanoflake electrodes exhibit faster ionic diffusion with enhanced redox peaks.
3D porous graphene electrode[182]	2013	98 Wh/kg			231 F/g	Wrinkled single layer graphene sheets a few nanometers in size, with at least some covalent bonds.
Graphene-based planar micro-supercapacitors for on-chip energy storage[183]	2013	2.42 Wh/l				On chip line filtering
Nanosheet capacitors[184][185]	2014				27.5 μF cm^−2	Electrodes: Ru0.95O2^0.2– Dielectric: Ca2Nb3O10^–. Room-temperature solution-based manufacturing processes. Total thickness less than 30 nm.
LSG/manganese dioxide[186]	2015	42 Wh/l	10 kW/l	10,000		Three-dimensional laser-scribed graphene (LSG) structure for conductivity, porosity and surface area. Electrodes are around15 microns thick.
Laser-induced graphene/solid-state electrolyte[187][188]	2015		0.02 mA/cm2		9 mF/cm2	Survives repeated flexing.

^A Research into electrode materials requires measurement of individual components, such as an electrode or half-cell.^[189] By using a counterelectrode that does not affect the measurements, the characteristics of only the electrode of interest can be revealed. Energy and power densities for real supercapacitors only have more or less roughly 1/3 of the electrode density.

Market

As of 2010 worldwide sales of supercapacitors reached US$400 million.^[190]

The market for batteries (estimated by Frost & Sullivan) grew from US$47.5 billion, (76.4% or US$36.3 billion of which was rechargeable batteries) to US$95 billion.^[191] The market for supercapacitors is still a small niche market that is not keeping pace with its larger rival.

In 2012, NanoMarkets forecast sales to grow to US$3.5 billion by 2020, an increase of about 900% within 10 years.^[192] Assumptions underlying this growth include a rapidly improving price/performance ratio and evolving "green energy" applications, such as energy recovery in electric vehicles. Otherwise the market was forecast to grow about 30% overall between 2013 and 2018 and remain in the hundreds of millions of dollars. Market Specially in Asia region is expected to get intense with many new manufactures of Supercapacitors coming up in China and Korea. India is also establishing its presence in Supercapacitor manufacturing.^[193]

Supercapacitor costs in 2006 were US$0.01 per farad or US$2.85 per kilojoule, moving in 2008 below US$0.01 per farad, and were expected to drop further in the medium term.^[194]

See also

• Electric vehicle battery
• Types of capacitors
• Nanoflower
• Rechargeable electricity storage system
• Flywheel energy storage
• List of emerging technologies
• Lithium ion capacitor
• Self-powered equipment
• Mechanically powered flashlight
• Conjugated microporous polymer
• Capa vehicle, including capabus

Literature

• Abruña, H. D.; Kiya, Y.; Henderson, J. C. (2008). "Batteries and Electrochemical Capacitors" (PDF). Phys. Today (12): 43–47.
• Bockris, J. O'M.; Devanathan, M. A. V.; Muller, K. (1963). "On the Structure of Charged Interfaces". P. Roy. Soc. Lond. A Mat. 274: 55–79. doi:10.1098/rspa.1963.0114.
• Béguin, F.; Raymundo-Piñeiro, E.; Frackowiak, E. (2009). "8. Electrical Double-Layer Capacitors and Pseudocapacitors". Carbons for Electrochemical Energy Storage and Conversion Systems. CRC Press. pp. 329–375. doi:10.1201/9781420055405-c8. ISBN 978-1-4200-5540-5.
• Conway, B. E. (1999). Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications. Springer. doi:10.1007/978-1-4757-3058-6. ISBN 0306457369.
• Zhang, J.; Zhang, L.; Liu, H.; Sun, A.; Liu, R.-S. (2011). "8. Electrochemical Supercapacitors". Electrochemical Technologies for Energy Storage and Conversion. Weinheim: Wiley-VCH. pp. 317–382. ISBN 978-3-527-32869-7.
• Leitner, K. W.; Winter, M.; Besenhard, J. O. (2003). "Composite Supercapacitor Electrodes". J. Solid State Electr. 8 (1): 15–16. doi:10.1007/s10008-003-0412-x.
• Ebrahimi (Editor), F. (September 27, 2012). Nanocomposites - New Trends and Developments. InTech. doi:10.5772/3389. ISBN 978-953-51-0762-0.
• Kinoshita, K. (January 18, 1988). Carbon: Electrochemical and Physicochemical Properties. John Wiley & Sons. ISBN 978-0-471-84802-8.
• Vol'fkovich, Y. M.; Serdyuk, T. M. (2002). "Electrochemical Capacitors". Russ. J. Electrochem. 38 (9): 935–959. doi:10.1023/A:1020220425954.
• Palaniselvam, Thangavelu; Baek, Jong-Beom (2015). "Graphene based 2D-materials for supercapacitors". 2D Materials 2: 032002. doi:10.1088/2053-1583/2/3/032002.
• Ploehn, Harry (2015). "Composite for energy storage takes the heat". Nature 523: 536–537. doi:10.1038/523536a.
• Li, Qui (2015). "Flexible high-temperature dielectric materials from polymer nanocomposites". Nature 523: 576–579. doi:10.1038/nature14647.

References

1. US 2800616, Becker, H.I., "Low voltage electrolytic capacitor", issued 1957-07-23 
2. Ho, J.; Jow, R.; Boggs, S. (Jan 2010). "Historical Introduction to Capacitor Technology" (PDF). IEEE Elect. Insul. Mag. (IEEE) 26 (1): 20–25. doi:10.1109/mei.2010.5383924.
3. A brief history of supercapacitors AUTUMN 2007 Batteries & Energy Storage Technology
4. US 3288641, Rightmire, Robert A., "Electrical energy storage apparatus", issued 1966-11-29 
5. J. G. Schindall, The Change of the Ultra-Capacitors, IEEE Spectrum, November 2007 The Charge of the Ultra – Capacitors
6. US 3536963, "Electrolytic capacitor having carbon paste electrodes", issued 1970-10-27 
7. Conway, B. E. (1999). Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications. Berlin: Springer. pp. 1–8. ISBN 978-1-4757-3058-6.
8. B. E. Conway (May 1991). "Transition from ‘Supercapacitor’ to ‘Battery’ Behavior in Electrochemical Energy Storage". J. Electrochem. Soc. 138 (6): 1539–1548. doi:10.1149/1.2085829.
9. Panasonic, Electric Double Layer Capacitor , Technical guide,1. Introduction,Panasonic Goldcaps
10. "Electric double-layer capacitors". ELNA. Retrieved 2015-02-21.
11. Adam Marcus Namisnyk. A survey of electrochemical supercapacitor technology (PDF) (Technical report). Retrieved 2015-02-21.
12. US 5369547, David A. Evans, "Containers with anodes and cathodes with electrolytes", issued 1994-11-29 
13. David A. Evans (Evans Company): High Energy Density Electrolytic-Electrochemical Hybrid Capacitor In: Proceedings of the 14th Capacitor & Resistor Technology Symposium. 22 March 1994
14. Evans Capacitor Company 2007 Capattery series
15. David A. Evans: The Littlest Big Capacitor - an Evans Hybrid Technical Paper, Evans Capacitor Company 2007
16. "FDK, Corporate Information, FDK History 2000s". FDK. Retrieved 2015-02-21.
17. Naoi, K.; Simon, P. (Spring 2008). "New Materials and New Configurations for Advanced Electrochemical Capacitors" (PDF). Interface (ECS) 17 (1): 34–37.
18. Frackowiak, E.; Béguin, F. (May 2001). "Carbon materials for the electrochemical storage of energy in capacitors". Carbon (Pergamon) 39 (6): 937–950. doi:10.1016/S0008-6223(00)00183-4.
19. Halper, Marin S.; Ellenbogen, James C. (March 2006). "Supercapacitors: A Brief Overview" (PDF). MITRE Nanosystems Group. Retrieved 2015-02-16.
20. "The electrical double layer". 2011. Retrieved 2014-01-20.
21. Srinivasan, S. (2006). "2. Electrode/Electrolyte Interfaces: Structure and Kinetics of Charge Transfer". Fuel Cells: From Fundamentals to Applications. Springer eBooks. ISBN 978-0-387-35402-6.
22. Despotuli, A.L.; Andreeva, A.V. (February 2011). "Advanced Carbon Nanostructures" for "Advanced Supercapacitors:" What Does it Mean?". Nanoscience and Nanotechnology Lett. 3 (1): 119–124. doi:10.1166/nnl.2011.1130.
23. Yu, G.L.; Jalil, R.; Belle, B.; Mayorov, A.S.; Blake, P.; Schedin, F.; Morozov, S.V.; Ponomarenko, L.A.; Chiappini, F.; Wiedmann, S.; Zeitler, U.; Katsnelson, M.I.; Geim, A.K.; Novoselov, K.S.; Elias, D.C. (February 2013). "Interaction phenomena in graphene seen through quantum capacitance". PNAS 110 (9): 3282–3286. doi:10.1073/pnas.1300599110.
24. Conway, B. E. "ELECTROCHEMICAL CAPACITORS: Their Nature, Function, and Applications". Electrochemistry Encyclopedia. Archived from the original on December 4, 2004. Retrieved 2015-02-23.
25. Frackowiak, E.; Jurewicz, K.; Delpeux, K.; Béguin, F. (July 2001). "Nanotubular Materials For Supercapacitors". J. Power Sources. 97-98: 822–825. doi:10.1016/S0378-7753(01)00736-4.
26. Garthwaite, Josie (12 July 2011). "How ultracapacitors work (and why they fall short)". Earth2Tech. GigaOM Network. Retrieved 2015-02-23.
27. "Could hemp nanosheets topple graphene for better supercapacitor electrodes?". Kurzweil Accelerating Intelligence. August 14, 2014. Retrieved 2015-02-28.
28. Pandolfo, A.G.; Hollenkamp, A.F. (June 2006). "Carbon properties and their role in supercapacitors". J. Power Sources 157 (1): 11–27. doi:10.1016/j.jpowsour.2006.02.065.
29. Kim Kinoshita (June 1992). Electrochemical Oxygen Technology. Wiley. ISBN 978-0-471-57043-1.
30. "EnterosorbU, FAQ". Carbon-Ukraine.
31. US 6787235, Nesbitt, C.C. & Sun, X., "Consolidated amorphous carbon materials, their manufacture and use", issued 2004-09-07, assigned to Reticle, Inc. 
32. Laine, J.; Yunes, S. (1992). "Effect of the preparation method on the pore size distribution of activated carbon from coconut shell". Carbon 30 (4): 601–604. doi:10.1016/0008-6223(92)90178-Y.
33. Fischer, U.; Saliger, R.; Bock, V.; Petricevic, R.; Fricke, J. (October 1997). "Carbon aerogels as electrode material in supercapacitors". J. Porous Mat. 4 (4): 281–285. doi:10.1023/A:1009629423578.
34. Lerner, E.J. (October 2004). "Less is more with aerogels: A laboratory curiosity develops practical uses" (PDF). The Industrial Physicist (American Institute of Physics). pp. 26–30. Retrieved 2015-02-28.
35. LaClair, M. (Feb 1, 2003). "Replacing energy storage with carbon aerogel supercapacitors". Power Electronics (Penton). Retrieved 2015-02-28.
36. Chien, Hsing-Chi; Cheng, Wei-Yun; Wang, Yong-Hui; Lu, Shih-Yuan (2012-12-05). "Ultrahigh Specific Capacitances for Supercapacitors Achieved by Nickel Cobaltite/Carbon Aerogel Composites". Advanced Functional Materials 22 (23): 5038–5043. doi:10.1002/adfm.201201176. ISSN 1616-3028.
37. Presser, V.; Heon, M.; Gogotsi, Y. (March 2011). "Carbide-derived carbons – From porous networks to nanotubes and graphene". Adv. Funct. Mater. 21 (5): 810–833. doi:10.1002/adfm.201002094.
38. Korenblit, Y.; Rose, M.; Kockrick, E.; Borchardt, L.; Kvit, A.; Kaskel, S.; Yushin, G. (February 2010). "High-rate electrochemical capacitors based on ordered mesoporous silicon carbide-derived carbon" (PDF). ACS Nano 4 (3): 1337–1344. doi:10.1021/nn901825y.
39. "SkelCap High Energy Ultracapacitors - Data Sheet" (PDF). Skeleton Technologies. Retrieved 2015-02-28.
40. Yoo, J.J.; Balakrishnan, K.; Huang, J.; Meunier, V.; Sumpter, B.G.; Srivastava, A.; Conway, M.; Reddy, A.L.M.; Yu, J.; Vajtai, R.; Ajayan, P.M. (March 2011). "Ultrathin planar graphene supercapacitors". Nano Lett. 11 (4): 1423–1427. doi:10.1021/nl200225j.
41. Palaniselvam, Thangavelu; Baek, Jong-Beom (2015). "Graphene based 2D-materials for supercapacitors". 2D Materials 2: 032002. doi:10.1088/2053-1583/2/3/032002.
42. Pushparaj, V.L.; Shaijumon, M.M.; Kumar, A.; Murugesan, S.; Ci, L.; Vajtai, R.; Linhardt, R.J.; Nalamasu, O.; Ajayan, P.M. (August 2007). "Flexible energy storage devices based on nanocomposite paper". Proc. Natl. Acad. Sci. USA 104 (34): 13574–13577. doi:10.1073/pnas.0706508104. PMC 1959422. PMID 17699622.
43. Marcus, J. (March 15, 2012). "Researchers develop graphene supercapacitor holding promise for portable electronics". PhysOrg (Science X network). Retrieved 2015-02-28.
44. El-Kady, M.F.; Strong, V.; Dubin, S.; Kaner, R.B. (March 2012). "Laser scribing of high-performance and flexible graphene-based electrochemical capacitors". Science 335 (6074): 1326–1330. doi:10.1126/science.1216744. PMID 22422977.
45. Dumé, B. (November 26, 2010). "Graphene supercapacitor breaks storage record". Physics World (IOP). Retrieved 2015-02-28.
46. Chenguang, L.; Zhenning, Y.; Neff, D.; Zhamu, A.; Jang, B.Z. (November 2010). "Graphene-based supercapacitor with an ultrahigh energy density". Nano Lett. 10 (12): 4863–4868. doi:10.1021/nl102661q.
47. Miller, J.R.; Outlaw, R.A.; Holloway, B.C. (September 2010). "Graphene double-layer capacitor with ac line-filtering". Science 329 (5999): 1637–1639. doi:10.1126/science.1194372. PMID 20929845.
48. Akbulut, S. (2011). Optimization of Carbon Nanotube Supercapacitor Electrode (PDF) (M.Sc. thesis). Nashville, Tennessee: Graduate School of Vanderbilt University.
49. Arepalli, S.; H. Fireman; C. Huffman; P. Moloney; P. Nikolaev; L. Yowell; C.D. Higgins; K. Kim; P.A. Kohl; S.P. Turano; W.J. Ready (2005). "Carbon-Nanotube-Based Electrochemical Double-Layer Capacitor Technologies for Spaceflight Applications" (PDF). JOM 57: 24–31. doi:10.1007/s11837-005-0179-x.
50. Signorelli, R.; D.C. Ku; J.G. Kassakian; J.E. Schindall (2009). "Electrochemical Double-Layer Capacitors Using Carbon Nanotube Electrode Structures". Proc. IEEE 97 (11): 1837–1847. doi:10.1109/JPROC.2009.2030240.
51. Li, X.; J. Rong; B. Wei (2010). "Electrochemical Behavior of Single-Walled Carbon Nanotube Supercapacitors under Compressive Stress". ACS Nano 4 (10): 6039–6049. doi:10.1021/nn101595y.
52. Wen Lu, ADA Technologies Inc, Carbon Nanotube Supercapacitors
53. B. E. Conway, V. Birss, J. Wojtowicz, The role and the utilization of pseudocapacitance for energy storage by supercapacitors, Journal of Power Sources, Volume 66, Issues 1–2, May–June 1997, Pages 1–14
54. Dillon, A.C. (2010). "Carbon Nanotubes for Photoconversion and Electrical Energy Storage". Chem. Rev. 110 (11): 6856–6872. doi:10.1021/cr9003314. PMID 20839769.
55. Jayalakshmi, M.; Balasubramanian, K. (2008). "Simple Capacitors to Supercapacitors - An Overview" (PDF). Int. J. Electrochem. Sci. 3: 1196–1217.
56. J. P. Zheng, P. J. Cygan, T. R. Jow, Hydrous Ruthenium Oxide as an Electrode Material for Electrochemical Capacitors, ECS, February 8, 1995
57. "Engineered Macroporosity in Single-Wall Carbon Nanotube Films". Nano Lett. 9 (2): 677–683. 2009. doi:10.1021/nl803168s.
58. Wang, W.; Guo, S.; Lee, I.; Ahmed, K.; Zhong, J.; Favors, Z.; Zaera, F.; Ozkan, M.; Ozkan, C. S. (2014). "Hydrous Ruthenium Oxide Nanoparticles Anchored to Graphene and Carbon Nanotube Hybrid Foam for Supercapacitors". Scientific Reports 4. doi:10.1038/srep04452.
60. Simon, Y.Gogotsi (November 2008). "Materials for electrochemical capacitors". Nature Materials 7: 845–854. doi:10.1038/nmat2297. PMID 18956000.
61. Yu.M. Volfkovich, A.A. Mikhailin, D.A. Bograchev, V.E. Sosenkin and V.S. Bagotsky, Studies of Supercapacitor Carbon Electrodes with High Pseudocapacitance, A. N. Frumkin Institute of Physical Chemistry and Electrochemistry, Russian Academy of Sciences, Moscow, Russia, Dr. Ujjal Kumar Sur (Ed.), ISBN 978-953-307-830-4, free copy: PDF
62. type PAS capacitor, Taiyo Yuden, Shoe Electronics Ltd.
63. Yu.M. Volfkovich, Studies of Supercapacitor Carbon Electrodes with High Pseudocapacitance
64. "Facile synthesis and super capacitive behavior of SWNT/MnO2 hybrid films". Nano Energy 1: 479–487. doi:10.1016/j.nanoen.2012.02.011.
65. H. Gualous et al.: Lithium Ion capacitor characterization and modelling ESSCAP’08 −3rd European Symposium on Supercapacitors and Applications, Rome/Italy 2008
66. "FDK To Begin Mass Production of High-Capacity Li-Ion Capacitors; Automotive and Renewable Energy Applications". Green Car Congress. 2009-01-04. Retrieved 2013-05-29.
67. K. Naoi, W. Naoi, Sh. Aoyagi, J. Miyamoto,T. Kamino, New Generation "Nanohybrid Supercapacitor", American Chemical Society, Chem. Res., Article ASAP, DOI: 10.1021/ar200308h, March 20, 2012
68. Yu.M. Volfkovich, Studies of Supercapacitor Carbon Electrodes with High Pseudocapacitance PDF
69. P. Simon, A. Burke, Nanostructured Carbons: Double-Layer Capacitance and More
70. Tetraethylammonium tetrafluoroborate - Compound SummaryCID 2724277 from PubChem
71. A. Schneuwly, R. Gallay, Properties and applications of supercapacitors, From the state-of-the-art to future trends, PCIM 2000
72. A. Laforgue et al. Development of New Generation Supercapacitors for Transportation Applications
73. Nesscap Ultracapacitor - Technical Guide NESSCAP Co., Ltd. 2008
74. Maxwell BOOSTCAP Product Guide – Maxwell Technologies BOOSTCAP Ultracapacitors– Doc. No. 1014627.1 Maxwell Technologies, Inc. 2009
75. Maxwell, K2 series
76. Wen Lu, Carbon Nanotube Supercapacitors
77. Christen, T.; Ohler, C. (2002). "Optimizing energy storage components using Ragone plots". J. Power Sources 110: 107–116. doi:10.1016/S0378-7753(02)00228-8.
78. Dunn-Rankin, D.; Leal, E. Martins; Walther, D.C. (2005). "Personal power systems". Prog. Energy Combust. Sci. 31: 422–465. doi:10.1016/j.pecs.2005.04.001.
79. Maxwell Application Note Application Note - Energy Storage Modules Life Duration Estimation. Maxwell Technologies, Inc. 2007
80. Panasonic Electronic Devices CO., LTD.: Gold capacitors Characteristics data In: Technical Guide of Electric Double Layer Capacitors, Edition 7.4, 2011)
81. "APowerCap Technologies: Ultracapacitors and Solutions / Products". Apowercap.com. Retrieved 2015-12-19.
82. AVX Kyocera, BestCap® (PDF; 869 kB)
83. Cap-XX
84. CDE Cornell Dubilier Supercapacitor
85. Cooper Bussmann. PowerStor
86. Elna, DYNACAP (PDF; 7.1 MB)
87. Evans Capacitor Company, Capattery
88. FastCAP Systems Corp., ultracapacitor
89. Green Tech
90. Illinois Capacitor Inc., Supercapacitor
91. Supercapacitor
92. JSR Micro, Ultimo
93. Korchip, STARCAP
94. LSMtron, Ultracapacitor
95. Maxwell Technologies. Ultracapacitor
96. Murata Manufactoring Co., EDLC
97. NEC Tokin, Supercapacitor
98. Nesscap Energy Inc.
99. Nichicon, EVerCAP
100. Nippon Chemi-Con. NCC, ECC, UCC, DLCCAP
101. Panasonic, Matsushita, Goldcap
102. Samwha Electric Co.
103. Skeleton, SkelCap (PDF; 9.1 MB)
104. Taiyo Yuden, PAS Capacitor, LIC Capacitor
105. Vina Technology Co., Hy-Cap
106. Vishay, 196 HVC ENYCAP™
107. Wima Spezialvertrieb Elektronischer Bauelemente, SuperCaps
108. YEC Yeon Long Technologies, Kapton capacitor
109. Yunasco
110. P. Van den Bossche et al.: The Cell versus the System: Standardization challenges for electricity storage devices EVS24 International Battery, Hybrid and Fuel Cell Electric Vehicle Symposium, Stavanger/Norway 2009
111. Graham Pitcher If the cap fits ... New Electronics. 26 March 2006
112. "Ultracapacitor LED Flashlight Charges In 90 Seconds - Slashdot". Tech.slashdot.org. 2008-12-10. Retrieved 2013-05-29.
113. "Helium Bluetooth speakers powered by supercapacitors". Gizmag.com. Retrieved 2013-11-29.
114. "Coleman FlashCell Cordless Screwdriver Recharges In Just 90 Seconds". OhGizmo!. 2007-09-11. Retrieved 2013-05-29.
115. M. Farhadi and O. Mohammed, Real-time operation and harmonic analysis of isolated and non-isolated hybrid DC microgrid, IEEE Trans. Ind. Appl., vol.50, no.4, pp.2900–2909, Jul./Aug. 2014.
116. M. Farhadi, O. Mohammed 2015 Adaptive energy management in redundant hybrid dc microgrid for pulse load mitigation IEEE Trans. Smart Grid, vol.6, no.1, pp.54–62,
117. Farhadi, Mustafa; Mohammed, Osama (2015). "Performance enhancement of actively controlled hybrid DC microgrid and pulsed power load". IEEE Trans. Ind. Appl. 51 (5): 3570–3578. doi:10.1109/tia.2015.2420630.
118. R. Gallay, Garmanage, Technologies and applications of Supercapacitors, University of Mondragon, June 22, 2012
119. David A. Johnson, P.E. "SuperCapacitors as Energy Storage". Discoversolarenergy.com. Retrieved 2013-05-29.
120. A. Stepanov, I. Galkin, Development of supercapacitor based uninterruptible power supply, Doctoral school of energy- and geo-technology, January 15–20, 2007. Kuressaare, Estonia
121. "Supercapacitor UPS". Marathon Power. Retrieved 2013-05-29.
122. "Maxwell Technologies Ultracapacitors (ups power supply) Uninterruptible Power Supply Solutions". Maxwell.com. Retrieved 2013-05-29.
123. International Energy Agency, Photovoltaic Power Systems Program, The role of energy storage for mini-grid stabilization, IEA PVPS Task 11, Report IEA-PVPS T11-02:2011, July 2011
124. J. R. Miller, JME, Inc. and Case Western Reserve University, Capacitors for Power Grid Storage, (Multi-Hour Bulk Energy Storage using Capacitors)
125. "A 30 Wh/kg Supercapacitor for Solar Energy and a New Battery > JEOL Ltd". Jeol.com. 2007-10-03. Retrieved 2013-05-29.
126. "Performance of printable supercapacitors in an RF energy harvesting circuit". International Journal of Electrical Power 58: 42–46. doi:10.1016/j.ijepes.2014.01.004.
127. "State & Federal Energy Storage Technology Advancement Partnership (ESTAP)" (PDF). Clean Energy States Alliance. Retrieved 26 December 2014.
128. Nippon Chemi-Con, Stanley Electric and Tamura announce: Development of "Super CaLeCS", an environment-friendly EDLC-powered LED Street Lamp. Press Release Nippon Chemi-Con Corp., 30. März 2010.
129. yec.com.tw. "super capacitor supplier list | YEC | This high-energy capacitor from a defibrillator can deliver a lethal 500 joules of energy". YEC. Retrieved 2013-05-29.
130. Cantec Systems, Power solutions
131. Evans Capacitor Company, High Energy Density Capacitors for Military Applications
132. Tecate Group, Back-up power for military applications- Batteries optional!
133. "First one up the drive -A new sort of storage device gives lithium-ion batteries a run for their money". Economist. July 12, 2014. Retrieved March 2015.
134. L. Lionginas, L. Povilas, Management of Locomotive Tractive Energy Resources
135. A. Jaafar, B. Sareni, X. Roboam, M. Thiounn-Guermeur (2010-09-03). "IEEE Xplore - Sizing of a hybrid locomotive based on accumulators and ultracapacitors". Ieeexplore.ieee.org. doi:10.1109/VPPC.2010.5729131. Retrieved 2013-05-29.
136. J. R. Miller, A. F. Burke, Electrochemical Capacitors: Challenges and Opportunities for Real-World Applications, ECS, Vol. 17, No. 1, Spring 2008
137. fuelcellworks.com. "Fuel Cell Works Supplemental News Page". Web.archive.org. Archived from the original on 2008-05-21. Retrieved 2013-05-29.
138. "SINAUTEC, Automobile Technology, LLC". Sinautecus.com. Retrieved 2013-05-29.
139. M. Fröhlich, M. Klohr, St. Pagiela: Energy Storage System with UltraCaps on Board of Railway Vehicles In: Proceedings - 8th World Congress on Railway Research Mai 2008, Soul, Korea
140. Bombardier, MITRAC Energy Saver Support PDF
141. Bombardier, MITRAC Energy Saver Presentation PDF
142. "Rhein-Neckar Verkehr orders more supercapacitor trams". Railway Gazette. 2011-04-05. Retrieved 2013-05-29.
143. Alstom, STEEM
144. "Supercapacitors to be tested on Paris STEEM tram". Railway Gazette. 2009-07-08. Retrieved 2013-05-29.
145. "Genève tram trial assesses supercapacitor performance". Railway Gazette. 2012-08-07. Retrieved 2013-05-29.
146. "Energy Storage - Siemens Global Website". Siemens.com. Retrieved 2013-05-29.
147. "Supercapacitor energy storage for South Island Line". Railway Gazette. 2012-08-03. Retrieved 2013-05-29.
148. "Supercapacitor light metro train unveiled". Railway Gazette. 2012-08-23. Retrieved 2013-05-29.
149. 4-Neo Green Power
151. "The Ultracapbus - VAG Nürnberg - Öffentlicher Personennahverkehr in Nürnberg". Vag.de. Retrieved 2013-05-29.
152. Stefan Kerschl, Eberhard Hipp, Gerald Lexen: Effizienter Hybridantrieb mit Ultracaps für Stadtbusse 14. Aachener Kolloquium Fahrzeug- und Motorentechnik 2005 (German)
153. V. Härri, S. Eigen, B. Zemp, D. Carriero: Kleinbus „TOHYCO-Rider" mit SAM-Superkapazitätenspeicher Jahresbericht 2003 - Programm "Verkehr & Akkumulatoren", HTA Luzern, Fachhochschule Zentralschweiz (Germany)
154. "TOHYCO Rider Fgyre". Ebookbrowse.com. Retrieved 2013-05-29.
155. Hamilton, Tyler (2009-10-19). "Next Stop: Ultracapacitor Buses | MIT Technology Review". Technologyreview.com. Retrieved 2013-05-29.
156. "Green 'tribrid' minibus unveiled". BBC. 2008-06-05. Retrieved 2013-01-12.
157. "Launch of Europe's First Tribrid Green Minibus". 2008-05-30. Retrieved 2013-01-12.
158. Formula One 2011: Power-Train Regulation Framework. 24 May 2007. Retrieved on 23 April 2013.
159. "Die große Analyse: KERS für Dummys - Formel 1 bei". Motorsport-total.com. 2013-05-25. Retrieved 2013-05-29.
160. "Toyota TS030 LMP1 hybrid revealed". Racecar Engineering. 2012-01-24. Retrieved 2013-05-30.
161. Die Hybridtechnik im Toyota TS030: Mit Superkondensatoren zum LeMans-Erfolg. Sportauto
162. Fred Jaillet (2012-06-15). "Post TOYOTA Racing Impresses In Le Mans Qualifying • TOYOTA Racing - FIA World Endurance Championship Team". Toyotahybridracing.com. Retrieved 2013-05-30.
163. A.F. Burke, Batteries and Ultracapacitors for Electric, Hybrid, and Fuel Cell Vehicles
164. Cap-XX Supercapacitors for Automotive & Other Vehicle Applications, March 2012
165. A. Pesaran, J. Gonder, Recent Analysis of UCAPs in Mild Hybrids, National Renewable Energy Laboratory, Golden, Colorado, 6th Advanced Automotive Battery Conference, Baltimore, Maryland, May 17–19, 2006
166. AFS TRINITY UNVEILS 150 MPG EXTREME HYBRID (XH™) SUV. AFS Trinity Power Corporation. 13 January 2008. Retrieved on 31 March 2013.
167. Auto news, 2014 Mazda6 i-Eloop to net 40 mpg hwy, 28 mpg city
168. A. E. KRAMER, Billionaire Backs a Gas-Electric Hybrid Car to Be Built in Russia, The New York Times, December 13, 2010
169. Londoner Emirates Air Line: Teuerste Seilbahn der Welt mit fraglicher verkehrlicher Bedeutung
170. ISR, Internationale Seilbahn Rundschau, Beste Unterhaltung über den Wolken
171. Yang, X.; Cheng, C.; Wang, Y.; Li, D. (August 2013). "Liquid-mediated dense integration of graphene materials for compact capacitive energy storage". Science 341 (6145): 534–537. doi:10.1126/science.1239089. PMID 23908233.
172. Fastcap. "Paradigm shift". FastCap Systems. Retrieved 2013-05-30.
173. "New carbon material boosts supercapacitors". Rsc.org. 2011-05-13. Retrieved 2015-03-01.
174. Y. Zhu et. al. (May 2011). "Carbon-based supercapacitors produced by activation of graphene". Science 332 (3067): 1537–1541. doi:10.1126/science.1200770. PMID 21566159.
175. Kim, T.Y.; Jung, G.; Yoo, S.; Suh, K.S.; Ruoff, R.S. (July 2013). "Activated graphene-based carbons as supercapacitor electrodes with macro- and mesopores". ACS Nano 7 (8): 6899–6905. doi:10.1021/nn402077v.
176. Microporous polymer material for supercapacitors with large capacitance, high energy and power densities and excellent cycle life
177. Kou, Yan; Xu, Yanhong; Guo, Zhaoqi; Jiang, Donglin (2011). "Supercapacitive Energy Storage and Electric Power Supply Using an Aza‐Fused π‐Conjugated Microporous Framework". Angew. Chem. Int. Ed. 50 (37): 8753–8757. doi:10.1002/ange.201103493.
178. Izadi-Najafabadi, A.; Yamada, T.; Futaba, D. N.; Yudasaka, M.; Takagi, H.; Hatori, H.; Iijima, S.; Hata, K. (2011). "High-Power Supercapacitor Electrodes from Single-Walled Carbon Nanohorn/Nanotube Composite". ACS Nano 5 (2): 811–819. doi:10.1021/nn1017457. PMID 21210712.
179. Zhe Tang, Chun-hua Tang, Hao Gong,A High Energy Density Asymmetric Supercapacitor from Nano-architectured Ni(OH)2/Carbon Nanotube Electrodes, Adv. Funct. Mater., 22: 1272–1278. doi:10.1002/adfm.201102796
180. Hsing-Chi Chien, Wei-Yun Cheng, Yong-Hui Wang, Shih-Yuan Lu, Ultrahigh Specific Capacitances for Supercapacitors Achieved by Nickel Cobaltite/Carbon Aerogel Composites, 25 JUL 2012; DOI: 10.1002/adfm.201201176
181. L Mai, H Li, Y Zhao, L Xu, X Xu, Y Luo, Z Zhang, W Ke, C Niu, Q. Zhang: Fast ionic diffusion-enabled nanoflake electrode by spontaneous electrochemical pre-intercalation for high-performance supercapacitor. April 2013, doi:10.1038/srep01718
182. L. Zang et al., Porous 3D graphene-based bulk materials with exceptional high surface area and excellent conductivity for supercapacitors, Key Laboratory for Functional Polymer Materials and Center for Nanoscale Science and Technology, Institute of Polymer Chemistry, College of Chemistry, Nankai University, Tianjin 300071, China, 2013, doi:10.1038/srep01408
183. Zhong-Shuai Wu, Xinliang Feng, Hui-Ming Cheng, Recent advances in graphene-based planar micro-supercapacitors for on-chip energy storage, Natl. Sci. Rev., 2013, doi:10.1093/nsr/nwt003
184. "Ultra-thin capacitors could acclerate development of next-gen electronics | KurzweilAI". www.kurzweilai.net. 2016-02-28. Retrieved 2014-02-11.
185. Wang, Chengxiang; Osada, Minoru; Ebina, Yasuo; Li, Bao-Wen; Akatsuka, Kosho; Fukuda, Katsutoshi; Sugimoto, Wataru; Ma, Renzhi; Sasaki, Takayoshi (2014-02-19). "All-Nanosheet Ultrathin Capacitors Assembled Layer-by-Layer via Solution-Based Processes". ACS Nano 8 (3): 2658–2666. doi:10.1021/nn406367p.
186. Borghino, Dario (2015-04-19). "New device combines the advantages of batteries and supercapacitors". www.gizmag.com. Retrieved 2016-02-10.
187. "Flexible 3D graphene supercapacitors may power portables and wearables | KurzweilAI". www.kurzweilai.net. Retrieved 2016-02-11.
188. Peng, Zhiwei; Lin, Jian; Ye, Ruquan; Samuel, Errol L. G.; Tour, James M. (2015-01-28). "Flexible and Stackable Laser-Induced Graphene Supercapacitors". ACS Applied Materials & Interfaces 7 (5): 3414–3419. doi:10.1021/am509065d.
189. A. Raut, C. Parker, and J. Glass. A method to obtain a Ragone plot for evaluation of carbon nanotube supercapacitor electrodes. Journal of Materials Research Vol. 25, No. 8 (2010).
190. "NanoMarkets forecasts supercapacitor market to reach $3B in 2016; decrease in transportation market share". Green Car Congress. 2010-11-21. Retrieved 2013-05-30.
191. Dennis Zogbi, Paumanok Group, 04.03.2013, Supercapacitors the Myth, the Potential and the Reality
192. "Ultracapacitor Market Forecast 2015-2020". Market Research Media. 2012-03-16. Retrieved 2013-05-30.
193. India on world map of Supercapacitor SPEL is India's first manufacturer of Super capacitor
194. T2+2™ Market Overview, Ch. Ahern, Supercapacitors, December 10, 2009, Project Number NET0007IO

External links

• Brian E. Conway, ELECTROCHEMICAL CAPACITORS Their Nature, Function, and Applications, An Encyclopedia Article From the Yeager center at CWRU
• ELECTRIC DOUBLE LAYER AND CAPACITANCE RESPONSE, The Bockris, Devanathan and Muller model
• MIT OPEN COURSEWARE, Lecture 37 and others
• A SURVEY OF ELECTROCHEMICAL SUPERCAPACITOR TECHNOLOGY
• Supercapacitors: A Brief Overview
• Simple Capacitors to Supercapacitors - An Overview
• Technologies and applications of Supercapacitors, University of Mondragon
• Properties and applications of supercapacitors from the state-of-the-art to future trends
• Perspectives on supercapacitors, pseudocapacitors and batteries
• Standardization challenges for electricity storage devices
• False capacitance of supercapacitors